Method of obtaining granulated and defluorated phosphogypsum
Assignee: Vish Chimiko Technologicheski Institute
•
Filing: 1978-08-28
•
Granted: 1979-07-24
•
Expires: 1998-08-28
Abstract
Abstract A combined method for granulation and defluoration of phosphogypsum, suitable for subsequent fluidized bed disassociation to lime and sulphur dioxide is described. The new phosphogypsum, obtained from phosphoric acid production, containing residual combined fluorine, is dried to reduce its residual water. It is moistened with sulfuric acid and aqueous solutions of binding agent additives and then granulated. The granules are heat-treated at temperatures between 170° C. and 700° C. During the heat treatment the residual fluorine residue is volatilized and the granules increase in strength sufficient for use in subsequent fluidized bed treatments.
Inventors
- 👤 Ivan N. Grancharov
- 👤 Fanka D. Tudjarova
- 👤 Yovka P. Bakalova
- 👤 Yoncho G. Pelovski
- 👤 Nikola B. Videnov
- 👤 Ivan P. Dombalov
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 19:43
CPC Classifications
C; C01; C01F; C01F11/00; C01F11/46
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
156 words
A method for the production of granulated and defluorated phosphogypsum for thermal processing which comprises the steps of: (a) preliminarily drying phosphogypsum, from phosphoric acid manufacture, to a residual moisture content of from 0.5 to 10 percent; (b) mixing said preliminarily dried phosphogypsum with sulfuric acid of concentration range 55 to 98%, and granulation-binding additives, in solution, said sulfuric acid being added in amounts of from 0.5 to 15 weight parts and said binding additives being added in amounts of from 0.01 to 6 weight parts per 100 parts of said phosphogypsum, said binding additives being selected from the group consisting of carbamide, ammonium nitrate, carboxymethylcellulose, calcium nitrate, polyethylene oxide and the distillation fluids from soda production; (c) granulating said mixture; and (d) then heating the granules to a temperature in the range of 170° C. to 700° C. to drive off fluorine-containing gases and to strengthen said granules for subsequent thermal processing in fluidized beds.
Claim 2
Independent Claim
156 words
A method for the production of granulated and defluorated phosphogypsum for thermal processing which comprises the steps of: (a) preliminarily drying phosphogypsum, from phosphoric acid manufacture, to a residual moisture content of from 0.5 to 10 percent; (b) mixing said preliminarily dried phosphogypsum with sulfuric acid of concentration range 55 to 98%, and granulation-binding additives, in solution, said sulfuric acid being added in amounts of from 0.5 to 15 weight parts and said binding additives being added in amounts of from 0.01 to 6 weight parts per 100 parts of said phosphogypsum, said binding additives being selected from the group consisting of carbamide, ammonium nitrate, carboxymethylcellulose, calcium nitrate, polyethylene oxide and the distillation fluids from soda production; (c) granulating said mixture; and (d) then heating the granules to a temperature in the range of 170° C. to 700° C. to drive off fluorine-containing gases and to strengthen said granules for subsequent thermal processing in fluidized beds.
Claim 3
Dependent Claim
26 words
The method according to claim 1 wherein said solutions of said additives contain sufficient water to provide a liquid content sufficient for granulation of said mixture.
Claim 4
Dependent Claim
20 words
The method according to claim 1 wherein said granules in step (d) are heated for from 15 to 120 minutes.
Claim 5
Dependent Claim
85 words
The method according to claim 1 wherein said phosphogypsum in step (a) is air dried to a residual moisture content of substantially 3.5 percent; then 13 weight parts of 90% sulfuric acid and 3 weight parts of carbamide, in sufficient water to provide a 21% moisture content, is added per 100 parts of dried phosphogypsum to provide a granulation mixture; and after granulation the granules are heated for 60 minutes at 170° C. to provide phosphogypsum granules having a fluorine content of substantially 0.07 percent.
Claim 6
Dependent Claim
32 words
The method according to claim 4 wherein said granules with fluorine content of substantially 0.07 percent are further heated at 450° for 25 minutes to reduce their fluorine content to 0.02 percent.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-07-23 | 1983-01-22 | 1983-07-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-07-23 | 1987-01-22 | 1987-07-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-07-23 | 1991-01-22 | 1991-07-24 | $7700.00 | Window Closed / Lapsed |