Aqueous acrylic contact cement

Claim 2

Contact cement for adhering like and unlike surfaces which is prepared from the ingredients comprising acrylic ester polymer selected from soft monomers having the following formula: ##STR3## hard monomers having the following formula ##STR4## and mixtures thereof, where R 1 is H or an alkyl group of 1 to 4 carbon atoms, R 2 is alkyl group containing from 1 to 14 carbon atoms and R 3 is an alkyl group containing 1 to 20 carbon atoms; about 0.002 to 0.5% of epoxy silane; about 0.0008 to 0.2% of a material selected from the group consisting essentially of glyoxal, formaldehyde paraformaldehyde and mixtures thereof; and sufficient amount of a thickener to give the desired consistency; amounts herein being based on 100 dry parts of the acrylic polymer.

Claim 3

Contact cement of claim 1 wherein the ingredients also include about 0.2 to 5% of a nitrogen compound or a mixture thereof to aid in cross-linking selected from amines and salts thereof, ureido monomers, heterocylic compounds and hydroxyalkyl or aminoalkyl derivatives thereof; and about 1 to 5% of an unsaturated carboxylic acid to aid in cross-linking; and wherein R 1 is selected from H or a methyl group; and R 2 and R 3 are selected from alkyl groups containing from about 1 to 8 carbon atoms; the cement being an aqueous system having viscosity of about 250 to 2500 cps; amounts herein are based on 100 dry parts of the acrylic ester polymer, the nitrogen compound and the acid.

Claim 4

Contact cement of claim 2 wherein the ingredients also include about 0.015 to 0.12% of a thickener; and a sufficient amount of a perfuming agent to mask unpleasant odors; amount of the material is about 0.0015 to 0.01%; amount of the silane is about 0.004 to 0.02%; and the nitrogen compound is selected from C 1-4 alkylamino C 1-4 alkyl acrylates and methacrylates.

Claim 5

Contact cement of claim 1, wherein the acrylic ester polymer has a T g of below about 0° C. and selection of values for the soft and hard monomers is made on the following criterion: when R 1 is H or methyl of the soft monomer, R 2 contains 1 to about 14 carbon atoms whereas when R 1 is alkyl radical of 2 to 4 carbon atoms, then R 2 contains 6 to 14 carbon atoms; and for R 3 of the hard monomer, when R 1 is H, R 3 is alkyl containing 1 or from 13 to 20 carbon atoms whereas when R 1 is CH 3 , R 3 contains from 1 to 5 carbon atoms or from 15 to 20 carbon atoms; the ingredients further include about 0.2 to 5% of a nitrogen compound or a mixture thereof selected from amines and salts thereof, ureido monomers, and heterocyclic compounds and hydroxyalkyl or aminoalkyl derivatives thereof; and about 1 to 5% of an alpha-beta unsaturated monocarboxylic acid or a mixture thereof; amounts herein are based on 100 dry parts of the acrylic ester polymer, the nitrogen compound and the acid.

Claim 6

Contact cement of claim 3 wherein amount of the acid is about 2 to 3% and the acid is selected from acrylic, methacrylic, and mixtures thereof.

Claim 7

Contact cement of claim 4 wherein the material is glyoxal, the thickener is xanthan gum, the acrylic polymer is supplied by Rhoplex CA-12 acrylic emulsion and the cement has the following physical properties: ______________________________________ solids 52.5 ± 1.5% pH 5.8 ± 0.30 Br. viscosity LVF #3 spindle at 60 RPM & 25° C. 600-800 cps. ______________________________________

Claim 8

Contact cement of claim 2 wherein the material is glyoxal, the thickener is xanthan gum, the acrylic polymer is supplied by Rhoplex CA-12 acrylic emulsion and the cement has the following physical properties: ______________________________________ solids 52.5 ± 1.5% pH 5.8 ± 0.30 Br. viscosity LVF #3 spindle at 60 RPM & 25° C. 600-800 cps. ______________________________________

Claim 9

Contact cement prepared from 98 to 99.75% of Rhoplex CA-12 acrylic emulsion which contains about 52% solids, 0.25 to 2% of a 3% aqueous solution of a thickener, 0.002 to 0.01% of a 40% aqueous solution of glyoxal and 0.002 to 0.01% of an epoxy silane, where the silane and glyoxal synergistically improve water resistance and adhesion of the cement without interfering with shelf stability and freeze/thaw property thereof.

Claim 10

Contact cement prepared from 98 to 99.75% of Rhoplex CA-12 acrylic emulsion which contains about 52% solids, 0.25 to 2% of a 3% aqueous solution of a thickener, 0.002 to 0.01% of a 40% aqueous solution of glyoxal and 0.002 to 0.01% of an epoxy silane, where the silane and glyoxal synergistically improve water resistance and adhesion of the cement without interfering with shelf stability and freeze/thaw property thereof.

Claim 11

Contact cement of claim 8 including a sufficient amount of a perfuming agent to mask unpleasant odors.

Claim 12

Contact cement of claim 9 wherein the thickener is xanthan gum; the perfuming agent is Tanafresh HFO; the silane is selected from gamma-glycidoxypropyltrimethoxysilane, beta-(3,4-epoxycyclohexyl)-ethyltrimethoxysilane and mixtures thereof; and the cement has the following physical properties: ______________________________________ solids 52.5 ± 1.5% pH 5.8 ± 0.30 Br. viscosity LVF #3 spindle at 60 RPM & 25° C. 600-800 cps. ______________________________________