Zirconium-base alloy nuclear fuel container and method
Assignee: General Electric Co
•
Filing: 1977-11-25
•
Granted: 1979-10-02
•
Expires: 1997-11-25
Abstract
Abstract A fast neutron-irradiated zirconium-base alloy body having load-carrying capacity substantially greater than similar conventional zirconium-base alloy bodies likewise irradiated is produced by subjecting a body heat treated at 930° C. and then water-quenched and containing 0.2 weight percent beryllium and at least 95 weight percent zirconium to integrated neutron flux approximating 1.2×10 21 nvt while maintaining the body at about 330° C.
Inventors
- 👤 Daeyong Lee
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-10 02:10
CPC Classifications
C; C22; C22F; C22F3/00; Y; Y10; Y10S; Y10S376/00; Y10S376/90; Y10S376/904; Y10S376/906
Claims Analysis
Total Claims: 3
Claim 1
Independent Claim
83 words
A fast neutron-irradiated zirconium-base alloy body selected from the group consisting of Zircaloy-2 and Zircaloy-4 containing from 0.05 to 0.25 weight percent beryllium and having substantially greater load-carrying capacity than similar conventional zirconium-base alloy bodies irradiated in the same way and to the same degree, and having at 327° C. an unique combination of physical properties including 2.5 percent uniform elongation, 8.2 percent total elongation and 35 percent area reduction, yield strength greater than 76,000 psi, and tensile strength greater than 80,000 psi.
Claim 2
Dependent Claim
83 words
A fast neutron-irradiated zirconium-base alloy body selected from the group consisting of Zircaloy-2 and Zircaloy-4 containing from 0.05 to 0.25 weight percent beryllium and having substantially greater load-carrying capacity than similar conventional zirconium-base alloy bodies irradiated in the same way and to the same degree, and having at 327° C. an unique combination of physical properties including 2.5 percent uniform elongation, 8.2 percent total elongation and 35 percent area reduction, yield strength greater than 76,000 psi, and tensile strength greater than 80,000 psi.
Claim 3
Dependent Claim
11 words
The zirconium-base alloy of claim 1 containing 0.2 weight percent beryllium.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-10-01 | 1983-04-02 | 1983-10-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-10-01 | 1987-04-02 | 1987-10-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-10-01 | 1991-04-02 | 1991-10-02 | $7700.00 | Window Closed / Lapsed |