Powdered metal filter composition and processes for producing the same
Assignee: Hoeganaes Corp
•
Filing: 1978-06-14
•
Granted: 1979-09-04
•
Expires: 1998-06-14
Abstract
Abstract A powdered metal filter composition and processes for producing the same by water atomization in which the composition exhibits an apparent density, compressibility and particle shape as a function of the composition chemistry and in particular the silicon, carbon and manganese content as well as the angle of intersection of the atomizing water jets; the composition providing an optimization of filtration efficiency, pressure drop across the filter pack, resistance to pressure deformation of the composition particles and the useful life of both the filter pack and the composition and the process producing such a composition with well-known apparatus and optimum yields of useful, particle-size fractions.
Inventors
- 👤 James G. Bewley
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 22:26
CPC Classifications
C; C22; C22C; C22C33/00; C22C33/02; C22C33/0257; C22C33/0278; C22C33/0285; B; B01; B01D; B01D39/00; B01D39/14; B01D39/20; B01D39/2027; B01D39/2031; B22; B22F; B22F9/00; B22F9/02; B22F9/06; B22F9/08; B22F9/082
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
51 words
A powdered metal composition consisting essentially of (a) a ferrous based alloy having by weight from approximately 0.60% to approximately 4.0% silicon; from approximately 0.08% to approximately 0.18% carbon; and from approximately 2.0% to 3.0% by weight molybdenum and exhibiting an apparent density of approximately 1.6 to 2.3 gm./cm. 3 .
Claim 2
Dependent Claim
51 words
A powdered metal composition consisting essentially of (a) a ferrous based alloy having by weight from approximately 0.60% to approximately 4.0% silicon; from approximately 0.08% to approximately 0.18% carbon; and from approximately 2.0% to 3.0% by weight molybdenum and exhibiting an apparent density of approximately 1.6 to 2.3 gm./cm. 3 .
Claim 3
Dependent Claim
24 words
A powdered metal composition in accordance with claim 1 in which the powder exhibits a compressibility of approximately 0.120 inches to approximately 0.160 inches.
Claim 4
Dependent Claim
20 words
A powdered metal composition in accordance with claim 1 or 2 having approximately 0.30% to approximately 0.90% by weight manganese.
Claim 5
Dependent Claim
38 words
A powdered metal composition in accordance with claim 1 or 2 having approximately 10.0% to approximately 15.0% by weight nickel; approximately 17.0% to 22% by weight chromium, and 0.30% to approximately 0.90% by manganese with the balance iron.
Claim 6
Dependent Claim
24 words
A powdered metal composition in accordance with claim 4 having a particle size distribution of from approximately 30 to approximately 100 mesh, U.S. Standard.
Claim 7
Dependent Claim
24 words
A powdered metal composition in accordance with claim 4 having a particle size distribution of from approximately 30 to approximately 60 mesh, U.S. Standard.
Claim 8
Dependent Claim
24 words
A powdered metal composition in accordance with claim 4 having a particle size distribution of from approximately 50 to approximately 100 mesh, U.S. Standard.
Claim 9
Dependent Claim
68 words
A powdered metal composition in accordance with claim 4 in which the apparent density varies as a function of the silicon and manganese content generally in accordance with the following formula: Δ Ad+(-)1.8(ΔS 1 )+ 0.16(Δ Mn) where Δ AD is the change in apparent density; Δ S 1 is the change in weight percent of silicon and Δ Mn is the change in weight percent of manganese.
Claim 10
Dependent Claim
32 words
A powdered metal composition consisting essentially of (a) a ferrous based alloy having by weight approximately 0.14% carbon; 0.60% manganese; 1.0% silicon; 12.0% nickel; 19.0% chromium; 2.2% molybdenum and the balance iron.
Claim 11
Dependent Claim
32 words
A powdered metal composition consisting essentially of (a) a ferrous based alloy having by weight approximately 0.14% carbon; 0.60% manganese; 1.0% silicon; 12.0% nickel; 19.0% chromium; 2.2% molybdenum and the balance iron.
Claim 12
Dependent Claim
40 words
A powdered metal composition in accordance with claim 9 exhibiting an apparent density of approximately 2.0 gm./cm 3 ; a compressibility of approximately 0.14 inches and a particle size distribution of from approximately 50 to approximately 100 mesh, U.S. Standard.
Claim 13
Dependent Claim
40 words
A powdered metal composition in accordance with claim 9 exhibiting an apparent density of approximately 1.85 gm./cm 3 ; a compressibility of approximately 0.150 inches and a particle size distribution of from approximately 30 to approximately 60 mesh, U.S. Standard.
Claim 14
Dependent Claim
60 words
A process for producing a powdered metal composition by water atomization in which (a) a stream of molten ferrous based metal alloy having by weight from approximately 0.60% to 4.0% silicon and approximately 0.08 to 0.18% carbon is impinged by water jets intersecting said stream at a common point and with an included angle from approximately 25° to approximately 45°.
Claim 15
Dependent Claim
60 words
A process for producing a powdered metal composition by water atomization in which (a) a stream of molten ferrous based metal alloy having by weight from approximately 0.60% to 4.0% silicon and approximately 0.08 to 0.18% carbon is impinged by water jets intersecting said stream at a common point and with an included angle from approximately 25° to approximately 45°.
Claim 16
Dependent Claim
61 words
A process for producing a powdered metal composition in accordance with claim 12 in which the powdered metal exhibits an apparent density of approximately 1.6 to 2.3 gm./cm 3 as a function of the said included angle in accordance with the following formula: ΔAD=(-)0.31Δ(Sin θ/2) where Δ AD is the change in apparent density and θ is the said included angle.
Claim 17
Dependent Claim
29 words
A process for producing a powdered metal composition in accordance with claim 12 or 13 in which the molten alloy has from approximately 0.30% to 0.90% by weight manganese.
Claim 18
Dependent Claim
45 words
A process for producing a powdered metal composition in accordance with claim 12 or 13 in which the molten alloy has by weight approximately from 10.0% to 15.0% nickel; 17.0% to 22.0% chromium; 2.0% to 3.0% molybdenum; 0.30% to 0.90% manganese and the balance iron.
Claim 19
Dependent Claim
23 words
A process for producing a powdered metal composition in accordance with claim 12 or 13 in which the included angle is approximately 38°.
Claim 20
Dependent Claim
47 words
A process for producing a powdered metal composition in accordance with claim 12 or 13 in which the water jets are fed by water under a pressure of approximately from 200 psi to 700 psi and the orifices are approximately 1/8 inch to 5/32 inch in diameter.
Claim 21
Dependent Claim
29 words
A process for producing a powdered metal composition in accordance with claim 12 or 13 in which the water pressure is limited to approximately 200 psi to 400 psi.
Claim 22
Dependent Claim
29 words
A process for producing a powdered metal composition in accordance with claim 12 or 13 in which the water pressure is limited to approximately 400 psi to 700 psi.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-09-03 | 1983-03-05 | 1983-09-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-09-03 | 1987-03-05 | 1987-09-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-09-03 | 1991-03-05 | 1991-09-04 | $7700.00 | Window Closed / Lapsed |