Assignee: Akzo NV
•
Filing: 1977-06-23
•
Granted: 1979-08-14
•
Expires: 1997-06-23
Abstract
Abstract A dialyzing membrane, especially for hemodialysis, formed as a hollow fiber, tubular foil or flat sheet by regeneration of cellulose from a cuprammonium solution, the membrane comprising at least two firmly adhered cellulosic layers including at least one dialyzing layer consisting essentially of a semipermeable regenerated cellulose and at least one adsorbent layer consisting of said regenerated cellulose containing embedded therein fine particles of an adsorbent material in an amount of up to 95% by weight with reference to the dry weight of the adsorbent layer, preferably 1 to 90% and especially 20 to 70% by weight, when the adsorbent layer is part of a hollow fiber structure. The dialyzing membrane of the invention is produced by a method requiring at least two cuprammonium cellulose solutions, one of which is free of adsorbent particles and another of which contains a suspension of adsorbent particles, the different solutions being spun from adjacent spinning slots for immediate layer to layer contact and then introduced over a short air gap into a coagulating or precipitating bath to entrap the adsorbent particles in the spun layer in which the particles were originally suspended. Isopropyl myristate is particularly advantageous as a liquid filler for the axial duct or canal of a hollow membrane.
Inventors
- 👤 Werner Henne
- 👤 Gustav Dunweg
- 👤 Werner Schmitz
- 👤 Raimund Pohle
- 👤 Friedrich Lawitzki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 15:36
CPC Classifications
B; B01; B01D; B01D71/00; B01D71/06; B01D71/08; B01D71/10; B01D69/00; B01D69/04; B01D69/06; B01D69/08; B01D69/12; B01D69/1212; B01D69/1216; B01D69/14; B01D69/141; B01D69/147
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
192 words
A method of producing a multilayer dialyzing membrane composed of two or more firmly adhered cellulosic layers formed by regeneration of cellulose from a cuprammonium solution, including at least one layer consisting essentially of a semipermeable regenerated cellulose and at least one other layer consisting essentially of a regenerated cellulose containing embedded therein fine particles of an adsorbent material, which method comprises: spinning at least two cuprammonium spinning solutions from adjacent slots of a spinning head for immediate layer to layer contact and conducting the spun contacting layers over an air gap of not more than 50 times the spacing of the adjacent slots to pass into a precipitating bath, one of said at least two cuprammonium spinning solutions having suspended therein said fine particles of an adsorbent material in an amount of up to 95% by weight and another of said at least two cuprammonium spinning solutions being free of adsorbent particles; coagulating the layers of spinning solutions in said precipitating bath to firmly adhere to each other and to entrap the fine particles of adsorbent material substantially completely in the spun layer in which said adsorbent material was originally suspended.
Claim 2
Independent Claim
192 words
A method of producing a multilayer dialyzing membrane composed of two or more firmly adhered cellulosic layers formed by regeneration of cellulose from a cuprammonium solution, including at least one layer consisting essentially of a semipermeable regenerated cellulose and at least one other layer consisting essentially of a regenerated cellulose containing embedded therein fine particles of an adsorbent material, which method comprises: spinning at least two cuprammonium spinning solutions from adjacent slots of a spinning head for immediate layer to layer contact and conducting the spun contacting layers over an air gap of not more than 50 times the spacing of the adjacent slots to pass into a precipitating bath, one of said at least two cuprammonium spinning solutions having suspended therein said fine particles of an adsorbent material in an amount of up to 95% by weight and another of said at least two cuprammonium spinning solutions being free of adsorbent particles; coagulating the layers of spinning solutions in said precipitating bath to firmly adhere to each other and to entrap the fine particles of adsorbent material substantially completely in the spun layer in which said adsorbent material was originally suspended.
Claim 3
Dependent Claim
82 words
A method as claimed in claim 1 wherein two cuprammonium cellulose solutions are spun into a hollow fiber having a central axial duct from a bicomponent hollow fiber spinning nozzle, one of the two solutions containing from 0.1 to 90% by weight, with reference to its cellulosic content, of said adsorbent material in a particle size of up to about 40μ, and the other of said two solutions consisting essentially of a substantially pure cellulose or cellulose derivative in a cuprammonium solution.
Claim 4
Dependent Claim
25 words
A method as claimed in claim 2 wherein isopropyl myristrate is injected into the central axial duct of said hollow fiber as it is produced.
Claim 5
Dependent Claim
30 words
A method as claimed in claim 1 wherein said at least two cuprammonium solutions are spun into a layered flat sheet or foil from adjacent slots of sheet-forming spinning extruder.
Claim 6
Dependent Claim
56 words
A method as claimed in claim 1 wherein said at least two cuprammonium solutions are spun into a tubular foil from adjacent annular slots of a tube-forming extrusion head having means to inject a fluid under pressure along the center hollow axis of the tube, simultaneously injecting said fluid under pressure into said center hollow axis.
Claim 7
Dependent Claim
19 words
A method as claimed in claim 5 wherein the tubular foil is flattened after entry into said precipitating bath.
Claim 8
Dependent Claim
14 words
A method as claimed in claim 5 wherein the injected fluid is isopropyl myristate.
Claim 9
Dependent Claim
47 words
A method as claimed in claim 1 wherein each layer containing said adsorbent material is spun and coagulated into a layer thickness of about 10 to 100μ and each layer free of adsorbent particles is spun and coagulated into a layer thickness of about 1 to 10μ.
Claim 10
Dependent Claim
33 words
A method as claimed in claim 8 wherein the spun contacting layers are passed through an air gap of from about 15 up to 50 times the spacing of the adjacent spinning slots.
Claim 11
Dependent Claim
81 words
A method as claimed in claim 9 wherein two cuprammonium cellulose solutions are spun into a hollow fiber having a central axial duct from a bicomponent hollow fiber spinning nozzle, one of the two solutions containing from 0.1 to 90% by weight, with reference to its cellulosic content, of said adsorbent material in a particle size of up to 40μ, and the other of said two solutions consisting essentially of a substantially pure cellulose or cellulose derivative in a cuprammonium solution.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-08-13 | 1983-02-12 | 1983-08-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-08-13 | 1987-02-12 | 1987-08-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-08-13 | 1991-02-12 | 1991-08-14 | $7700.00 | Window Closed / Lapsed |