Cracking process and catalyst for same containing tellurium

Claim 2

A process for cracking a hydrocarbon feedstock which comprises contacting said hydrocarbon feedstock containing metal contaminants with a cracking catalyst under cracking conditions and in the absense of added hydrogen wherein said cracking catalyst has been modified with a modifying amount of at least one treating agent selected from the group consisting of elemental tellurium, oxides of tellurium and compounds convertible to elemental tellurium or oxide thereof during cracking or catalyst regeneration.

Claim 3

A process according to claim 1 wherein said cracking catalyst contains said treating agent in an amount such as to provide in the range of from about 0.005 to about 5 parts by weight tellurium per 100 parts by weight of said cracking catalyst prior to being contacted with said treating agent.

Claim 4

A process according to claim 1 wherein said cracking catalyst is a used cracking catalyst.

Claim 5

A process according to claim 3 wherein said used cracking catalyst has an at least partially deactivating amount of one or more of the metals nickel, iron and vanadium deposited thereon.

Claim 6

A process according to claim 1 wherein said cracking catalyst is an unused cracking catalyst.

Claim 7

A process according to claim 1 wherein said cracking catalyst is a mixture of used and unused cracking catalyst.

Claim 8

A process according to claim 1 wherein said treating agent is added to said catalyst prior to contacting thereof with said hydrocarbon feedstock.

Claim 9

A process according to claim 1 wherein said treating agent is added to said catalyst by addition thereof to said hydrocarbon feedstock prior to contacting said cracking catalyst.

Claim 10

In a cracking process comprising (a) introducing a hydrocarbon feedstock stream containing metal contaminants into a cracking zone, (b) contacting the hydrocarbon feedstock stream in said cracking zone with a cracking catalyst in the absense of added hydrogen under elevated temperature conditions to produce a cracked product, (c) withdrawing said cracked product from said cracking zone, (d) separating said cracked product from said catalyst, (e) introducing said catalyst into a regeneration zone with free oxygen-containing gas such as to burn off at least a portion of the coke deposited on said cracking catalyst and reintroducing the thus regenerated catalyst into the cracking zone, the improvement which comprises contacting said cracking catalyst with a modifying amount of at least one treating agent selected from the group consisting of elemental tellurium, oxides of tellurium and compounds convertible to elemental tellurium or oxide thereof during cracking or catalyst regeneration.

Claim 11

In a cracking process comprising (a) introducing a hydrocarbon feedstock stream containing metal contaminants into a cracking zone, (b) contacting the hydrocarbon feedstock stream in said cracking zone with a cracking catalyst in the absense of added hydrogen under elevated temperature conditions to produce a cracked product, (c) withdrawing said cracked product from said cracking zone, (d) separating said cracked product from said catalyst, (e) introducing said catalyst into a regeneration zone with free oxygen-containing gas such as to burn off at least a portion of the coke deposited on said cracking catalyst and reintroducing the thus regenerated catalyst into the cracking zone, the improvement which comprises contacting said cracking catalyst with a modifying amount of at least one treating agent selected from the group consisting of elemental tellurium, oxides of tellurium and compounds convertible to elemental tellurium or oxide thereof during cracking or catalyst regeneration.

Claim 12

A process according to claim 9 wherein said treating agent is added in an amount such as to provide in the range of from about 0.005 to about 5 parts by weight tellurium per 100 parts by weight of said cracking catalyst prior to being contacted with said treating agent.

Claim 13

A process according to claim 10 wherein said cracking catalyst is contacted under elevated temperature conditions and under reducing conditions with said treating agent.

Claim 14

A process according to claim 9 wherein said contacting of said cracking catalyst is effected by addition of said treating agent to said hydrocarbon feedstock.

Claim 15

A process according to claim 9 wherein said treating agent is admixed with said regenerated catalyst prior to introduction thereof into said cracking zone.

Claim 16

A process according to claim 9 wherein said treating agent is deposited on unused cracking catalyst and the resulting composition is introduced into said regeneration zone.

Claim 17

A process according to claim 9 wherein said treating agent is elemental tellurium.

Claim 18

A process according to claim 9 wherein said hydrocarbon feedstock is a heavy oil.

Claim 19

A process according to claim 16 wherein said heavy oil has from 40 to 800 ppm metals therein.