US4169599A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Two-piece solid golf balls
Assignee: Bridgestone Corp
•
Filing: 1977-06-16
•
Granted: 1979-10-02
•
Expires: 1997-06-16
Abstract
Abstract Two-piece solid golf balls having an improved initial velocity are disclosed. The core is obtained by curing a composition comprising (a) 100 parts by weight of polybutadiene, (b) 9-20 parts by weight of a polyfunctional unsaturated ester, (c) 5-10 parts by weight of methacrylic acid and/or acrylic acid, the total amount of the ingredients (b) and (c) being 15-30 parts by weight and the weight ratio of the ingredient (b)/the ingredient (c) being 55/45-80/20, (d) 20-80 parts by weight of a zinc compound and (e) 0.5-5 parts by weight of an alkyl peroxide. The cover comprises (f) 100 parts by weight of a metal salt of a copolymer of ethylene and unsaturated carboxylic acid, said metal salt having a loss tangent of lower than 0.08, and (g) 1-5 parts by weight of an inorganic filler.
Inventors
- 👤 Ryota Fujio
- 👤 Motozumi Kitayama
- 👤 Fumio Odaka
- 👤 Takashi Nyomura
- 👤 Shiro Anzai
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 09:09
CPC Classifications
C; C08; C08K; C08K5/00; C08K5/04; C08K5/10; C08K5/101; C08K5/103; A; A63; A63B; A63B37/00; A63B37/0003; A63B37/0023; A63B37/0029; A63B37/0033; A63B37/005; A63B37/006; A63B37/0064; A63B37/007; A63B37/0072; A63B37/0074; A63B37/0077; A63B37/008; A63B37/0083; A63B37/0084; B; B29; B29D; B29D99/00; B29D99/0042; C08K5/09; B29K; B29K2009/00; B29K2033/00; B29K2033/04; B29L; B29L2031/00; B29L2031/54
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
246 words
A two-piece solid golf ball comprising a solid core and a cover enclosing the core, said core being obtained by curing a composition comprising (a) 100 parts by weight of polybutadiene containing at least 40% of cis-1,4 configuration, (b) 9-20 parts by weight of a polyfunctional unsaturated ester being selected from the reaction products of an acid selected from the group consisting of acrylic acid and methacrylic acid with an alcohol selected from the group consisting of di-hydric alcohols, tri-hydric alcohols and tetra-hydric alcohols (c) 5-10 parts by weight of an acid selected from the group consisting of methacrylic acid, acrylic acid and mixtures thereof, the total amount of the ingredients (b) and (c) being 15-30 parts by weight and the weight ratio of the ingredient (b) to the ingredient (c) being within the range of 55/45-80/20, (d) 20-80 parts by weight of a zinc compound which reacts with the ingredient (c) to form crosslinkage by metal ion bonding, wherein the amount of the zinc compound exceeding 10 parts by weight based on 100 parts by weight of the ingredient (a) acts as a filler to adjust the weight of the golf ball, and (e) 0.5-5 parts by weight of an alkyl peroxide, and said cover comprising (f) 100 parts by weight of a metal salt of a copolymer of ethylene and unsaturated carboxylic acid, said metal salt having a loss tangent of lower than 0.08, and (g) 1-5 parts by weight of an inorganic filler.
Claim 2
Dependent Claim
246 words
A two-piece solid golf ball comprising a solid core and a cover enclosing the core, said core being obtained by curing a composition comprising (a) 100 parts by weight of polybutadiene containing at least 40% of cis-1,4 configuration, (b) 9-20 parts by weight of a polyfunctional unsaturated ester being selected from the reaction products of an acid selected from the group consisting of acrylic acid and methacrylic acid with an alcohol selected from the group consisting of di-hydric alcohols, tri-hydric alcohols and tetra-hydric alcohols (c) 5-10 parts by weight of an acid selected from the group consisting of methacrylic acid, acrylic acid and mixtures thereof, the total amount of the ingredients (b) and (c) being 15-30 parts by weight and the weight ratio of the ingredient (b) to the ingredient (c) being within the range of 55/45-80/20, (d) 20-80 parts by weight of a zinc compound which reacts with the ingredient (c) to form crosslinkage by metal ion bonding, wherein the amount of the zinc compound exceeding 10 parts by weight based on 100 parts by weight of the ingredient (a) acts as a filler to adjust the weight of the golf ball, and (e) 0.5-5 parts by weight of an alkyl peroxide, and said cover comprising (f) 100 parts by weight of a metal salt of a copolymer of ethylene and unsaturated carboxylic acid, said metal salt having a loss tangent of lower than 0.08, and (g) 1-5 parts by weight of an inorganic filler.
Claim 3
Dependent Claim
18 words
The golf ball according to claim 1, wherein said polybutadiene (a) contains at least 90% of cis-1,4 configuration.
Claim 4
Dependent Claim
32 words
The golf ball according to claim 1, wherein said polyfunctional unsaturated ester (b) is at least one ester selected from the group consisting of ethylene glycol dimethacrylate, trimethylolpropane trimethacrylate and tetramethylolmethane triacrylate.monomethacrylate.
Claim 5
Dependent Claim
14 words
The golf ball according to claim 1, wherein said acid (c) is methacrylic acid.
Claim 6
Dependent Claim
30 words
The golf ball according to claim 1, wherein said zinc compound (d) is at least one member selected from the group consisting of zinc oxide, zinc carbonate and zinc hydroxide.
Claim 7
Dependent Claim
16 words
The golf ball according to claim 5, wherein said zinc compound (d) is activated zinc oxide.
Claim 8
Dependent Claim
15 words
The golf ball according to claim 1, wherein said alkyl peroxide (e) is dicumyl peroxide.
Claim 9
Dependent Claim
29 words
The golf ball according to claim 1, wherein said inorganic filler (g) is at least one member selected from the group consisting of silica, zinc oxide and titanium dioxide.
Claim 10
Dependent Claim
21 words
The golf ball according to claim 1, wherein the amount of said polyfunctional unsaturated ester (b) is 11.5-17.5 parts by weight.
Claim 11
Dependent Claim
19 words
The golf ball according to claim 1, wherein the amount of said acid (c) is 6-8.5 parts by weight.
Claim 12
Dependent Claim
22 words
The golf ball according to claim 1, wherein the total amount of the ingredients (b) and (c) is 18-26 parts by weight.
Claim 13
Dependent Claim
21 words
The golf ball according to claim 1, wherein the weight ratio of the ingredient (b) to the ingredient (c) is 57/43-75/25.
Claim 14
Dependent Claim
254 words
A two-piece solid golf ball comprising a solid core and a cover enclosing the core, said core being obtained by curing a composition comprising (a) 100 parts by weight of polybutadiene containing at least 40% of cis-1,4 configuration, (b) 9-20 parts by weight of a polyfunctional unsaturated ester being selected from the reaction products of an acid selected from the group consisting of acrylic acid and methacrylic acid with an alcohol selected from the group consisting of dihydric alcohols, tri-hydric alcohols and tetra-hydric alcohols, (c) 5-10 parts by weight of an acid selected from the group consisting of methacrylic acid, acrylic acid and mixtures thereof, the total amount of the ingredients (b) and (c) being 15-30 parts by weight and the weight ratio of the ingredient (b) to the ingredient (c) being within the range of 55/45-80/20, (d) 20-80 parts by weight of a zinc compound which reacts with the ingredient (c) to form crosslinkage by metal ion bonding, wherein the amount of the zinc compound exceeding 10 parts by weight based on 100 parts by weight of the ingredient (a) acts as a filler to adjust the weight of the golf ball, (e) 0.5-5 parts by weight of an alkyl peroxide, and (f) 0.1-5 parts by weight of stearic acid, and said cover comprising (g) 100 parts by weight of a metal salt of a copolymer of ethylene and unsaturated carboxylic acid, said metal salt having a loss tangent of lower than 0.08, and (h) 1-5 parts by weight of an inorganic filler.
Claim 15
Dependent Claim
254 words
A two-piece solid golf ball comprising a solid core and a cover enclosing the core, said core being obtained by curing a composition comprising (a) 100 parts by weight of polybutadiene containing at least 40% of cis-1,4 configuration, (b) 9-20 parts by weight of a polyfunctional unsaturated ester being selected from the reaction products of an acid selected from the group consisting of acrylic acid and methacrylic acid with an alcohol selected from the group consisting of dihydric alcohols, tri-hydric alcohols and tetra-hydric alcohols, (c) 5-10 parts by weight of an acid selected from the group consisting of methacrylic acid, acrylic acid and mixtures thereof, the total amount of the ingredients (b) and (c) being 15-30 parts by weight and the weight ratio of the ingredient (b) to the ingredient (c) being within the range of 55/45-80/20, (d) 20-80 parts by weight of a zinc compound which reacts with the ingredient (c) to form crosslinkage by metal ion bonding, wherein the amount of the zinc compound exceeding 10 parts by weight based on 100 parts by weight of the ingredient (a) acts as a filler to adjust the weight of the golf ball, (e) 0.5-5 parts by weight of an alkyl peroxide, and (f) 0.1-5 parts by weight of stearic acid, and said cover comprising (g) 100 parts by weight of a metal salt of a copolymer of ethylene and unsaturated carboxylic acid, said metal salt having a loss tangent of lower than 0.08, and (h) 1-5 parts by weight of an inorganic filler.
References Cited (Backward Citations)
US3454280A
Cited
US3940146A
Cited
US3974238A
Cited
US3819768A
Cited
US4056269A
Cited
US4068849A
Cited
US4065537A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-10-01 | 1983-04-02 | 1983-10-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-10-01 | 1987-04-02 | 1987-10-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-10-01 | 1991-04-02 | 1991-10-02 | $7700.00 | Window Closed / Lapsed |