Deposition method and products
Assignee: Air Products and Chemicals Inc
•
Filing: 1977-11-07
•
Granted: 1979-07-24
•
Expires: 1997-11-07
Abstract
Abstract A method for producing a hard deposit on a substrate is described wherein a volatile halide of tungsten or molybdenum is reacted with a gas or gases containing hydrogen, oxygen and carbon to effect the deposition on a substrate of a compound of the metal in a liquid phase. The liquid phase deposited on the substrate is then reacted to remove oxygen and halogen and produce a hard deposit containing the metal and carbon. Also described are products which may be produced by the above method.
Inventors
- 👤 Robert A. Holzl
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 18:49
CPC Classifications
C; C23; C23C; C23C16/00; C23C16/22; C23C16/30; C23C16/32; Y; Y10; Y10T; Y10T428/00; Y10T428/25; Y10T428/256
Claims Analysis
Total Claims: 31
Claim 1
Independent Claim
141 words
A method for producing a hard deposit on a substrate, comprising, providing a gaseous volatile halide of tungsten or molybdenum, reacting said volatile halide spaced from the surface of the substrate in the presence of an alcohol, ketone or ether to form a first intermediate compound of tungsten or molybdenum which is spaced from the surface of the substrate, reacting said first intermediate compound in the presence of gaseous hydrogen and one or more gases containing oxygen and carbon to cause the deposition on the substrate of a second intermediate compound of tungsten or molybdenum which is in a liquid phase, and reacting the liquid phase second intermediate compound on the surface of the substrate to produce a hard deposit containing essentially tungsten or molybdenum and carbon and having a modulus of rupture in bending exceeding 200 kilograms per square millimeter.
Claim 2
Independent Claim
141 words
A method for producing a hard deposit on a substrate, comprising, providing a gaseous volatile halide of tungsten or molybdenum, reacting said volatile halide spaced from the surface of the substrate in the presence of an alcohol, ketone or ether to form a first intermediate compound of tungsten or molybdenum which is spaced from the surface of the substrate, reacting said first intermediate compound in the presence of gaseous hydrogen and one or more gases containing oxygen and carbon to cause the deposition on the substrate of a second intermediate compound of tungsten or molybdenum which is in a liquid phase, and reacting the liquid phase second intermediate compound on the surface of the substrate to produce a hard deposit containing essentially tungsten or molybdenum and carbon and having a modulus of rupture in bending exceeding 200 kilograms per square millimeter.
Claim 3
Dependent Claim
15 words
A method according to claim 1 wherein the hard deposit is essentially tungsten and carbon.
Claim 4
Independent Claim
137 words
A method for producing a hard deposit on a substrate, comprising, providing a gaseous volatile halide of tungsten, reacting said volatile halide spaced from the surface of the substrate in the presence of an alcohol, ketone or ether to form a first intermediate compound of tungsten which is in a gaseous phase spaced from the surface of the substrate, reacting said first intermediate compound in the presence of gaseous hydrogen and one or more gases containing oxygen and carbon to cause the deposition on the substrate of a second intermediate compound of tungsten which is in a liquid phase, and reacting the liquid phase second intermediate compound on the surface of the substrate to produce a hard deposit containing essentially tungsten and carbon and having a modulus of rupture in bending exceeding 200 kilograms per square millimeter.
Claim 5
Independent Claim
137 words
A method for producing a hard deposit on a substrate, comprising, providing a gaseous volatile halide of tungsten, reacting said volatile halide spaced from the surface of the substrate in the presence of an alcohol, ketone or ether to form a first intermediate compound of tungsten which is in a gaseous phase spaced from the surface of the substrate, reacting said first intermediate compound in the presence of gaseous hydrogen and one or more gases containing oxygen and carbon to cause the deposition on the substrate of a second intermediate compound of tungsten which is in a liquid phase, and reacting the liquid phase second intermediate compound on the surface of the substrate to produce a hard deposit containing essentially tungsten and carbon and having a modulus of rupture in bending exceeding 200 kilograms per square millimeter.
Claim 6
Independent Claim
156 words
A method for producing a hard deposit on a substrate, comprising, placing the substrate in a chemical vapor deposition reactor and heating the substrate to a temperature of between about 650° C. and 1100° C., providing a flow in the reactor of a gaseous volatile halide of tungsten or molybdenum, providing in the reactor a flow of hydrogen and of a gaseous alcohol, ketone or ether and controlling the relative amounts of volatile halid, hydrogen, oxygen, and carbon, the substrate temperature and the reactor pressure to form a gaseous compound of tungsten or molybdenum which is spaced from the surface of the substrate and to cause the deposition on the substrate of a compound of tungsten or molybdenum which is in a liquid phase and a subsequent conversion of said liquid phase to a hard deposit containing tungsten or molybdenum and carbon and having a modulus of rupture in bending exceeding 200 kilograms per square millimeter.
Claim 7
Independent Claim
156 words
A method for producing a hard deposit on a substrate, comprising, placing the substrate in a chemical vapor deposition reactor and heating the substrate to a temperature of between about 650° C. and 1100° C., providing a flow in the reactor of a gaseous volatile halide of tungsten or molybdenum, providing in the reactor a flow of hydrogen and of a gaseous alcohol, ketone or ether and controlling the relative amounts of volatile halid, hydrogen, oxygen, and carbon, the substrate temperature and the reactor pressure to form a gaseous compound of tungsten or molybdenum which is spaced from the surface of the substrate and to cause the deposition on the substrate of a compound of tungsten or molybdenum which is in a liquid phase and a subsequent conversion of said liquid phase to a hard deposit containing tungsten or molybdenum and carbon and having a modulus of rupture in bending exceeding 200 kilograms per square millimeter.
Claim 8
Dependent Claim
23 words
A method according to claim 4 wherein the ratio of hydrogen to the volatile halide is equal to or less than stoichiometric proportions.
Claim 9
Dependent Claim
30 words
A method according to claim 4 wherein the ratio of gram atoms of carbon to gram atoms of the tungsten or molybdenum in the gas stream does not exceed unity.
Claim 10
Dependent Claim
29 words
A method according to claim 4 wherein the ratio of gram atoms of carbon to gram atoms of oxygen in the gas stream does not exceed 3 to 1.
Claim 11
Dependent Claim
21 words
A method according to claim 4 wherein the temperature of the substrate is maintained between about 800° C. and 950° C.
Claim 12
Independent Claim
181 words
A method for producing a hard deposit on a substrate, comprising, placing the substrate in a chemical vapor deposition reactor and heating the substrate to a temperature not exceeding about 1000° C., providing a flow in the reactor of a gaseous volatile halide of tungsten, providing in the reactor a flow of hydrogen and a gaseous alcohol, ketone or ether, wherein the ratio of hydrogen to the volatile halide is equal to or less than stoichiometric proportions, wherein the ratio of gram atoms of carbon to gram atoms of tungsten does not exceed unity, and wherein the ratio of gram atoms of carbon to gram atoms of oxygen does not exceed 3 to 1, and controlling the relative amounts of volatile halide, hydrogen, oxygen, and carbon, the substrate temperature and the reactor pressure to cause the deposition on the substrate of a compound of tungsten which is in a liquid phase and a subsequent conversion of said liquid phase to a hard deposit containing tungsten and carbon and having a modulus of rupture in bending exceeding 200 kilograms per square millimeter.
Claim 13
Independent Claim
181 words
A method for producing a hard deposit on a substrate, comprising, placing the substrate in a chemical vapor deposition reactor and heating the substrate to a temperature not exceeding about 1000° C., providing a flow in the reactor of a gaseous volatile halide of tungsten, providing in the reactor a flow of hydrogen and a gaseous alcohol, ketone or ether, wherein the ratio of hydrogen to the volatile halide is equal to or less than stoichiometric proportions, wherein the ratio of gram atoms of carbon to gram atoms of tungsten does not exceed unity, and wherein the ratio of gram atoms of carbon to gram atoms of oxygen does not exceed 3 to 1, and controlling the relative amounts of volatile halide, hydrogen, oxygen, and carbon, the substrate temperature and the reactor pressure to cause the deposition on the substrate of a compound of tungsten which is in a liquid phase and a subsequent conversion of said liquid phase to a hard deposit containing tungsten and carbon and having a modulus of rupture in bending exceeding 200 kilograms per square millimeter.
Claim 14
Dependent Claim
19 words
A method according to claim 9 wherein the flow of gases provided in the reactor includes hydrogen and methanol.
Claim 15
Independent Claim
139 words
A method for producing a hard deposit on a substrate comprising providing a gaseous volatile halide of tungsten or molybdenum, reacting the volatile halide spaced from the surface of the substrate in the presence of gaseous hydrogen and ethyl alcohol, methyl alcohol, a ketone, or an ether to form a first intermediate compound of tungsten or molybdenum which is spaced from the surface of the substrate and to effect the deposition on the substrate of a second intermediate compound of tungsten or molybdenum which is in a liquid phase, and reacting the liquid phase deposit on the substrate in the presence of gaseous hydrogen and ethyl alcohol, methyl alcohol, a ketone or an ether to produce a hard deposit containing tungsten or molybdenum and carbon and having a modulus of rupture in bending exceeding 200 kilograms per square millimeter.
Claim 16
Independent Claim
139 words
A method for producing a hard deposit on a substrate comprising providing a gaseous volatile halide of tungsten or molybdenum, reacting the volatile halide spaced from the surface of the substrate in the presence of gaseous hydrogen and ethyl alcohol, methyl alcohol, a ketone, or an ether to form a first intermediate compound of tungsten or molybdenum which is spaced from the surface of the substrate and to effect the deposition on the substrate of a second intermediate compound of tungsten or molybdenum which is in a liquid phase, and reacting the liquid phase deposit on the substrate in the presence of gaseous hydrogen and ethyl alcohol, methyl alcohol, a ketone or an ether to produce a hard deposit containing tungsten or molybdenum and carbon and having a modulus of rupture in bending exceeding 200 kilograms per square millimeter.
Claim 17
Dependent Claim
36 words
A method according to claim 11 wherein the volatile halide is reacted in the presence of a substance selected from the group consisting of methyl alcohol, ethyl alcohol, acetone, dimethyl ether, diethyl ether, and ethylene oxide.
Claim 18
Dependent Claim
27 words
A method according to claim 11 wherein the ratio of gram atoms of carbon to gram atoms of tungsten in the gas stream does not exceed unity.
Claim 19
Independent Claim
185 words
A method for producing a hard deposit on a substrate, comprising, placing the substrate in a chemical vapor deposition reactor and heating the substrate to a temperature of about 650° C. to about 1100° C., maintaining a pressure in the reactor of between about 50 Torr and one atmosphere, providing in the reactor a flow of gaseous tungsten hexafluoride, gaseous hydrogen and a gaseous compound containing carbon, hydrogen and oxygen wherein the ratio of the gram atoms of the hydrogen to gram atoms of tungsten hexafluoride is between about 0.5 to 1 and 3 to 1, wherein the ratio of gram atoms of carbon to gram atoms of tungsten is between about 0.03 to 1 and about unity, wherein the ratio of gram atoms of carbon to gram atoms of oxygen is less than about 3 to 1, and controlling the relative amounts of tungsten hexafluoride, hydrogen, oxygen and carbon, the substrate temperature in the reactor pressure to produce a deposit on the substrate containing tungsten and a finely dispersed carbide and having a modulus of rupture in bending exceeding 200 kilograms per square millimeter.
Claim 20
Independent Claim
185 words
A method for producing a hard deposit on a substrate, comprising, placing the substrate in a chemical vapor deposition reactor and heating the substrate to a temperature of about 650° C. to about 1100° C., maintaining a pressure in the reactor of between about 50 Torr and one atmosphere, providing in the reactor a flow of gaseous tungsten hexafluoride, gaseous hydrogen and a gaseous compound containing carbon, hydrogen and oxygen wherein the ratio of the gram atoms of the hydrogen to gram atoms of tungsten hexafluoride is between about 0.5 to 1 and 3 to 1, wherein the ratio of gram atoms of carbon to gram atoms of tungsten is between about 0.03 to 1 and about unity, wherein the ratio of gram atoms of carbon to gram atoms of oxygen is less than about 3 to 1, and controlling the relative amounts of tungsten hexafluoride, hydrogen, oxygen and carbon, the substrate temperature in the reactor pressure to produce a deposit on the substrate containing tungsten and a finely dispersed carbide and having a modulus of rupture in bending exceeding 200 kilograms per square millimeter.
Claim 21
Dependent Claim
18 words
A method according to claim 14 wherein the substrate temperature is between about 800° C. and 950° C.
Claim 22
Dependent Claim
70 words
A thermochemically deposited product consisting of a hard metal alloy, primarily of tungsten and carbon, free of columnar grains, having a hardness of greater than 1000 VHN with a modulus of rupture in bending of greater than 200 kg/mm 2 in the deposited or deposited and heat treated condition, said product containing between about 0.1 percent and one percent carbon finely dispersed in a form other than W 2 C.
Claim 23
Dependent Claim
70 words
A thermochemically deposited product consisting of a hard metal alloy, primarily of tungsten and carbon, free of columnar grains, having a hardness of greater than 1000 VHN with a modulus of rupture in bending of greater than 200 kg/mm 2 in the deposited or deposited and heat treated condition, said product containing between about 0.1 percent and one percent carbon finely dispersed in a form other than W 2 C.
Claim 24
Dependent Claim
23 words
A product according to claim 16 containing between about 0.1 percent and one percent carbon as finely dispersed carbide in the form WC.
Claim 25
Dependent Claim
27 words
A product according to claim 16 wherein the product is laminar in appearance when cross sectioned and etched, with layers of the order of 2000 A thick.
Claim 26
Dependent Claim
15 words
A product according to claim 16 having a grain size of less than one micron.
Claim 27
Dependent Claim
118 words
A coated substrate comprising a substrate having a coating thereon primarily of tungsten and carbon which is essentially free of columnar grains and which has a hardness greater than 2000 VHN, a grain size equal to or less than 5 microns, a modulus of rupture as deposited or as deposited and after heat treating equal to or greater than 200 kg/mm 2 , a modulus of elasticity as deposited or as deposited and after heat treating of equal to or greater than 50,000 kg/mm 2 , and a surface smoothness exceeding 4 rms in the as-deposited condition, said coating containing between about 0.1 percent and one percent carbon finely dispersed in a form other than W 2 C.
Claim 28
Dependent Claim
118 words
A coated substrate comprising a substrate having a coating thereon primarily of tungsten and carbon which is essentially free of columnar grains and which has a hardness greater than 2000 VHN, a grain size equal to or less than 5 microns, a modulus of rupture as deposited or as deposited and after heat treating equal to or greater than 200 kg/mm 2 , a modulus of elasticity as deposited or as deposited and after heat treating of equal to or greater than 50,000 kg/mm 2 , and a surface smoothness exceeding 4 rms in the as-deposited condition, said coating containing between about 0.1 percent and one percent carbon finely dispersed in a form other than W 2 C.
Claim 29
Dependent Claim
19 words
A coated substrate according to claim 20 wherein the coating has a grain size of less than one micron.
Claim 30
Dependent Claim
31 words
A coating substrate according to claim 20 wherein the coating has a laminar appearance when cross sectioned and etched, with the layers having a thickness of the order of 2000 A.
Claim 31
Dependent Claim
28 words
A coated substrate according to claim 20 wherein the coating contains between about 0.1 percent and 1 percent carbon as a finely dispersed carbide in the form WC.
References Cited (Backward Citations)
US3574672A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-07-23 | 1983-01-22 | 1983-07-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-07-23 | 1987-01-22 | 1987-07-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-07-23 | 1991-01-22 | 1991-07-24 | $7700.00 | Window Closed / Lapsed |