US4168372A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for reducing the unreacted vinylidene chloride content of a vinylidene chloride polymer
Assignee: EIDP Inc
•
Filing: 1976-07-15
•
Granted: 1979-09-18
•
Expires: 1996-07-15
Abstract
Abstract A method for reducing the amount of free vinylidene chloride in an aqueous dispersion of a vinylidene chloride polymer by adding to the dispersion a small amount of a redox initiator, and then subjecting the dispersion to a temperature in the range of room temperature to about 40° C. for a period of at least one hour. Substrates such as packaging films can be coated with the aqueous dispersion, or with a solvent solution of the polymer after separation from the dispersion. By use of such a coating bath, the amount of vinylidene chloride vapor in the atmosphere near the coating station is significantly less than the amount when using a coating bath of polymer not subjected to the method of the invention.
Inventors
- 👤 John W. Meier
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 20:09
CPC Classifications
C; C08; C08F; C08F259/00; C08F259/02; C08F259/04
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
119 words
A method for reducing the amount of free vinylidene chloride in an aqueous dispersion of a vinylidene chloride polymer, said dispersion containing 600 to 10,000 ppm free vinylidene chloride by weight of dispersion and said polymer containing at least 80% by weight of vinylidene chloride units, comprising adding to said dispersion a redox initiator in an amount of at least 50% of that which is sufficient to polymerize at least 98% of the total initial monomer charge in a period of 4 hours at a temperature no greater than 40° C., and then subjecting said dispersion to a temperature in the range from room temperature to no greater than 40° C. for a period of at least one hour.
Claim 2
Independent Claim
119 words
A method for reducing the amount of free vinylidene chloride in an aqueous dispersion of a vinylidene chloride polymer, said dispersion containing 600 to 10,000 ppm free vinylidene chloride by weight of dispersion and said polymer containing at least 80% by weight of vinylidene chloride units, comprising adding to said dispersion a redox initiator in an amount of at least 50% of that which is sufficient to polymerize at least 98% of the total initial monomer charge in a period of 4 hours at a temperature no greater than 40° C., and then subjecting said dispersion to a temperature in the range from room temperature to no greater than 40° C. for a period of at least one hour.
Claim 3
Dependent Claim
135 words
In a method for preparing an aqueous dispersion of a vinylidene chloride polymer by contacting an aqueous emulsion of a mixture of monomers of which at least 80% by weight is vinylidene chloride with a first initiator which effects initiation thermally or by redox action, the improvement comprising reducing the amount of unpolymerized vinylidene chloride remaining when conversion of monomer to polymer is at least 99% complete, to below 600 ppm by weight of said dispersion by adding to said dispersion a second initiator which is a redox initiator in an amount of at least 0.05% by weight of the polymer of each component of the initiator, and then subjecting said dispersion to a temperature in the range from room temperature to no greater than 40° C. for a period of at least 1 hour.
Claim 4
Dependent Claim
135 words
In a method for preparing an aqueous dispersion of a vinylidene chloride polymer by contacting an aqueous emulsion of a mixture of monomers of which at least 80% by weight is vinylidene chloride with a first initiator which effects initiation thermally or by redox action, the improvement comprising reducing the amount of unpolymerized vinylidene chloride remaining when conversion of monomer to polymer is at least 99% complete, to below 600 ppm by weight of said dispersion by adding to said dispersion a second initiator which is a redox initiator in an amount of at least 0.05% by weight of the polymer of each component of the initiator, and then subjecting said dispersion to a temperature in the range from room temperature to no greater than 40° C. for a period of at least 1 hour.
Claim 5
Dependent Claim
13 words
The method of claim 1 wherein said redox initiator is a persulfate/bisulfite initiator.
Claim 6
Dependent Claim
21 words
The method of claim 3 wherein said aqueous dispersion is a dispersion prepared with the use of a persulfate/bisulfite redox initiator.
Claim 7
Dependent Claim
22 words
The method of claim 3 wherein said aqueous dispersion is a dispersion prepared by thermal initiation with the use of a persulfate.
Claim 8
Dependent Claim
11 words
The method of claim 5 wherein said persulfate is ammonium persulfate.
Claim 9
Dependent Claim
17 words
The method of claim 3 wherein said temperature to which said dispersion is subjected is room temperature.
Claim 10
Dependent Claim
13 words
The method of claim 7 wherein said period is at least 4 hours.
Claim 11
Dependent Claim
13 words
The method of claim 7 wherein said period is at least 20 hours.
Claim 12
Dependent Claim
12 words
The method of claim 3 wherein said dispersion contains an iron salt.
Claim 13
Dependent Claim
34 words
The method of claim 3 wherein said redox initiator is used in an amount of at least 80% of that which is sufficient to polymerize at least 98% of the total initial monomer charge.
Claim 14
Dependent Claim
40 words
The method of claim 11 wherein said redox initiator comprises equal weights of ammonium persulfate and meta sodium bisulfite and is added to said dispersion in aqueous solution having a concentration no greater than 6% by weight of said solution.
Claim 15
Dependent Claim
21 words
The method of claim 2 wherein the addition of said second initiator is after said conversion is at least 99.7% complete.
Claim 16
Dependent Claim
13 words
The method of claim 2 wherein said second initiator is a persulfate/bisulfite initiator.
Claim 17
Dependent Claim
14 words
The method of claim 14 wherein said first initiator is a persulfate/bisulfite redox initiator.
Claim 18
Dependent Claim
16 words
The method of claim 14 wherein said first initiator effects initiation thermally and is a persulfate.
Claim 19
Dependent Claim
11 words
The method of claim 14 wherein said temperature is room temperature.
Claim 20
Dependent Claim
13 words
The method of claim 17 wherein said period is at least 4 hours.
Claim 21
Dependent Claim
13 words
The method of claim 17 wherein said period is at least 20 hours.
Claim 22
Dependent Claim
12 words
The method of claim 14 wherein said dispersion contains an iron salt.
Claim 23
Dependent Claim
67 words
The method of claim 14 wherein said first initiator comprises equal weights of ammonium persulfate and meta sodium bisulfite, and said second initiator comprises equal weights of ammonium persulfate and meta sodium bisulfite each in an amount of 0.1 to 0.3% by weight of the polymer and is added to said dispersion in aqueous solution having a concentration no greater than 6% by weight of said solution.
References Cited (Backward Citations)
US2662867A
Cited
US2776273A
Cited
US2843572A
Cited
GB965022A
Cited
US3423352A
Cited
US3692726A
Cited
US3532675A
Cited
US3832317A
Cited
US4015065A
Cited
JPS515149A
Cited
US4008361A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-09-17 | 1983-03-19 | 1983-09-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-09-17 | 1987-03-19 | 1987-09-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-09-17 | 1991-03-19 | 1991-09-18 | $7700.00 | Window Closed / Lapsed |