Method of making frangible seal
Assignee: Baxter International Inc
•
Filing: 1978-03-13
•
Granted: 1979-10-16
•
Expires: 1998-03-13
Abstract
Abstract A method is provided for forming a fracturable seal of the type wherein a plastic cup-shaped closure is hermetically sealed to a plastic planar surface, such as the neck of pharmaceutical solution containers. The seal is formed with the closure by forcing a die heated above the melting point of the plastic material into the planar surface, with the sealing die also being in heat exchange relationship with a portion of the closure. Both the planar surface and the closure adjacent thereto become molten and the surface material is displaced to form a fused seal transverse to the surface. The surface is depressed at least 0.005 inch from its original height by the sealing action of the die, and a frangible section is formed in the vertical side wall of the depression. The seal will be fractured due to tension stress when the closure is removed from the surface.
Inventors
- 👤 David A. Winchell
- 👤 Thomas A. Fowles
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 16:20
CPC Classifications
B; B29; B29C; B29C66/00; B29C66/50; B29C66/51; B29C66/54; B29C66/542; A; A61; A61J; A61J1/00; A61J1/14; A61J1/1412; A61J1/1418; A61J1/18; B29C65/00; B29C65/02; B29C65/18; B29C65/76; B65; B65D; B65D1/00; B65D1/02; B65D1/0223; B65D1/023; B65D1/0238; A61J1/1468; B29C66/80; B29C66/83; B29C66/832; B29C66/8322; B29L; B29L2031/00; B29L2031/56; B29L2031/565; B29L2031/712; B29L2031/7158; Y; Y10; Y10T; Y10T156/00; Y10T156/10; Y10T156/1002; Y10T156/1043
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
161 words
A method of forming a fracturable seal of the type wherein a first part is hermetically fused to a second part, the method comprising the steps of: assembling the first part on the second part with the first part substantially seated on the surface of the second part; heating a sealing die above the melting point of the material of said parts; bringing said sealing die towards said surface on which said first part is seated and alongside and in heat exchange relationship with a side portion of the first part; and pressing said sealing die into said surface so that said surface is depressed from its original height by the sealing action of the die, with both said surface and said first part portion becoming molten and displacing said surface material to form a fused seal transverse to said surface, whereby said seal will be fractured due to tension stress when the first part is removed from the second part.
Claim 2
Independent Claim
161 words
A method of forming a fracturable seal of the type wherein a first part is hermetically fused to a second part, the method comprising the steps of: assembling the first part on the second part with the first part substantially seated on the surface of the second part; heating a sealing die above the melting point of the material of said parts; bringing said sealing die towards said surface on which said first part is seated and alongside and in heat exchange relationship with a side portion of the first part; and pressing said sealing die into said surface so that said surface is depressed from its original height by the sealing action of the die, with both said surface and said first part portion becoming molten and displacing said surface material to form a fused seal transverse to said surface, whereby said seal will be fractured due to tension stress when the first part is removed from the second part.
Claim 3
Dependent Claim
29 words
A method as described in claim 1, wherein said sealing die is heated in the range of 1° F. to 100° F. above the melting point of both parts.
Claim 4
Dependent Claim
27 words
A method as described in claim 1, wherein said surface is depressed at least 0.005 inch from its original height by the sealing action of the die.
Claim 5
Independent Claim
191 words
A method of forming a fracturable seal of the type wherein a plastic cup-shaped closure is sealed to a plastic planar surface, said cup-shaped closure having a bottom edge and a side wall extending upwardly from said bottom edge, said method comprising the steps of: assembling the closure on the planar surface with said bottom edge substantially seated on said surface; heating a sealing die, which sealing die has an internal dimension that is substantially equal to the external dimension of the side wall adjacent the bottom surface, to a temperature that is above the melting temperature of the plastic material of the closure and surface; bringing the sealing die towards said surface and around, and in heat relationship with said side wall; and pressing said sealing die into said surface so that said surface is depressed from its original height by the sealing action of the die, with both said surface and said side wall becoming molten and displacing said surface material to form a fused seal transverse to said surface, whereby said seal will be fractured due to tension stress when the closure is removed from the planar surface.
Claim 6
Independent Claim
191 words
A method of forming a fracturable seal of the type wherein a plastic cup-shaped closure is sealed to a plastic planar surface, said cup-shaped closure having a bottom edge and a side wall extending upwardly from said bottom edge, said method comprising the steps of: assembling the closure on the planar surface with said bottom edge substantially seated on said surface; heating a sealing die, which sealing die has an internal dimension that is substantially equal to the external dimension of the side wall adjacent the bottom surface, to a temperature that is above the melting temperature of the plastic material of the closure and surface; bringing the sealing die towards said surface and around, and in heat relationship with said side wall; and pressing said sealing die into said surface so that said surface is depressed from its original height by the sealing action of the die, with both said surface and said side wall becoming molten and displacing said surface material to form a fused seal transverse to said surface, whereby said seal will be fractured due to tension stress when the closure is removed from the planar surface.
Claim 7
Dependent Claim
33 words
A method as described in claim 4, wherein said sealing die is heated in the range of 1° F. to 100° F. above the melting point of said surface and said side wall.
Claim 8
Dependent Claim
27 words
A method as described in claim 4, wherein said surface is depressed at least 0.005 inch from its original height by the sealing action of the die.
Claim 9
Dependent Claim
39 words
A method as described in claim 4, said closure having a generally circular cross-sectional configuration with the side wall tapering upwardly and inwardly, said sealing die being brought vertically downwardly toward and into said surface to form said seal.
Claim 10
Independent Claim
211 words
A method of forming a fracturable seal of the type wherein a plastic cup-shaped closure is sealed to a plastic planar surface, said cup-shaped closure having a generally circular cross-sectional configuration, a bottom edge, and a side wall extending upwardly and inwardly from said bottom edge, said method comprising the steps of: assembling the closure on the planar surface with said bottom edge substantially seated on said surface; heating a sealing die to a temperature in the range of 1° F. to 100° F. above the melting point of said surface and side wall material, said sealing die having an internal dimension that is substantially equal to the external dimension of the side wall adjacent the bottom surface; bringing the sealing die vertically downwardly towards said surface and around, and in heat relationship with said side wall; and pressing said sealing die vertically into said surface, so that said surface is depressed at least 0.005 inch from its original height by the sealing action of the die, with both said surface and said side wall becoming molten and thus displacing said surface material to form a fused seal transverse to said surface, whereby said seal will be fractured due to tension stress when the closure is removed from the planar surface.
Claim 11
Independent Claim
211 words
A method of forming a fracturable seal of the type wherein a plastic cup-shaped closure is sealed to a plastic planar surface, said cup-shaped closure having a generally circular cross-sectional configuration, a bottom edge, and a side wall extending upwardly and inwardly from said bottom edge, said method comprising the steps of: assembling the closure on the planar surface with said bottom edge substantially seated on said surface; heating a sealing die to a temperature in the range of 1° F. to 100° F. above the melting point of said surface and side wall material, said sealing die having an internal dimension that is substantially equal to the external dimension of the side wall adjacent the bottom surface; bringing the sealing die vertically downwardly towards said surface and around, and in heat relationship with said side wall; and pressing said sealing die vertically into said surface, so that said surface is depressed at least 0.005 inch from its original height by the sealing action of the die, with both said surface and said side wall becoming molten and thus displacing said surface material to form a fused seal transverse to said surface, whereby said seal will be fractured due to tension stress when the closure is removed from the planar surface.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-10-15 | 1983-04-16 | 1983-10-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-10-15 | 1987-04-16 | 1987-10-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-10-15 | 1991-04-16 | 1991-10-16 | $7700.00 | Window Closed / Lapsed |