Assignee: Wyeth Holdings LLC
•
Filing: 1977-11-21
•
Granted: 1979-10-02
•
Expires: 1997-11-21
Abstract
Abstract Disclosed is a process for preparing shaped alumina particles for catalysts or catalyst supports by passing droplets of an aqueous slurry of a rehydratable alumina composition through a shaping medium, such as a column of water-immiscible liquid. The alumina composition undergoes rehydration while being shaped as it passes through the shaping medium, and accordingly, firm, discrete alumina bodies are produced.
Inventors
- 👤 William E. Bambrick
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 14:56
CPC Classifications
B; B01; B01J; B01J37/00; B01J37/0009; B01J37/0018; B01J21/00; B01J21/02; B01J21/04; C; C01; C01F; C01F7/00; C01F7/02; C01F7/021; C01F7/025; B01J37/0072; C01P; C01P2004/00; C01P2004/30; C01P2006/00; C01P2006/11; C01P2006/12; C01P2006/14; C01P2006/21
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
169 words
In a method for producing low density shaped alumina particles suitable for use as catalysts and catalyst supports comprising preparing an aqueous slurry of an alumina composition containing a substantial portion of a rehydratable alumina, shaping the alumina into desired form, rehydrating to harden the shaped alumina, and curing, drying, and calcining the shaped alumina particles to produce catalyst and catalyst support material, an improvement comprising introducing an aqueous slurry comprising water, an alumina containing a substantial portion of a rehydratable alumina, and a combustible filler to a shaping medium selected from (a) a water immiscible phase into which droplets of said alumina slurry are introduced to be shaped by surface tension forces into a spherical beaded form, and (b) tubing of desired cross sectional size and shape to shape said alumina into extrudate form, whereby the alumina is fashioned into a desired configuration, and applying heat to said shaping medium to rehydrate and harden the alumina while it is being subjected to the influence of the shaping medium.
Claim 2
Dependent Claim
169 words
In a method for producing low density shaped alumina particles suitable for use as catalysts and catalyst supports comprising preparing an aqueous slurry of an alumina composition containing a substantial portion of a rehydratable alumina, shaping the alumina into desired form, rehydrating to harden the shaped alumina, and curing, drying, and calcining the shaped alumina particles to produce catalyst and catalyst support material, an improvement comprising introducing an aqueous slurry comprising water, an alumina containing a substantial portion of a rehydratable alumina, and a combustible filler to a shaping medium selected from (a) a water immiscible phase into which droplets of said alumina slurry are introduced to be shaped by surface tension forces into a spherical beaded form, and (b) tubing of desired cross sectional size and shape to shape said alumina into extrudate form, whereby the alumina is fashioned into a desired configuration, and applying heat to said shaping medium to rehydrate and harden the alumina while it is being subjected to the influence of the shaping medium.
Claim 3
Dependent Claim
28 words
The method of claim 1 wherein the combustible filler is selected from the group consisting essentially of microcrystalline cellulose, starch, wood flour, fine particle carbon black, and sawdust.
Claim 4
Dependent Claim
12 words
The method of claim 1 wherein the combustible filler is microcrystalline cellulose.
Claim 5
Dependent Claim
23 words
The method of claim 1 wherein the combustible filler is used at about 1 to 25 percent by weight of the dry ingredients.
Claim 6
Dependent Claim
19 words
The method of claim 1 wherein the solids content of said aqueous slurry is about 25 to 50 percent.
Claim 7
Dependent Claim
28 words
The method of claim 1 wherein the alumina composition used to prepare said aqueous slurry is an alumina powder having a rehydration index of about 40 to 80.
Claim 8
Dependent Claim
25 words
The method of claim 1 wherein said immiscible phase is a mineral oil-polyterpene resin mixture heated to a temperature of about 80° to 100° C.
Claim 9
Dependent Claim
15 words
The method of claim 1 wherein steam heat is applied to the tubing shaping medium.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-10-01 | 1983-04-02 | 1983-10-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-10-01 | 1987-04-02 | 1987-10-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-10-01 | 1991-04-02 | 1991-10-02 | $7700.00 | Window Closed / Lapsed |