Coupled block copolymers with improved tack for adhesives

Claim 2

The process for the preparation of a coupled block copolymer which comprises the steps of polymerizing a first monomer selected from monovinyl aromatic hydrocarbons under solution polymerization conditions employing a hydrocarbon diluent, a first effective increment of a hydrocarbylmonolithium initiator, at effective conditions of temperature, pressure, and time, adding to the still-living polymerization admixture resulting therefrom at least one second monomer selected from conjugated dienes, together with a second effective increment of a hydrocarbyllithium initiator, provided that said second initiator increment is greater than said first initiator increment, and continuing said polymerization, and thereafter treating the resulting polymerization admixture with an effective amount of a coupling agent which is at least difunctional, thereby producing a mixture of coupled block copolymers exhibiting effective properties in adhesive formulations.

Claim 3

The process according to claim 1 wherein said monovinyl aromatic hydrocarbon contains 8 to 12 carbon atoms per molecule, and said conjugated diene contains 4 to 8 carbon atoms per molecule.

Claim 4

The process according to claim 2 wherein said solution polymerization conditions include a polymerization temperature in the range of about -20° C. to 150° C., and a pressure sufficient to maintain reactants and diluents substantially in the liquid phase.

Claim 5

The process according to claim 3 wherein said hydrocarbyllithium initiator is employed in a range of about 0.001 to 3 phm in each of said first initiator addition and second initiator addition.

Claim 6

The process according to claim 4 wherein said polymerization of said first monomer is conducted in the further presence of a polar organic compound in the range of about 0.001 to 10 phm.

Claim 7

The process according to claim 4 employing a weight ratio of said conjugated diene:monovinyal aromatic hydrocarbon in the range of about 50:50 to 95:5.

Claim 8

The process according to claim 6 wherein said monovinyl aromatic hydrocarbon is styrene, 1-vinylnaphthalene, 2-vinylnaphthalene, 3-methylstyrene, or 4-propylstyrene; and said conjugated diene is 1,3-butadiene, isoprene, 2,3-dimethyl-1,3-butadiene, piperylene, 1,3-hexadiene, 3,4-dimethyl-1,3-hexadiene, or 1,3-octadiene.

Claim 9

The process according to claim 7 employing a weight ratio of said conjugated diene:monovinyl aromatic hydrocarbon in the range of about 85:15 to 70:30, wherein said monovinylarene is styrene, and said conjugated diene is butadiene.

Claim 10

The process according to claim 8 wherein said hydrocarbyllithium initiator is n-butyllithium, said organic polar compound is tetrahydrofuran, and said ratio is about 80 butadiene:20 styrene, and wherein said coupling agent is silicon tetrachloride.

Claim 11

The process according to claim 4 wherein the amount of said hydrocarbyllithium initiator added as said second initiator amount is at least about 1 percent by weight to 400 percent by weight greater than the amount added as said first initiator amount.

Claim 12

The process according to claim 4 wherein said polymerization employs said hydrocarbyllithium initiator in a range of about 0.01 to 0.3 phm in said first initiator increment, and about 0.01 to 0.3 in said second initiator increment, with a proviso that said second increment is greater than said first increment by at least about 0.01 phm.

Claim 13

The process according to claim 1 wherein said coupling agent is a multivinyl aromatic compound, multiepoxide, multiiscocyanate, multiimine, multialdehyde, multiketone, multihalide, multianhydride, multiester as the ester of a polyalcohol with a monocarboxylic acids, or diester as the ester of a monohydric alcohol with a dicarboxylic acid, or mixtures.

Claim 14

The process according to claim 12 wherein said coupling agent is a multihalide and is a silicon halide.

Claim 15

The process according to claim 12 employing about 0.01 to 4.5 equivalents of coupling agent per equivalent of polymer-lithium.

Claim 16

The copolymeric product produced by the process which comprises the steps of polymerizing a first monomer selected from monovinyl aromatic hydrocarbons under solution polymerization conditions employing a hydrocarbon diluent, a first effective increment of a hydrocarbylmonolithium initiator, at effective conditions of temperature, pressure, and time, adding to the still-living polymerization admixture resulting therefrom at least one second monomer selected from conjugated dienes, together with a second effective increment of a hydrocarbyllithium initiator, provided that said second initiator increment is greater than said first initiator increment, and continuing said polymerization, and thereafter treating the resulting polymerization admixture with an effective amount of a coupling agent which is at least difunctional, thereby producing a mixture of coupled block copolymers exhibiting effective properties in adhesive formulations.

Claim 17

The copolymeric product produced by the process which comprises the steps of polymerizing a first monomer selected from monovinyl aromatic hydrocarbons under solution polymerization conditions employing a hydrocarbon diluent, a first effective increment of a hydrocarbylmonolithium initiator, at effective conditions of temperature, pressure, and time, adding to the still-living polymerization admixture resulting therefrom at least one second monomer selected from conjugated dienes, together with a second effective increment of a hydrocarbyllithium initiator, provided that said second initiator increment is greater than said first initiator increment, and continuing said polymerization, and thereafter treating the resulting polymerization admixture with an effective amount of a coupling agent which is at least difunctional, thereby producing a mixture of coupled block copolymers exhibiting effective properties in adhesive formulations.

Claim 18

The adhesive composition employing 100 parts by weight of coupled block copolymer, about 40-150 parts tackifier, up to 100 parts plasticizer, 0.1-5 parts stabilizer, optionally employing solvent in the range of 75-2000 parts or water in the range of about 5-250 parts, wherein said coupled block copolymer is the copolymeric product prepared by the process which comprises the steps of polymerizing a first monomer selected from monovinyl aromatic hydrocarbons under solution polymerization conditions employing a hydrocarbon diluent, a first effective increment of a hydrocarbylmonolithium initiator, at effective conditions of temperature, pressure, and time, adding to the still-living polymerization admixture resulting therefrom at least one second monomer selected from conjugated dienes, together with a second effective increment of a hydrocarbyllithium initiator, provided that said second initiator increment is greater than said first initiator increment, and continuing said polymerization, and thereafter treating the resulting polymerization admixture with an effective amount of a coupling agent which is at least difunctional, thereby producing a mixture of coupled block copolymers exhibiting effective properties in adhesive formulations.

Claim 19

The adhesive composition employing 100 parts by weight of coupled block copolymer, about 40-150 parts tackifier, up to 100 parts plasticizer, 0.1-5 parts stabilizer, optionally employing solvent in the range of 75-2000 parts or water in the range of about 5-250 parts, wherein said coupled block copolymer is the copolymeric product prepared by the process which comprises the steps of polymerizing a first monomer selected from monovinyl aromatic hydrocarbons under solution polymerization conditions employing a hydrocarbon diluent, a first effective increment of a hydrocarbylmonolithium initiator, at effective conditions of temperature, pressure, and time, adding to the still-living polymerization admixture resulting therefrom at least one second monomer selected from conjugated dienes, together with a second effective increment of a hydrocarbyllithium initiator, provided that said second initiator increment is greater than said first initiator increment, and continuing said polymerization, and thereafter treating the resulting polymerization admixture with an effective amount of a coupling agent which is at least difunctional, thereby producing a mixture of coupled block copolymers exhibiting effective properties in adhesive formulations.

Claim 20

The adhesive composition of claim 16 wherein said copolymer is a butadiene/styrene block copolymer.

Claim 21

The adhesive composition of claim 17 wherein said copolymer is an 80/20 butadiene/styrene block copolymer.

Claim 22

The adhesive composition according to claim 18 employing about 100 parts said coupled block copolymer, about 100 parts glycerol ester of rosin acid, 40 parts coumarone-indene resin, 60 parts extender oil, 1 part dilaurylthiodiproprionate, 4 parts alkylated arylated bis-phenolic phosphite.

Claim 23

A copolymer as defined by claim 15 wherein a tetrafunctional silicon based coupling agent is employed, and the resulting copolymer product is an admixture comprising species represented by ##STR2## wherein Bd represents a block of poly(conjugated diene), and St a block of poly(monovinyl arene).

Claim 24

The process for the preparation of a coupled block copolymer which comprises the steps of polymerizing a first monomer selected from monovinyl aromatic hydrocarbons under solution polymerization conditions employing a hydrocarbon diluent, a first effective increment of a hydrocarbylmonolithium initiator, at effective conditions of temperature, pressure, and time, adding to the still-living polymerization admixture resulting therefrom at least one second monomer selected from conjugated dienes, together with a second effective increment of a hydrocarbyllithium initiator, provided that said second initiator increment is greater than said first initiator increment, and continuing said polymerization, and thereafter treating the resulting polymerization admixture with an effective amount of a coupling agent which is at least trifunctional, thereby producing a mixture of coupled block copolymers.

Claim 25

The process for the preparation of a coupled block copolymer which comprises the steps of polymerizing a first monomer selected from monovinyl aromatic hydrocarbons under solution polymerization conditions employing a hydrocarbon diluent, a first effective increment of a hydrocarbylmonolithium initiator, at effective conditions of temperature, pressure, and time, adding to the still-living polymerization admixture resulting therefrom at least one second monomer selected from conjugated dienes, together with a second effective increment of a hydrocarbyllithium initiator, provided that said second initiator increment is greater than said first initiator increment, and continuing said polymerization, and thereafter treating the resulting polymerization admixture with an effective amount of a coupling agent which is at least trifunctional, thereby producing a mixture of coupled block copolymers.

Claim 26

The copolymeric product produced in accordance with the process which comprises the steps of polymerizing a first monomer selected from monovinyl aromatic hydrocarbons under solution polymerization conditions employing a hydrocarbon diluent, a first effective increment of a hydrocarbylmonolithium initiator, at effective conditions of temperature, pressure, and time, adding to the still-living polymerization admixture resulting therefrom at least one second monomer selected from conjugated dienes, together with a second effective increment of a hydrocarbyllithium intiator, provided that said second initiator increment is greater than said first initiator increment, and continuing said polymerization, and thereafter treating the resulting polymerization admixture with an effective amount of a coupling agent which is at least trifunctional, resulting in an admixture comprising radial coupled block polymers.

Claim 27

The copolymeric product produced in accordance with the process which comprises the steps of polymerizing a first monomer selected from monovinyl aromatic hydrocarbons under solution polymerization conditions employing a hydrocarbon diluent, a first effective increment of a hydrocarbylmonolithium initiator, at effective conditions of temperature, pressure, and time, adding to the still-living polymerization admixture resulting therefrom at least one second monomer selected from conjugated dienes, together with a second effective increment of a hydrocarbyllithium intiator, provided that said second initiator increment is greater than said first initiator increment, and continuing said polymerization, and thereafter treating the resulting polymerization admixture with an effective amount of a coupling agent which is at least trifunctional, resulting in an admixture comprising radial coupled block polymers.

Claim 28

The adhesive composition employing 100 parts by weight of coupled block copolymer, about 40-150 parts tackifier, up to 100 parts plasticizer, 0.1-5 parts stabilizer, optionally employing solvent in the range of 75-2000 parts or water in the range of about 5-250 parts, wherein said coupled block copolymer is prepared by the process which comprises the steps of polymerizing a first monomer selected from monovinyl aromatic hydrocarbons under solution polymerization conditions employing a hydrocarbon diluent, a first effective increment of a hydrocarbylmonolithium initiator, at effective conditions of temperature, pressure, and time, adding to the still-living polymerization admixture resulting therefrom at least one second monomer selected from conjugated dienes, together with a second effective increment of a hydrocarbyllithium initiator, provided that said second initiator increment is greater than said first initiator increment, and continuing said polymerization, and therafter treating the resulting polymerization admixture with an effective amount of a coupling agent which is at least trifunctional, thereby producing a mixture of coupled block copolymers.

Claim 29

The adhesive composition employing 100 parts by weight of coupled block copolymer, about 40-150 parts tackifier, up to 100 parts plasticizer, 0.1-5 parts stabilizer, optionally employing solvent in the range of 75-2000 parts or water in the range of about 5-250 parts, wherein said coupled block copolymer is prepared by the process which comprises the steps of polymerizing a first monomer selected from monovinyl aromatic hydrocarbons under solution polymerization conditions employing a hydrocarbon diluent, a first effective increment of a hydrocarbylmonolithium initiator, at effective conditions of temperature, pressure, and time, adding to the still-living polymerization admixture resulting therefrom at least one second monomer selected from conjugated dienes, together with a second effective increment of a hydrocarbyllithium initiator, provided that said second initiator increment is greater than said first initiator increment, and continuing said polymerization, and therafter treating the resulting polymerization admixture with an effective amount of a coupling agent which is at least trifunctional, thereby producing a mixture of coupled block copolymers.

Claim 30

The adhesive composition of claim 23 wherein said copolymer is a butadiene/styrene block copolymer.

Claim 31

The adhesive composition of claim 24 wherein said copolymer is an 80/20 butadiene/styrene block copolymer.

Claim 32

The adhesive composition according to claim 25 employing about 100 parts said coupled block copolymer, about 100 parts glycerol ester of rosin acid, 40 parts coumarone-indene resin, 60 parts extender oil, 1 part dilauryl thiodipropionate, 4 parts alkylated arylated bis-phenolic phosphite.

Claim 33

An article of manufacture formed of at least two parts bonded with the adhesive composition of claim 23.

Claim 34

An article of manufacture formed of at least two parts bonded with the adhesive composition of claim 16.