US4159358A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of bonding a bioglass to metal
Assignee: University of Florida
•
Filing: 1977-05-19
•
Granted: 1979-06-26
•
Expires: 1997-05-19
Abstract
Abstract A method of bonding a bioglass layer to a metal substrate comprising heating the metal substrate having a roughened, oxidized surface to about a temperature at which the expansion of the metal is substantially equal to that of the bioglass at the temperature above which the thermal expansion of the bioglass is non-linear, immersing the heated metal surface in molten bioglass, the time of immersion being of such duration that the temperature of the metal does not rise substantially above the temperature to which it is heated, allowing the coated substrate to cool whereby the bioglass layer is bonded to the metal substrate by ion diffusion and thermo-mechanical stresses in the bioglass and metal layer are relieved at a substantially equal rate and the product produced by said process.
Inventors
- 👤 Larry L. Hench
- 👤 Paul J. Buscemi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 16:35
CPC Classifications
C; C03; C03C; C03C4/00; C03C4/0007; A; A61; A61C; A61C8/00; A61C8/0012; A61C8/0013; A61F; A61F2/00; A61F2/02; A61F2/30; A61F2/30767; A61L; A61L27/00; A61L27/28; A61L27/30; A61L27/306; A61L27/32; C03C27/00; C03C27/02; C23; C23D; C23D5/00; C23D5/04; A61F2310/00; A61F2310/00389; A61F2310/00592; A61F2310/00796; A61F2310/00928
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
256 words
A method of bonding a bioglass layer to a metal substrate comprising: (1) heating a metal substrate having a roughened, oxidized surface to about a maximum temperature (T 1 ) where said T 1 is selected such that the total volume expansion of said metal is substantially equal to that of said bioglass at the temperature (T s ) at which the temperature dependence of the volume of said bioglass becomes non-linear, (2) providing a body of molten bioglass at temperature T w where T w is sufficiently high that the said bioglass is sufficiently fluid to allow immersion of said metal heated to temperature T 1 , (3) immersing said metal surface in said molten bioglass for the minimum time required to permit a layer of desired thickness of said bioglass to adhere to said surface upon termination of said immersion, the time of said immersion being of such duration that the temperature of said metal surface does not rise substantially above T 1 , (4) terminating said immersion, (5) allowing said coating to cool rapidly from T w to about T s , whereby the thermo-mechanical stresses in said bioglass layer are rapidly relieved, and (6) allowing said coated substrate to further cool to a temperature below about T s , whereby the thermo-mechanical stresses in said bioglass coating and said metal surface are relieved at a substantially equal rate due to the substantially linear thermal expansions thereof, said bioglass coating being bonded to said metal surface by ion diffusion through said oxidized surface.
Claim 2
Independent Claim
256 words
A method of bonding a bioglass layer to a metal substrate comprising: (1) heating a metal substrate having a roughened, oxidized surface to about a maximum temperature (T 1 ) where said T 1 is selected such that the total volume expansion of said metal is substantially equal to that of said bioglass at the temperature (T s ) at which the temperature dependence of the volume of said bioglass becomes non-linear, (2) providing a body of molten bioglass at temperature T w where T w is sufficiently high that the said bioglass is sufficiently fluid to allow immersion of said metal heated to temperature T 1 , (3) immersing said metal surface in said molten bioglass for the minimum time required to permit a layer of desired thickness of said bioglass to adhere to said surface upon termination of said immersion, the time of said immersion being of such duration that the temperature of said metal surface does not rise substantially above T 1 , (4) terminating said immersion, (5) allowing said coating to cool rapidly from T w to about T s , whereby the thermo-mechanical stresses in said bioglass layer are rapidly relieved, and (6) allowing said coated substrate to further cool to a temperature below about T s , whereby the thermo-mechanical stresses in said bioglass coating and said metal surface are relieved at a substantially equal rate due to the substantially linear thermal expansions thereof, said bioglass coating being bonded to said metal surface by ion diffusion through said oxidized surface.
Claim 3
Dependent Claim
38 words
The method of claim 1 wherein a predetermined viscosity of the molten bioglass, prior to immersion, is maintained by temperature adjustment in order to control the desired thickness of said adhered layer of bioglass on said metal surface.
Claim 4
Dependent Claim
23 words
The method of claim 2 wherein the temperature of said molten bioglass is maintained at between about 1250° C. to about 1550° C.
Claim 5
Dependent Claim
14 words
The method of claim 1 wherein said T 1 is above about 700° C.
Claim 6
Dependent Claim
29 words
The method of claim 1 wherein said metal surface has a degree of roughness below that at which mechanical interlocking between said metal surface and said bioglass coating occurs.
Claim 7
Dependent Claim
14 words
The method of claim 1 including the step of oxidizing said roughened metal surface.
Claim 8
Dependent Claim
24 words
The method of claim 6 wherein said metal surface is oxidized by exposing said metal surface to an oxidizing temperature at an elevated temperature.
Claim 9
Dependent Claim
29 words
The method of claim 1, wherein said metal is a steel, a cobalt-chrome alloy, titanium or titanium alloy, a noble metal or noble metal alloy, or a molybdenum-nickel-cobalt-chrome alloy.
Claim 10
Dependent Claim
11 words
The method of claim 8 wherein said steel is stainless steel.
Claim 11
Dependent Claim
11 words
The method of claim 8 wherein said steel is carbon steel.
Claim 12
Dependent Claim
23 words
The method of claim 1 wherein said bioglass has a moderately high alkali content and is substantially invert with respect to silica content.
Claim 13
Dependent Claim
31 words
The method of claim 11 wherein said bioglass contains, by weight: SiO 2 --40-62% Na 2 O--10-32% Ca0--10-32% P 2 o 5 --0-12% caF 2 --0-18% B 2 o 3 --0-20%.
Claim 14
Dependent Claim
25 words
the method of claim 1 wherein said biologically active glass contains, by weight: SiO 2 --45.0% Na 2 O--24.5% CaO--24.5% P 2 o 5 --6.0%.
Claim 15
Dependent Claim
19 words
the method of claim 1 wherein said biologically active glass contains, by weight: SiO 2 --42.94% Na 2 O--23.37%
Claim 16
Dependent Claim
9 words
CaO--11.69% P 2 o 5 --5.72% caF 2 --16.26%.
Claim 17
Dependent Claim
9 words
CaO--11.69% P 2 o 5 --5.72% caF 2 --16.26%.
Claim 18
Dependent Claim
30 words
The method of claim 1 wherein said biologically active glass contains, by weight: SiO 2 --40.0% Na 2 O--24.5% CaO--24.5% P 2 o 5 --6.0% b 2 o 3 --5.0%.
Claim 19
Dependent Claim
19 words
the method of claim 1 wherein the thickness of said bioglass coating is from about 0.2mm to about 2mm.
Claim 20
Dependent Claim
16 words
The method of claim 1 wherein the time of immersion is less than about 5 seconds.
Claim 21
Dependent Claim
26 words
The method of claim 6 wherein said metal is a steel and is oxidized by exposure to air at about 800° C. for about 20 minutes.
References Cited (Backward Citations)
US2886463A
Cited
US3220815A
Cited
US3370991A
Cited
US3497376A
Cited
US3465424A
Cited
US3669715A
Cited
US3922155A
Cited
US3981736A
Cited
US3987499A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-06-25 | 1982-12-25 | 1983-06-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-06-25 | 1986-12-25 | 1987-06-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-06-25 | 1990-12-25 | 1991-06-26 | $7700.00 | Window Closed / Lapsed |