Process for producing oxidizing metal catalysts incorporating platinum and catalyst produced by the process
Assignee: Kanadevia Corp
•
Filing: 1978-01-30
•
Granted: 1979-10-09
•
Expires: 1998-01-30
Abstract
Abstract An oxidizing metal catalyst incorporating platinum is produced by converting the surface layer of steel material of specified shape resembling a ring, honeycomb, plate or the like to an aluminum alloy, treating the steel material with an aluminum dissolving solution to dissolve out the aluminum and to render the surface layer porous, subjecting the steel material to oxidation treatment to obtain a catalyst carrier, immersing the carrier in a solution of chloroplatinic acid adjusted to weak alkalinity with sodium hydroxide, and drying the carrier after withdrawing the carrier from the solution.
Inventors
- 👤 Hideya Inaba
- 👤 Yasumi Kamino
- 👤 Shigenori Onizuka
- 👤 Chikashi Inazumi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 15:27
CPC Classifications
B; B01; B01J; B01J23/00; B01J23/38; B01J23/40; B01J23/42; B01D; B01D53/00; B01D53/34; B01D53/74; B01D53/86; B01D53/8621; B01D53/8634; B01D53/864; C; C01; C01B; C01B21/00; C01B21/20; C01B21/24; C01B21/26; C01B21/265
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
100 words
A process for producing a catalyst precursor for decomposing NH 3 by oxidation consisting essentially of the steps of converting the surface layer of steel material of specified shape resembling a ring, honeycomb or plate to an aluminum alloy, treating the steel material with an aluminum dissolving solution to dissolve out the aluminum and to render the surface layer porous, subjecting the resulting steel material to oxidation treatment to obtain a catalyst carrier, immersing the carrier in a solution of chloroplatinic acid adjusted to weak alkalinity with sodium hydroxide and drying the carrier after withdrawing the carrier from the solution.
Claim 2
Dependent Claim
100 words
A process for producing a catalyst precursor for decomposing NH 3 by oxidation consisting essentially of the steps of converting the surface layer of steel material of specified shape resembling a ring, honeycomb or plate to an aluminum alloy, treating the steel material with an aluminum dissolving solution to dissolve out the aluminum and to render the surface layer porous, subjecting the resulting steel material to oxidation treatment to obtain a catalyst carrier, immersing the carrier in a solution of chloroplatinic acid adjusted to weak alkalinity with sodium hydroxide and drying the carrier after withdrawing the carrier from the solution.
Claim 3
Dependent Claim
27 words
A process as defined in claim 1 wherein the surface layer of the steel material is converted to an aluminum alloy by heat-treating an aluminum-coated steel material.
Claim 4
Dependent Claim
27 words
A process as defined in claim 1 wherein the aluminum is dissolved out by immersing the steel material having the alloy layer in the aluminum dissolving solution.
Claim 5
Dependent Claim
21 words
A process as defined in claim 1 wherein the aluminum dissolving solution is an aqueous solution of an alkali metal hydroxide.
Claim 6
Dependent Claim
34 words
A process as defined in claim 1 wherein the oxidation treatment is conducted by contacting the porous surface layer of the steel material with a gas containing 0.1 to 20.8% by volume of oxygen.
Claim 7
Dependent Claim
31 words
A process as defined in claim 1 wherein the carrier is immersed in an aqueous solution of chloroplatinic acid having a concentration of 0.01 to 1.0% by weight calculated as platinum.
Claim 8
Dependent Claim
20 words
A process as defined in claim 1 wherein the sodium hydroxide is used in the form of an aqueous solution.
Claim 9
Dependent Claim
18 words
A process as defined in claim 7 wherein the aqueous solution has a concentration of about 10 moles/liter.
Claim 10
Dependent Claim
27 words
A process as defined in claim 1 wherein the carrier is immersed in an aqueous solution of chloroplatinic acid having its pH adjusted to 8 to 9.
Claim 11
Dependent Claim
13 words
An oxidizing catalyst precursor produced by the process as defined in claim 1.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-10-08 | 1983-04-09 | 1983-10-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-10-08 | 1987-04-09 | 1987-10-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-10-08 | 1991-04-09 | 1991-10-09 | $7700.00 | Window Closed / Lapsed |