US4168249A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Acrylic lacquer coating composition of polymethyl methacrylate, copolymers of methyl methacrylate, cellulose acetate butyrate and a polyester plasticizer
Assignee: EIDP Inc
•
Filing: 1977-07-01
•
Granted: 1979-09-18
•
Expires: 1997-07-01
Abstract
Abstract A coating composition for finishing the exterior of automobile and truck bodies having a film forming binder of the following constituents: (a) polymethyl methacrylate; (b) a copolymer of methyl methacrylate and an alkyl amino alkyl methacrylate such as diethyl amino ethyl methacrylate; (c) a copolymer of methyl methacrylate and an alkyl acrylate such as butyl acrylate; (d) cellulose acetate butyrate; (e) a polyester plasticizer (f) a polymer of methyl methacrylate, an alkyl acrylate and an α-β ethylenically unsaturated monocarboxylic acid such as acrylic acid or methacrylic acid reacted with an alkylene imine such as propylene imine; The composition has good adhesion to lacquer and enamel finishes used on automobiles and truck bodies and is excellent for refinishing automobile and truck bodies.
Inventors
- 👤 Walter C. Meyer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 08:24
CPC Classifications
C; C09; C09D; C09D101/00; C09D101/08; C09D101/10; C09D101/14; C09D133/00; C09D133/04; C09D133/06; C09D133/10; C09D133/12; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31786; Y10T428/31855; Y10T428/31935; Y10T428/31971
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
304 words
A coating composition consisting essentially of 5-40% by weight of a film forming binder and 60-95% by weight of volatile organic solvents; wherein the binder consists essentially of about (a) 15-25% by weight, based on the weight of the binder, of polymethyl methacrylate having a relative viscosity of about 1.17 to 1.20 measured at 25° C. on a 0.5% polymer solids solution using dichloroethylene solvent; (b) 5-15% by weight, based on the weight of the binder, of a copolymer of units of methyl methacrylate and alkyl amino alkyl methacrylate having 1-4 carbon atoms in the alkyl groups and having a relative viscosity of about 1.17 to 1.20 measured as above; (c) 20-40% by weight, based on the weight of the binder, of a copolymer of units of methyl methacrylate and an alkyl acrylate having 2-8 carbon atoms in the alkyl group and having a relative viscosity of about 1.17 to 1.20 measured as above; (d) 5-25% by weight, based on the weight of the binder, of cellulose acetate butyrate having a viscosity of about 1-20 seconds and a butyryl content of 30-55% by weight; (e) 15-30% by weight, based on the weight of the binder, of a polyester plasticizer consisting essentially of the reaction product of a saturated fatty oil, a polyol and an organic dicarboxylic acid or an anhydride of an orginic dicarboxylic acid and having an acid number of about 0.1-10; and (f) 1-10% by weight, based on the weight of the binder, of a polymer of units of methyl methacrylate, an alkyl acrylate having 2-12 carbon atoms in the alkyl group and an α,β-unsaturated monocarboxylic acid and in which the polymer is reacted with an propylene imine and having a relative viscosity of about 1.17-1.20 measured as above; wherein the total of (a), (b), (c), (d), (e) and (f) are 100%
Claim 2
Dependent Claim
304 words
A coating composition consisting essentially of 5-40% by weight of a film forming binder and 60-95% by weight of volatile organic solvents; wherein the binder consists essentially of about (a) 15-25% by weight, based on the weight of the binder, of polymethyl methacrylate having a relative viscosity of about 1.17 to 1.20 measured at 25° C. on a 0.5% polymer solids solution using dichloroethylene solvent; (b) 5-15% by weight, based on the weight of the binder, of a copolymer of units of methyl methacrylate and alkyl amino alkyl methacrylate having 1-4 carbon atoms in the alkyl groups and having a relative viscosity of about 1.17 to 1.20 measured as above; (c) 20-40% by weight, based on the weight of the binder, of a copolymer of units of methyl methacrylate and an alkyl acrylate having 2-8 carbon atoms in the alkyl group and having a relative viscosity of about 1.17 to 1.20 measured as above; (d) 5-25% by weight, based on the weight of the binder, of cellulose acetate butyrate having a viscosity of about 1-20 seconds and a butyryl content of 30-55% by weight; (e) 15-30% by weight, based on the weight of the binder, of a polyester plasticizer consisting essentially of the reaction product of a saturated fatty oil, a polyol and an organic dicarboxylic acid or an anhydride of an orginic dicarboxylic acid and having an acid number of about 0.1-10; and (f) 1-10% by weight, based on the weight of the binder, of a polymer of units of methyl methacrylate, an alkyl acrylate having 2-12 carbon atoms in the alkyl group and an α,β-unsaturated monocarboxylic acid and in which the polymer is reacted with an propylene imine and having a relative viscosity of about 1.17-1.20 measured as above; wherein the total of (a), (b), (c), (d), (e) and (f) are 100%
Claim 3
Dependent Claim
21 words
The coating composition of claim 1 containing pigment in a pigment to binder weight ratio of about 1/100 to about 100/100.
Claim 4
Dependent Claim
31 words
The coating composition of claim 1 in which the methyl methacrylate and alkyl amino alkyl methacrylate copolymer consists essentially of units of methyl methacrylate and units of diethyl amino ethyl methacrylate.
Claim 5
Dependent Claim
33 words
The coating composition of claim 3 in which the copolymer consists essentially of about 90-99.5% by weight of units of methyl methacrylate and 0.5-10% by weight of units of diethyl amino ethyl methacrylate.
Claim 6
Dependent Claim
29 words
The coating composition of claim 1 in which the copolymer of methyl methacrylate and an alkyl acrylate consists essentially of units of methyl methacrylate and units of butyl acrylate.
Claim 7
Dependent Claim
31 words
The coating composition of claim 5 in which the copolymer consists essentially of about 80-90% by weight of units of methyl methacrylate and 10-20% by weight of units of butyl acrylate.
Claim 8
Dependent Claim
29 words
The coating composition of claim 1 in which the cellulose acetate butyrate is a mixture of a high viscosity cellulose acetate butyrate and a low viscosity cellulose acetate butyrate.
Claim 9
Dependent Claim
75 words
The coating composition of claim 7 in which the high viscosity cellulose acetate butyrate has a butyryl content of about 35-40% by weight and a viscosity of about 15-20 seconds and in which the low viscosity cellulose acetate butyrate has a butyryl content of 35-40% by weight and a viscosity of 1-3 seconds and in which the weight ratio of the high viscosity to low viscosity cellulose acetate butyrate is about 1:1 to about 1:6.
Claim 10
Dependent Claim
25 words
The coating composition of claim 1 in which the polyester plasticizer consists essentially of the reaction product of coconut oil, ethylene glycol and phthalic anhydride.
Claim 11
Dependent Claim
43 words
The coating composition of claim 1 in which the methyl methacrylate, alkyl acrylate, α,β-unsaturated monocarboxylic polymer reacted with an alkylene imine consists essentially of units of methyl methacrylate, units of ethyl acrylate, units of methacrylic acid and the alkylene imine is propylene imine.
Claim 12
Dependent Claim
45 words
The coating composition of claim 10 in which the polymer consists essentially of about 70-90% by weight of units of methyl methacrylate, 9-20% by weight of units of ethyl acrylate and 1-10% by weight of units of methacrylic acid which are reacted with propylene imine.
Claim 13
Dependent Claim
189 words
The coating composition of claim 2 in which the binder consists essentially of (a) polymethyl methacrylate (b) a copolymer consisting essentially of about 90-99.5% by weight of units of methyl methacrylate and 0.5-10% by weight of units of diethyl amino ethyl methacrylate; (c) a copolymer consisting essentially of 80-90% by weight of units of methyl methacrylate and 10-20% by weight of units of butyl acrylate; (d) a mixture of a high viscosity cellulose acetate butyrate having a butyryl content of about 35-40% by weight and a viscosity of about 15-20 seconds and a low viscosity cellulose acetate butyrate having a butyryl content of 35-40% by weight and a viscosity of about 1-3 seconds in which the ratio of the high to low viscosity cellulose acetate butyrate is about 1:1 to about 1:6; (e) a polyester plasticizer consisting essentially of the reaction product of coconut oil, ethylene glycol and phthalic anhydride; and (f) a polymer consisting essentially of about 70-90% by weight of units of methyl methacrylate, 9-20% by weight of units of ethyl acrylate and 1-10% by weight of units of methacrylic acid which are reacted with propylene imine.
Claim 14
Dependent Claim
230 words
A coating composition consisting essentially of 5-40% by weight of a film forming binder and 60-95% by weight of volatile organic solvents; wherein the binder consists essentially of about (a) 30-50% by weight, based on the weight of the binder, of polymethyl methacrylate having a relative viscosty of about 1.17-1.20 measured at 25° C. on a 0.5% polymer solids solution using dichloroethylene solvent; (b) 20-40% by weight, based on the weight of the binder, of cellulose acetate butyrate having a viscosity of about 1-3 seconds and a butyryl content of 30-55% by weight; (c) 5-15% by weight, based on the weight of the binder, of a phthalate ester plasticizer; (d) 10-30% by weight, based on the weight of the binder, of a polyester plasticizer consisting essentially of the reaction product of a saturated fatty oil, a polyol and an organic carboxylic acid or an anhydride of an organic dicarboxylic acid and having an acid number of about 0.1-10; and (e) 1-10% by weight, based on the weight of the binder, of a polymer of units of methyl methacrylate, an alkyl acrylate having 2-12 carbon atoms in the alkyl group and an α,β-unsaturated monocarboxylic acid and in which the polymer is reacted with an propylene imine and having a relative viscosity of about 1.17 to 1.20 measured as above; wherein the total of (a), (b), (c), (d) and (e) are 100%.
Claim 15
Dependent Claim
230 words
A coating composition consisting essentially of 5-40% by weight of a film forming binder and 60-95% by weight of volatile organic solvents; wherein the binder consists essentially of about (a) 30-50% by weight, based on the weight of the binder, of polymethyl methacrylate having a relative viscosty of about 1.17-1.20 measured at 25° C. on a 0.5% polymer solids solution using dichloroethylene solvent; (b) 20-40% by weight, based on the weight of the binder, of cellulose acetate butyrate having a viscosity of about 1-3 seconds and a butyryl content of 30-55% by weight; (c) 5-15% by weight, based on the weight of the binder, of a phthalate ester plasticizer; (d) 10-30% by weight, based on the weight of the binder, of a polyester plasticizer consisting essentially of the reaction product of a saturated fatty oil, a polyol and an organic carboxylic acid or an anhydride of an organic dicarboxylic acid and having an acid number of about 0.1-10; and (e) 1-10% by weight, based on the weight of the binder, of a polymer of units of methyl methacrylate, an alkyl acrylate having 2-12 carbon atoms in the alkyl group and an α,β-unsaturated monocarboxylic acid and in which the polymer is reacted with an propylene imine and having a relative viscosity of about 1.17 to 1.20 measured as above; wherein the total of (a), (b), (c), (d) and (e) are 100%.
Claim 16
Dependent Claim
21 words
The coating composition of claim 13 containing pigment in a pigment to binder weight ratio of about 1/100 to about 100/100.
Claim 17
Dependent Claim
31 words
The coating composition of claim 13 in which the methyl methacrylate and alkyl amino alkyl methacrylate copolymer consists essentially of units of methyl methacrylate and units of diethyl amino ethyl methacrylate.
Claim 18
Dependent Claim
33 words
The coating composition of claim 15 in which the copolymer consists essentially of about 90-99.5% by weight of, units of methyl methacrylate and 0.5-10% by weight of units of diethyl amino ethyl methacrylate.
Claim 19
Dependent Claim
19 words
The coating composition of claim 13 in which the phthalate plasticizer is butyl cyclohexyl phthalate or butyl benzyl phthalate.
Claim 20
Dependent Claim
25 words
The coating composition of claim 13 in which the polyester plasticizer consists essentially of the reaction product of coconut oil, ethylene glycol and phthalic anhydride.
Claim 21
Dependent Claim
39 words
The coating composition of claim 13 in which the methyl methacrylate, alkyl acrylate, α,β-unsaturated monocarboxylic polymer reacted with an alkylene imine consists essentially of units of methyl methacrylate, ethyl acrylate, methacrylic acid and the alkylene imine is propylene imine.
Claim 22
Dependent Claim
45 words
The coating composition of claim 13 in which the polymer consists essentially of about 70-90% by weight of units of methyl methacrylate, 9-20% by weight of units of ethyl acrylate and 1-10% by weight of units of methacrylic acid which are reacted with propylene imine.
Claim 23
Dependent Claim
101 words
The coating composition of claim 13 in which the binder consists essentially of (a) polymethyl methacrylate; (b) cellulose acetate butyrate having a viscosity of about 1-3 seconds and a butyryl content of about 35-40% by weight; (c) a phthalate plasticizer of butyl cyclohexyl phthalate; (d) a polyester plasticizer consisting essentially of the reaction product of coconut oil, ethylene glycol and phthalic anhydride; and (e) a polymer consisting essentially of about 70-90% by weight of units of methyl methacrylate, 9-20% by weight of units of ethyl acrylate and 1-10% by weight of units of methacrylic acid which are reacted with propylene imine.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-09-17 | 1983-03-19 | 1983-09-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-09-17 | 1987-03-19 | 1987-09-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-09-17 | 1991-03-19 | 1991-09-18 | $7700.00 | Window Closed / Lapsed |