Process for preparing an element of a dual-in-line ceramic package provided with a layer of sealing glass
Assignee: Narumi China Corp
•
Filing: 1978-03-29
•
Granted: 1979-08-21
•
Expires: 1998-03-29
Abstract
Abstract An element of a dual-in-line ceramic package such as a substrate or cover provided with a layer of sealing glass is prepared by forming powdered low-melting sealing glass into a shape conforming to that of the element, compressing and sintering the shaped powdered glass to form a solid sintered sealing glass preform, applying the preform to the surface of the element, and fusing it thereto by heating the assembly.
Inventors
- 👤 Katsuhiko Kita
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 04:21
CPC Classifications
H; H10; H10W; H10W76/00; H10W76/10; H10W76/12; H10W76/15; H10W76/157; H10W95/00
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
111 words
In a process for hermetically sealing together the substrate and cover of a ceramic dual-in-line package, the improvement comprising: (1) forming powdered low-melting sealing glass into a shape corresponding to the peripheral area of said substrate and/or cover, (2) compressing and sintering said shaped powdered sealing glass, whereby a solid sintered sealing glass preform is produced, (3) positioning said preform together with a lead frame between said substrate and cover of said dual-in-line ceramic package to be sealed, whereby an assembly of said substrate, lead frame, preform and cover is produced, (4) heating said assembly to fuse said sealing glass, whereby an hermetic seal is formed between said substrate and cover.
Claim 2
Dependent Claim
111 words
In a process for hermetically sealing together the substrate and cover of a ceramic dual-in-line package, the improvement comprising: (1) forming powdered low-melting sealing glass into a shape corresponding to the peripheral area of said substrate and/or cover, (2) compressing and sintering said shaped powdered sealing glass, whereby a solid sintered sealing glass preform is produced, (3) positioning said preform together with a lead frame between said substrate and cover of said dual-in-line ceramic package to be sealed, whereby an assembly of said substrate, lead frame, preform and cover is produced, (4) heating said assembly to fuse said sealing glass, whereby an hermetic seal is formed between said substrate and cover.
Claim 3
Dependent Claim
59 words
The process of claim 1, wherein said preform is prepared by mixing said powdered low-melting sealing glass with a binder, whereby a powder is formed, forming said powder into a shape corresponding to the peripheral area of the substrate and/or cover of a ceramic dual-in-line package, compressing said formed powder, whereby a blank is formed, and sintering said blank.
Claim 4
Dependent Claim
21 words
The process of claim 2, wherein the pressure used in compressing said shaped powder is at least 600 kg/cm 2 .
Claim 5
Dependent Claim
18 words
The process of claim 3, wherein said pressure is between 600 kg/cm 2 and 1000 kg/cm 2 .
Claim 6
Dependent Claim
48 words
The process of claim 2, wherein said sintering is accomplished by gradually increasing the temperature of said blank in a range from 300° C. to 340° C. whereby said binder is removed and subsequently heating said blank to a temperature of about 390° C. to complete the sintering.
Claim 7
Dependent Claim
22 words
The process of claim 5, wherein said heating from 300° C. to 390° C. takes place over a period of 1.5 hours.
Claim 8
Dependent Claim
12 words
The process of claim 2, wherein said binder is an acrylic resin.
Claim 9
Dependent Claim
41 words
The process of claim 1, wherein said preform is prepared by sintering powdered low-melting sealing glass under pressure in a die at a temperature above the glass transition temperature of said sealing glass and below the softening point of said glass.
Claim 10
Dependent Claim
15 words
The process of claim 8, wherein said pressure is at least 500 kg/cm 2 .
Claim 11
Dependent Claim
27 words
A process according to claim 1, wherein, before said preform is positioned between said substrate and said cover, said preform is fused to said substrate and/or cover.
References Cited (Backward Citations)
US2466849A
Cited
US2842500A
Cited
US3725186A
Cited
US3988405A
Cited
US4009238A
Cited
US4021216A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-08-20 | 1983-02-19 | 1983-08-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-08-20 | 1987-02-19 | 1987-08-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-08-20 | 1991-02-19 | 1991-08-21 | $7700.00 | Window Closed / Lapsed |