US4160751A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Low pressure injection moldable compositions
Assignee: ExxonMobil Technology and Engineering Co
•
Filing: 1977-11-29
•
Granted: 1979-07-10
•
Expires: 1997-11-29
Abstract
Abstract This invention relates to injection moldable type elastomeric compositions having a viscosity at 200 DEG C. at 0.73 sec-1 of less than about 8x104 poises. The compositions used for elastomeric articles include 100 parts of a neutralized sulfonated EPDM terpolymer; about 25 to about 150 parts per hundred of a non-polar process oil; about 25 to about 200 parts per hundred of a filler; and a preferential plasticizer at about less than 50 parts per hundred based on 100 parts of the sulfonated elastomeric polymer. The composition may also include a crystalline polyolefinic thermoplastic at least than about 100 parts per hundred by weight.
Inventors
- 👤 Jan Bock
- 👤 Robert D. Lundberg
- 👤 Henry S. Makowski
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 03:32
CPC Classifications
C; C08; C08L; C08L23/00; C08L23/26; C08L23/32; Y; Y10; Y10S; Y10S260/00; Y10S260/31
Claims Analysis
Total Claims: 31
Claim 1
Independent Claim
275 words
An elastomeric composition having a viscosity at 0.73 sec -1 at 200° C. of less than about 8×10 4 , and greater than 5×10 3 poises, said composition injection moldable into an elastomeric article, which consists essentially of: (a) a neutralized sulfonated elastomeric polymer having a viscosity at 0.73 sec -1 at 200° C. of about 3×10 5 poises to about 5×10 6 poises and about 15 to about 50 meq. neutralized metal sulfonate groups per 100 grams of said neutralized sulfonated elastomeric polymer; (b) about 25 to about 150 parts by weight of a non-polar process oil per 100 parts by weight of said neutralized sulfonated elastomeric polymer, said non-polar process oil having less than about 2 wt. % polar type compounds therein; (c) about 25 to about 300 parts by weight of an inorganic filler per 100 parts by weight of said neutralized sulfonated elastomeric polymer, said inorganic filler being selected from the group consisting of clay, talc, and calcium carbonate and mixtures thereof, a ratio of said inorganic filler to said non-polar process oil being about 0.6 to about 1.25, and (d) at least 8 parts by weight of a preferential ionic plasticizer per 100 parts by weight of said neutralized sulfonated elastomeric polymer, said preferential plasticizer having a melting point of at least 25° C. and is selected from the group consisting of carboxylic acids having about 5 to about 30 carbon atoms and salts of said carboxylic acids and mixtures thereof, an ion of said salt being selected from the group consisting of aluminum, ammonium, lead, Cd, Hg, and Groups IA, IIA and IB of the Periodic Table of Elements.
Claim 2
Dependent Claim
275 words
An elastomeric composition having a viscosity at 0.73 sec -1 at 200° C. of less than about 8×10 4 , and greater than 5×10 3 poises, said composition injection moldable into an elastomeric article, which consists essentially of: (a) a neutralized sulfonated elastomeric polymer having a viscosity at 0.73 sec -1 at 200° C. of about 3×10 5 poises to about 5×10 6 poises and about 15 to about 50 meq. neutralized metal sulfonate groups per 100 grams of said neutralized sulfonated elastomeric polymer; (b) about 25 to about 150 parts by weight of a non-polar process oil per 100 parts by weight of said neutralized sulfonated elastomeric polymer, said non-polar process oil having less than about 2 wt. % polar type compounds therein; (c) about 25 to about 300 parts by weight of an inorganic filler per 100 parts by weight of said neutralized sulfonated elastomeric polymer, said inorganic filler being selected from the group consisting of clay, talc, and calcium carbonate and mixtures thereof, a ratio of said inorganic filler to said non-polar process oil being about 0.6 to about 1.25, and (d) at least 8 parts by weight of a preferential ionic plasticizer per 100 parts by weight of said neutralized sulfonated elastomeric polymer, said preferential plasticizer having a melting point of at least 25° C. and is selected from the group consisting of carboxylic acids having about 5 to about 30 carbon atoms and salts of said carboxylic acids and mixtures thereof, an ion of said salt being selected from the group consisting of aluminum, ammonium, lead, Cd, Hg, and Groups IA, IIA and IB of the Periodic Table of Elements.
Claim 3
Dependent Claim
30 words
A composition according to claim 1, wherein said neutralized sulfonated elastomeric polymer is formed from an elastomeric polymer selected from the group consisting of Butyl rubber and an EPDM terpolymer.
Claim 4
Dependent Claim
45 words
A composition according to claim 2, wherein said EPDM terpolymer consists essentially of about 40 to about 75 wt. % of ethylene, of about 10 to about 53 wt. % of propylene and of about 1 to about 10 wt. % of a non-conjugated diene.
Claim 5
Dependent Claim
42 words
A composition according to claim 1, wherein said sulfonate groups are neutralized with a counterion being selected from the group consisting of ammonium, antimony, aluminum, lead and Groups I-A, II-A, I-B and II-B of the Periodic Table of Elements and mixtures thereof.
Claim 6
Dependent Claim
27 words
A composition according to claim 5, wherein said non-conjugated diene is selected from the group consisting of 1,4-hexadiene, dicyclopentadiene, alkylidene substituted norbornenes, alkenyl substituted norbornenes and tetrahydroindenes.
Claim 7
Dependent Claim
12 words
A composition according to claim 5, wherein said non-conjugated diene is 5-ethylidene-2-norbornene.
Claim 8
Dependent Claim
17 words
A composition according to claim 1, having a Shore Hardness A of about 45 to about 70.
Claim 9
Dependent Claim
56 words
A composition according to claim 1, wherein said preferential plasticizeris a combination of stearic acid and a metallic salt of said stearic acid, a metal ion of said metallic salt being selected from the group consisting of lead, antimony, aluminum, and Groups I-A, II-A, I-B and II-B of the Periodic Table of Elements and mixtures thereof.
Claim 10
Dependent Claim
20 words
A composition according to claim 1, wherein said filler has a particle size of about 0.03 to about 20 microns.
Claim 11
Dependent Claim
19 words
A composition according to claim 1, wherein said filler has an oil absorption of about 10 to about 100.
Claim 12
Dependent Claim
25 words
A composition according to claim 1, wherein said non-polar process oil is selected from the group consisting of paraffinic, naphthenic or aromatics and mixtures thereof.
Claim 13
Dependent Claim
22 words
A composition according to claim 1, wherein said non-polar process oil is paraffinic having an Mn of about 400 to about 1000.
Claim 14
Dependent Claim
16 words
An elastomeric composition according to claim 1, wherein said non-polar process oil is a paraffinic oil.
Claim 15
Dependent Claim
227 words
An elastomeric composition having a viscosity at 0.73 sec -1 at 200° C. of about 5×10 3 to about 8×10 4 poises, said composition formable by extrusion or injection molding into an elastomeric article, which consists essentially of: (a) a neutralized sulfonated elastomeric polymer having a viscosity at 0.73 sec -1 at 200° C. of about 3×10 5 poises to about 5×10 6 poises and about 15 to about 50 meq. neutralized sulfonate groups per 100 grams of said neutralized sulfonated elastomeric polymer; (b) about 25 to about 150 parts by weight of a non-polar process oil per 100 parts by weight of said neutralized sulfonated elastomeric polymer, said non-polar process oil having less than about 2 wt. % polar type compounds therein; (c) about 25 to about 300 parts by weight of an inorganic filler per 100 parts by weight of said neutralized sulfonated elastomeric polymer, said inorganic filler being selected from the group consisting of clay, talc, and calcium carbonate and mixtures thereof, a ratio of said inorganic filler to said non-polar process oil being about 0.6 to about 1.25; and (d) at least 8 parts by weight of a preferential plasticizer per one hundred parts by weight of said neutralized sulfonated elastomeric polymer, said preferential plasticizer being a mixture of a carboxylic acid having about 5 to about 30 carbon atoms and zinc stearate.
Claim 16
Dependent Claim
227 words
An elastomeric composition having a viscosity at 0.73 sec -1 at 200° C. of about 5×10 3 to about 8×10 4 poises, said composition formable by extrusion or injection molding into an elastomeric article, which consists essentially of: (a) a neutralized sulfonated elastomeric polymer having a viscosity at 0.73 sec -1 at 200° C. of about 3×10 5 poises to about 5×10 6 poises and about 15 to about 50 meq. neutralized sulfonate groups per 100 grams of said neutralized sulfonated elastomeric polymer; (b) about 25 to about 150 parts by weight of a non-polar process oil per 100 parts by weight of said neutralized sulfonated elastomeric polymer, said non-polar process oil having less than about 2 wt. % polar type compounds therein; (c) about 25 to about 300 parts by weight of an inorganic filler per 100 parts by weight of said neutralized sulfonated elastomeric polymer, said inorganic filler being selected from the group consisting of clay, talc, and calcium carbonate and mixtures thereof, a ratio of said inorganic filler to said non-polar process oil being about 0.6 to about 1.25; and (d) at least 8 parts by weight of a preferential plasticizer per one hundred parts by weight of said neutralized sulfonated elastomeric polymer, said preferential plasticizer being a mixture of a carboxylic acid having about 5 to about 30 carbon atoms and zinc stearate.
Claim 17
Dependent Claim
30 words
A composition according to claim 14 wherein said neutralized sulfonated elastomeric polymer is formed from an elastomeric polymer selected from the group consisting of Butyl rubber and an EPDM terpolymer.
Claim 18
Dependent Claim
45 words
A composition according to claim 14 wherein said EPDM terpolymer consists essentially of about 40 to about 75 wt. % of ethylene, of about 10 to about 53 wt. % of propylene and of about 2 to about 10 wt. % of a non-conjugated diene.
Claim 19
Dependent Claim
23 words
A composition according to claim 16 wherein said non-conjugated diene is selected from the group consisting of 1,4-hexadiene, dicyclopentadiene, 5-alkylidene-2-norbornenes, 5-alkenyl-2-norbornenes and tetrahydroindene.
Claim 20
Dependent Claim
12 words
A composition according to claim 17 wherein said non-conjugated diene is 5-ethylidene-2-norbornene.
Claim 21
Dependent Claim
248 words
An elastomeric article formed from an elastomeric composition consisting essentially of: (a) a neutralized sulfonated elastomeric polymer having a viscosity at 0.73 sec - 1 at 200° C. of about 3×10 5 poises to about 5×10 6 poises and about 15 to about 50 meq. neutralized sulfonate groups per 100 grams of said neutralized sulfonated elastomeric polymer; (b) about 25 to about 150 parts by weight of a non-polar process oil per 100 parts by weight of said neutralized sulfonated elastomeric polymer, said non-polar process oil having less than about 2 wt. % polar type compounds therein; (c) about 25 to about 300 parts by weight of an inorganic filler per 100 parts by weight of said neutralized sulfonated elastomeric polymer, said inorganic filler being selected from the group consisting of clay, talc, and calcium carbonate and mixtures thereof, a ratio of said inorganic filler to said non-polar process oil being about 0.6 to about 1.25; and (d) at least 8 parts by weight of a preferential ionic plasticizer per 100 parts by weight of said neutralized sulfonated elastomeric polymer, said preferential plasticizer having a melting point of at least 25° C. and is selected from the group consisting of carboxylic acids having about 5 to about 30 carbon atoms and salts of said carboxylic acids and mixtures thereof, an ion of said salt being selected from the group consisting of aluminum, ammonium, lead, Cd, Hg, and Groups IA, IIA and IB of the Periodic Table of Elements.
Claim 22
Dependent Claim
248 words
An elastomeric article formed from an elastomeric composition consisting essentially of: (a) a neutralized sulfonated elastomeric polymer having a viscosity at 0.73 sec - 1 at 200° C. of about 3×10 5 poises to about 5×10 6 poises and about 15 to about 50 meq. neutralized sulfonate groups per 100 grams of said neutralized sulfonated elastomeric polymer; (b) about 25 to about 150 parts by weight of a non-polar process oil per 100 parts by weight of said neutralized sulfonated elastomeric polymer, said non-polar process oil having less than about 2 wt. % polar type compounds therein; (c) about 25 to about 300 parts by weight of an inorganic filler per 100 parts by weight of said neutralized sulfonated elastomeric polymer, said inorganic filler being selected from the group consisting of clay, talc, and calcium carbonate and mixtures thereof, a ratio of said inorganic filler to said non-polar process oil being about 0.6 to about 1.25; and (d) at least 8 parts by weight of a preferential ionic plasticizer per 100 parts by weight of said neutralized sulfonated elastomeric polymer, said preferential plasticizer having a melting point of at least 25° C. and is selected from the group consisting of carboxylic acids having about 5 to about 30 carbon atoms and salts of said carboxylic acids and mixtures thereof, an ion of said salt being selected from the group consisting of aluminum, ammonium, lead, Cd, Hg, and Groups IA, IIA and IB of the Periodic Table of Elements.
Claim 23
Dependent Claim
31 words
An elastomeric article according to claim 19, wherein said neutralized sulfonated elastomeric polymer is formed from an elastomeric polymer selected from the group consisting of Butyl rubber and an EPDM terpolymer.
Claim 24
Dependent Claim
43 words
An elastomeric article according to claim 19, wherein said sulfonated groups are neutralized with a counterion being selected from the group consisting of antimony, iron, aluminum, lead and Groups IA, IIA, IB and IIB of the Periodic Table of Elements and mixtures thereof.
Claim 25
Dependent Claim
44 words
An elastomeric article according to claim 20, wherein said EPDM terpolymer consists of about 40 to about 75 wt. % ethylene, of about 10 to about 53 wt. % of propylene, and of about 2 to about 10 wt. % of a conjugated diene.
Claim 26
Dependent Claim
25 words
An elastomeric article according to claim 22, wherein said non-conjugated diene is selected from the group consisting of 1,4-hexadiene, dicyclopentadiene, 5-alkylidene-2- norbornenes, 5-alkenyl-2-norbornenes and tetrahydroindene.
Claim 27
Dependent Claim
200 words
An elastomeric article formed from an elastomeric composition consisting essentially of: (a) a neutralized sulfonated elastomeric polymer having a viscosity at 0.73 sec -1 at 200° C. of about 3×10 5 poises to about 5×10 6 poises and about 15 to about 50 meq. neutralized sulfonate groups per 100 grams of said neutralized sulfonated elastomeric polymer; (b) about 25 to about 150 parts by weight of a non-polar process oil per 100 parts by weight of said neutralized sulfonated elastomeric polymer, said non-polar process oil having less than about 2 wt. % polar type compounds therein; (c) about 25 to about 300 parts by weight of an inorganic filler per 100 parts by weight of said neutralized sulfonated elastomeric polymer, said inorganic filler being selected from the group consisting of clay, talc, and calcium carbonate and mixtures thereof, a ratio of said inorganic filler to said non-polar process oil being about 0.6 to about 1.25; and (d) at least 8 parts by weight of a preferential plasticizer per one hundred parts by weight of said neutralized sulfonated elastomeric polymer, said preferential plasticizer being a mixture of a carboxylic acid having about 5 to about 30 carbon atoms and zinc stearate.
Claim 28
Dependent Claim
200 words
An elastomeric article formed from an elastomeric composition consisting essentially of: (a) a neutralized sulfonated elastomeric polymer having a viscosity at 0.73 sec -1 at 200° C. of about 3×10 5 poises to about 5×10 6 poises and about 15 to about 50 meq. neutralized sulfonate groups per 100 grams of said neutralized sulfonated elastomeric polymer; (b) about 25 to about 150 parts by weight of a non-polar process oil per 100 parts by weight of said neutralized sulfonated elastomeric polymer, said non-polar process oil having less than about 2 wt. % polar type compounds therein; (c) about 25 to about 300 parts by weight of an inorganic filler per 100 parts by weight of said neutralized sulfonated elastomeric polymer, said inorganic filler being selected from the group consisting of clay, talc, and calcium carbonate and mixtures thereof, a ratio of said inorganic filler to said non-polar process oil being about 0.6 to about 1.25; and (d) at least 8 parts by weight of a preferential plasticizer per one hundred parts by weight of said neutralized sulfonated elastomeric polymer, said preferential plasticizer being a mixture of a carboxylic acid having about 5 to about 30 carbon atoms and zinc stearate.
Claim 29
Dependent Claim
31 words
An elastomeric article according to claim 24, wherein said neutralized sulfonated elastomeric polymer is formed from an elastomeric polymer selected from the group consisting of Butyl rubber and an EPDM terpolymer.
Claim 30
Dependent Claim
44 words
An elastomeric article according to claim 25, wherein said EPDM terpolymer consists of about 40 to about 75 wt. % ethylene, of about 10 to about 53 wt. % of propylene, and of about 2 to about 10 wt. % of a conjugated diene.
Claim 31
Dependent Claim
24 words
An elastomeric article according to claim 26, wherein said non-conjugated diene is selected from the group consisting of 1,4-hexadiene, dicyclopentadiene, 5-alkylidene-2-norbornenes, 5-alkenyl-2-norbornenes and tetrahydroindene.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-07-09 | 1983-01-08 | 1983-07-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-07-09 | 1987-01-08 | 1987-07-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-07-09 | 1991-01-08 | 1991-07-10 | $7700.00 | Window Closed / Lapsed |