US4165351A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of manufacturing a metal oxide varistor
Assignee: General Electric Co
•
Filing: 1977-03-23
•
Granted: 1979-08-21
•
Expires: 1997-03-23
Abstract
Abstract Disclosed is a method of manufacturing a metal oxide varistor body. Conventional manufacturing techniques through sintering are utilized on any metal oxide varistor formulation which includes bismuth oxide. Following sintering, the devices are heat treated at a temperature between 750° C. and 1200° C. for a time in excess of about 10 hours. The heat treatment increases the alpha of the devices and substantially lowers the leakage current.
Inventors
- 👤 John E. May
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 09:04
CPC Classifications
H; H01; H01C; H01C7/00; H01C7/10; H01C7/105; H01C7/108; H01C7/112
Claims Analysis
Total Claims: 39
Claim 1
Independent Claim
105 words
A method for making metal oxide varistor bodies comprising: combining a zinc oxide base material with a small amount of a plurality of preselected additives in particulate form to provide a final mixture, at least one of said additives being bismuth oxide; pressing and sintering a portion of such final mixture to provide a fused body; heat treating said fused body after said sintering by maintaining said body at a temperature of between about 750° C. and 1200° C. for a time of at about ten hours or more to significantly reduce the leakage current as well as to increase the alpha of said body.
Claim 2
Independent Claim
105 words
A method for making metal oxide varistor bodies comprising: combining a zinc oxide base material with a small amount of a plurality of preselected additives in particulate form to provide a final mixture, at least one of said additives being bismuth oxide; pressing and sintering a portion of such final mixture to provide a fused body; heat treating said fused body after said sintering by maintaining said body at a temperature of between about 750° C. and 1200° C. for a time of at about ten hours or more to significantly reduce the leakage current as well as to increase the alpha of said body.
Claim 3
Dependent Claim
34 words
The method of claim 1 wherein said heat treating comprises heat treating said fused body by maintaining said body at a substantially constant temperature in the range of about 800° C. to 1200° C.
Claim 4
Dependent Claim
18 words
The method of claim 2 wherein the leakage current is reduced by at least a factor of 2.
Claim 5
Dependent Claim
30 words
The method of claim 3 wherein said heat treatment step comprises maintaining said body between about 800° C. and 1200° C. during the cool down portion of the sintering cycle.
Claim 6
Independent Claim
117 words
A method for making metal oxide varistor bodies comprising: combining a zinc oxide base material with a small amount of a plurality of preselected additives in particulate form to provide a final mixture, at least one of said additives being bismuth oxide; pressing and sintering a portion of said final mixture to provide a fused body; cooling said fused body to a temperature substantially less than 750° C.; heat treating said fused body by reheating said body to a temperature in the range of about 750° C. to 1200° C. for a time of about ten hours or more sufficient to significantly reduce the leakage current of said body as well as to significantly increase the alpha.
Claim 7
Independent Claim
117 words
A method for making metal oxide varistor bodies comprising: combining a zinc oxide base material with a small amount of a plurality of preselected additives in particulate form to provide a final mixture, at least one of said additives being bismuth oxide; pressing and sintering a portion of said final mixture to provide a fused body; cooling said fused body to a temperature substantially less than 750° C.; heat treating said fused body by reheating said body to a temperature in the range of about 750° C. to 1200° C. for a time of about ten hours or more sufficient to significantly reduce the leakage current of said body as well as to significantly increase the alpha.
Claim 8
Dependent Claim
18 words
The method of claim 5 wherein said leakage current is reduced by at least a factor of 2.
Claim 9
Independent Claim
88 words
A method for making metal oxide varistor bodies comprising: combining a zinc oxide base material with a small amount of a plurality of preselected additives in particulate form to provide a final mixture, at least one of said additives being bismuth oxide; pressing and sintering a portion of such final mixture to provide a fused body; heat treating said fused body by maintaining said body at a temperature of between about 750° C. and 1200° C. for a time sufficient to significantly increase the alpha of said body.
Claim 10
Independent Claim
88 words
A method for making metal oxide varistor bodies comprising: combining a zinc oxide base material with a small amount of a plurality of preselected additives in particulate form to provide a final mixture, at least one of said additives being bismuth oxide; pressing and sintering a portion of such final mixture to provide a fused body; heat treating said fused body by maintaining said body at a temperature of between about 750° C. and 1200° C. for a time sufficient to significantly increase the alpha of said body.
Claim 11
Dependent Claim
34 words
The method of claim 7 wherein said heat treating comprises heat treating said fused body by maintaining said body at a substantially constant temperature in the range of about 750° C. to 1200° C.
Claim 12
Dependent Claim
17 words
The method of claim 8 wherein said heat treating comprises heating treating for at least ten hours.
Claim 13
Dependent Claim
33 words
The method of claim 9 wherein said pressing and sintering step includes a cooling step and wherein said heat treating comprises maintaining said fused body at said constant temperature during said cooling operation.
Claim 14
Dependent Claim
17 words
The method of claim 9 wherein said alpha is increased by at least a factor of 2.
Claim 15
Dependent Claim
36 words
The method of claim 11 wherein said pressing and sintering step includes a cooling step and wherein said heat treating comprises maintaining said fused body at said constant temperature during a portion of said cooling step.
Claim 16
Independent Claim
94 words
A method for making metal oxide varistor bodies comprising: combining a zinc oxide base material with a small amount of a plurality of preselected additives in particulate form to provide a final mixture, at least one of said additives being bismuth oxide; pressing and sintering a portion of said final mixture to provide a fused body; cooling said fused body; heat treating said fused body by reheating said body to a temperature in the range of about 750° C. to 1200° C. for a time sufficient to significantly increase the alpha of said body.
Claim 17
Independent Claim
94 words
A method for making metal oxide varistor bodies comprising: combining a zinc oxide base material with a small amount of a plurality of preselected additives in particulate form to provide a final mixture, at least one of said additives being bismuth oxide; pressing and sintering a portion of said final mixture to provide a fused body; cooling said fused body; heat treating said fused body by reheating said body to a temperature in the range of about 750° C. to 1200° C. for a time sufficient to significantly increase the alpha of said body.
Claim 18
Dependent Claim
17 words
The method of claim 13 wherein said alpha is increased by at least a factor of 2.
Claim 19
Dependent Claim
17 words
The method of claim 13 wherein said reheating comprises reheating said body for at least ten hours.
Claim 20
Dependent Claim
17 words
The method of claim 15 wherein said alpha is increased by at least a factor of 2.
Claim 21
Dependent Claim
30 words
The method of claim 13 wherein said heat treating comprises reheating said fused body to a substantially constant temperature in the range of between about 750° C. and 1200° C.
Claim 22
Independent Claim
100 words
A method for making metal oxide varistor bodies comprising: combining a zinc oxide base material with a small amount of a plurality of preselected additives in particulate form to provide a final mixture, at least one of said additives being bismuth oxide; pressing and sintering a portion of such final mixture to provide a fused body; heat treating said fused body by maintaining said body at a temperature of between about 750° C. and 1200° C. for a time sufficient to cause a significant portion of the bismuth oxide in said body to convert to a body centered cubic phase.
Claim 23
Independent Claim
100 words
A method for making metal oxide varistor bodies comprising: combining a zinc oxide base material with a small amount of a plurality of preselected additives in particulate form to provide a final mixture, at least one of said additives being bismuth oxide; pressing and sintering a portion of such final mixture to provide a fused body; heat treating said fused body by maintaining said body at a temperature of between about 750° C. and 1200° C. for a time sufficient to cause a significant portion of the bismuth oxide in said body to convert to a body centered cubic phase.
Claim 24
Dependent Claim
21 words
The method of claim 18 wherein said heat treating comprises maintaining said body at a substantially constant temperature in said range.
Claim 25
Dependent Claim
24 words
The method of claim 18 wherein said heat treating comprises maintaining said body at said temperature for a period in excess of ten hours.
Claim 26
Dependent Claim
29 words
The method of claim 20 wherein said heat treating comprises maintaining said temperature at a substantially constant level in the range of between about 750° C. and 1200° C.
Claim 27
Dependent Claim
22 words
The method of claim 20 wherein substantially all of said bismuth oxide in said body is converted to a body-centered cubic phase.
Claim 28
Dependent Claim
22 words
The method of claim 21 wherein substantially all of said bismuth oxide in said body is converted to a body-centered cubic phase.
Claim 29
Dependent Claim
31 words
The method of claim 20 wherein said pressing and sintering step includes a cooling step and wherein said heat treating comprises maintaining said body in said range during said cooling step.
Claim 30
Independent Claim
105 words
A method for making metal oxide varistor bodies comprising: combining a zinc oxide base material with a small amount of a plurality of preselected additives in particulate form to provide a final mixture, at least one of said additives being bismuth oxide; pressing and sintering a portion of said final mixture to provide a fused body; cooling said fused body; heat treating said fused body by reheating said body to a temperature in the range of about 750° C. to 1200° C. for a time sufficient to cause a significant portion of the bismuth oxide in said body to convert to a body-centered cubic phase.
Claim 31
Independent Claim
105 words
A method for making metal oxide varistor bodies comprising: combining a zinc oxide base material with a small amount of a plurality of preselected additives in particulate form to provide a final mixture, at least one of said additives being bismuth oxide; pressing and sintering a portion of said final mixture to provide a fused body; cooling said fused body; heat treating said fused body by reheating said body to a temperature in the range of about 750° C. to 1200° C. for a time sufficient to cause a significant portion of the bismuth oxide in said body to convert to a body-centered cubic phase.
Claim 32
Dependent Claim
19 words
The method of claim 25 wherein substantially all of said bismuth oxide is converted to the body-centered cubic phase.
Claim 33
Dependent Claim
36 words
The method of claim 25 wherein said heat treating comprises heat treating said fused body by heating it to a preselected elevated temperature within said temperature range for a time in excess of about ten hours.
Claim 34
Dependent Claim
34 words
The method of claim 25 wherein said heat treating comprises heat treating said fused body by maintaining said body at a substantially constant temperature in the range of about 750° C. to 1200° C.
Claim 35
Dependent Claim
19 words
The method of claim 27 wherein substantially all of said bismuth oxide is converted to the body-centered cubic phase.
Claim 36
Dependent Claim
44 words
The method of claim 1 wherein said additives consist essentially of a mixture of the the oxides of cobalt, manganese and titanium and said step of heat treating is carried out at a temperature in the range of about 750° C. to 850° C.
Claim 37
Dependent Claim
51 words
The method of claim 1 wherein said additives consist essentially of a mixture of the oxides of manganese, cobalt, tin, antimony and boron, said additives also comprising barium carbonate and said step of heat treating is carried out at a temperature in the range of about 800° C. to 1150° C.
Claim 38
Dependent Claim
27 words
The method of claim 31 wherein said step of heat treating is carried out at a temperature in the range of about 800° C. to 1100° C.
Claim 39
Dependent Claim
20 words
The method of claim 4 wherein the varistor voltage of said varistor is increased by said step of heat treating.
References Cited (Backward Citations)
US3899451A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-08-20 | 1983-02-19 | 1983-08-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-08-20 | 1987-02-19 | 1987-08-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-08-20 | 1991-02-19 | 1991-08-21 | $7700.00 | Window Closed / Lapsed |