Process for the production of β-lithium aluminate and needle-shaped product
Assignee: Evonik Operations GmbH
•
Filing: 1978-03-14
•
Granted: 1979-08-14
•
Expires: 1998-03-14
Abstract
Abstract A process for the production of β-lithium aluminate LiAlO 2 , is disclosed wherein a lithium hydroxide aluminate of the formula: Li 2 O . Al 2 O 3 . nH 2 O is precipitated from aqueous solutions which contain the lithium ions and aluminum in ionogenic or elementary form at a pH value above 7. The concentration of the two metal components is at least 0.1, at most 6 g-atoms per liter, preferably 2 to 5 g-atoms per liter. The precipitation product is washed and dried and then is converted by annealing into β-lithium aluminate, in the temperature range between 200° C. and 800° C., preferably 400° C.-650° C., and especially 450° C.-550° C. The β-LiAlO 2 obtained thereby has a lamellae-shaped or fine crystalline form which is converted into a needle-shaped, crystalline lithium aluminate, is obtained by the process of the invention and is suitable for the construction of electrolyte matrices.
Inventors
- 👤 Martin Feldmann
- 👤 Edgar Koberstein
- 👤 Klaus Seibold
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 11:11
CPC Classifications
H; H01; H01M; H01M8/00; H01M8/02; H01M8/0289; H01M8/0295; C; C01; C01F; C01F7/00; C01F7/02; C01F7/04; C01F7/043; Y; Y02; Y02E; Y02E60/00; Y02E60/10; Y02E60/30; Y02E60/50; Y02P; Y02P70/00; Y02P70/50
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
125 words
A process for the production of β-lithium aluminate which has the formula: LiAl0 2 , comprising forming an aqueous solution containing lithium ions and aluminum in ionogenic or elementary form, precipitating a lithium hydroxoaluminate of the composition Li 2 O.Al 2 O 3 .nH 2 O wherein n is at least 1 from said aqueous solution at a pH value above 7 and at concentrations of the two metal components of at least 0.1 g-atoms/liter, at most 6 g-atoms per liter, wherein Li and Al are present in equimolar ratios or wherein there is an excess of Li present, washing the product obtained by said precipitating and converting said product by annealing in the temperature range between 200° C. and 800° C. into β-lithium aluminate.
Claim 2
Dependent Claim
125 words
A process for the production of β-lithium aluminate which has the formula: LiAl0 2 , comprising forming an aqueous solution containing lithium ions and aluminum in ionogenic or elementary form, precipitating a lithium hydroxoaluminate of the composition Li 2 O.Al 2 O 3 .nH 2 O wherein n is at least 1 from said aqueous solution at a pH value above 7 and at concentrations of the two metal components of at least 0.1 g-atoms/liter, at most 6 g-atoms per liter, wherein Li and Al are present in equimolar ratios or wherein there is an excess of Li present, washing the product obtained by said precipitating and converting said product by annealing in the temperature range between 200° C. and 800° C. into β-lithium aluminate.
Claim 3
Dependent Claim
18 words
The process of claim 1 wherein the concentration of the said metal components is 2 to 5 g-atoms/liter.
Claim 4
Dependent Claim
16 words
The process of claim 1 wherein the temperature of annealing is 400° C. to 650° C.
Claim 5
Dependent Claim
16 words
The process of claim 1 wherein the temperature of annealing is 450° C. to 550° C.
Claim 6
Dependent Claim
20 words
The process of claim 1 wherein the precipitation is carried out at a temperature between 20° C. and 100° C.
Claim 7
Dependent Claim
20 words
The process of claim 1 wherein the precipitation is carried out at a temperature between 40° C. and 60° C.
Claim 8
Dependent Claim
19 words
The process of claim 1 wherein the precipitation product is dried and is annealed for at least 2 hours.
Claim 9
Dependent Claim
26 words
The process of claim 1 wherein the dried precipitation product is dried and annealed at temperatures between 450° C. and 550° C., for approximately 25 hours.
Claim 10
Dependent Claim
29 words
The process of claim 1 wherein the water contained in the precipitation product is exchanged for a water miscible, volatile, organic liquid which is then removed by flashing off.
Claim 11
Dependent Claim
33 words
The process of claim 1 wherein the β-lithium aluminate obtained is converted into a needle crystalline shape by annealing in an alkali carbonate melt in the temperature range between about 497° C.-800° C.
Claim 12
Dependent Claim
24 words
The process of claim 10 wherein the temperature of the annealing in the alkali carbonate melt is about 550° C. to about 600° C.
Claim 13
Dependent Claim
18 words
The process of claim 10 wherein the annealing is accomplished at 550° C. for more than 10 hours.
Claim 14
Dependent Claim
14 words
The process of claim 12 wherein the annealing is carried out for 25 hours.
Claim 15
Dependent Claim
12 words
Needle-shaped crystalline β-lithium aluminate obtained according to the process of claim 10.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-08-13 | 1983-02-12 | 1983-08-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-08-13 | 1987-02-12 | 1987-08-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-08-13 | 1991-02-12 | 1991-08-14 | $7700.00 | Window Closed / Lapsed |