Pneumatic tire comprising polyisoprene rubber and alkali metal alginate in at least tread portion thereof adapted for travelling on frozen roads
Assignee: Bridgestone Corp
•
Filing: 1977-06-13
•
Granted: 1979-08-28
•
Expires: 1997-06-13
Abstract
Abstract A rubber composition containing polyisoprene rubber or a blend of polyisoprene rubber and polybutadiene rubber has a high friction coefficient against the frozen road surface due to the easy deformability at low temperature and high affinity for water. A pneumatic tire comprising a tread consisting of the rubber composition is excellent in the brake, traction and cornering performances and can travel safely on frozen roads without the use of spikes or a chain.
Inventors
- 👤 Noboru Kusakabe
- 👤 Nobumasa Ikeda
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 06:55
CPC Classifications
B; B60; B60C; B60C1/00; B60C1/0016
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
183 words
A pneumatic tire for travelling on frozen roads, wherein at least the ground contact portion thereof, including to the depth end of the grooves, is composed of a rubber composition consisting of a rubber component selected from the group consisting of polyisoprene rubber or a blend of polyisoprene rubber and polybutadiene rubber, an agent for improving affinity to water selected from the group consisting of alkali metal alginates, carbon black and a commonly used softener, vulcanizer and other compounding agents, the amount of said agent for improving affinity to water being 3-20 parts by weight based on 100 parts by weight of the rubber component, and said rubber composition having JIS hardnesses of 50-80 degrees at -30° C. and 50-65 degrees at 25° C., a tan δ peak temperature of not higher than -40° C. and an affinity for water of not lower than 6.5 cm 2 /cc, wherein if the rubber component is said blend it is a blend consisting of not less than 10 parts by weight of polyisoprene rubber and not more than 90 parts by weight of polybutadiene rubber.
Claim 2
Dependent Claim
183 words
A pneumatic tire for travelling on frozen roads, wherein at least the ground contact portion thereof, including to the depth end of the grooves, is composed of a rubber composition consisting of a rubber component selected from the group consisting of polyisoprene rubber or a blend of polyisoprene rubber and polybutadiene rubber, an agent for improving affinity to water selected from the group consisting of alkali metal alginates, carbon black and a commonly used softener, vulcanizer and other compounding agents, the amount of said agent for improving affinity to water being 3-20 parts by weight based on 100 parts by weight of the rubber component, and said rubber composition having JIS hardnesses of 50-80 degrees at -30° C. and 50-65 degrees at 25° C., a tan δ peak temperature of not higher than -40° C. and an affinity for water of not lower than 6.5 cm 2 /cc, wherein if the rubber component is said blend it is a blend consisting of not less than 10 parts by weight of polyisoprene rubber and not more than 90 parts by weight of polybutadiene rubber.
Claim 3
Dependent Claim
14 words
The tire according to claim 1, wherein the rubber component is said polyisoprene rubber.
Claim 4
Dependent Claim
37 words
The tire according to claim 1, wherein the rubber component is a rubber blend consisting of not less than 50 parts by weight of polyisoprene rubber and not more than 50 parts by weight of polybutadiene rubber.
Claim 5
Dependent Claim
44 words
The tire according to claim 1, wherein the rubber composition has a JIS hardnesses of 72 degrees at -30° C. and 55 degrees at 25° C. a tan δ peak temperature of -40° C. and an affinity for water of 6.8 cm 2 /cc.
Claim 6
Dependent Claim
67 words
The tire according to claim 1, wherein the rubber composition is a blend of 50 parts by weight of polyisoprene rubber and 50 parts by weight of polybutadiene rubber as said rubber component and has JIS hardnesses of 63 degrees at -30° C. and 54 degrees at 25° C., a tan δ peak temperature of -50° C. and an affinity for water of 6.6 cm 2 /cc.
Claim 7
Dependent Claim
75 words
The tire according to claim 1, wherein the rubber composition is a blend of 50 parts by weight of polyisoprene rubber and 50 parts by weight of polybutadiene rubber as said rubber component and 10 parts by weight of sodium alginate, and has JIS hardnesses of 64 degrees at -30° C. and 55 degrees at 25° C., a tan δ peak temperature of -50° C. and an affinity for water of 7.0 cm 2 /cc.
Claim 8
Dependent Claim
52 words
A pneumatic tire for travelling on frozen roads, comprising a tread including a cap having a thickness from the ground contact surface to the depth of the grooves and a width extending over all the ground contact area of the tread, said cap consisting of a rubber composition according to claim 1.
Claim 9
Dependent Claim
14 words
The tire according to claim 1, wherein said alkali metal alginate is sodium alginate.
Claim 10
Dependent Claim
13 words
The tire of claim 10, wherein said alkali metal alginate is sodium alginate.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-08-27 | 1983-02-26 | 1983-08-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-08-27 | 1987-02-26 | 1987-08-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-08-27 | 1991-02-26 | 1991-08-28 | $7700.00 | Window Closed / Lapsed |