Process for producing ceramic substrates for electronic circuits
Assignee: Siemens AG
•
Filing: 1978-06-02
•
Granted: 1979-06-26
•
Expires: 1998-06-02
Abstract
Abstract A substantially homogeneous ceramic mass comprised of about 48 to 88 wt. % of alumina; about 4 to 12 wt. % of polyvinyl butyral; about 0.5 to 5 wt. % of polypropylene oxide - ethylene oxide block polymer; about 3 to 10 wt. % of a polymer solution comprised of acrylic acid esters, methacrylic acid esters and mixed polymers thereof; about 3 to 10 wt. % of a polyvalent alcohol and mixtures of such alcohols; about 1 to 5 wt. % of triethylene glycol and about 0.5 to 10 wt. % of water is produced and vacuum-extruded into an endless relatively flat strip, dried to a green state, shaped into a desired substrate shape and, if to be used with thin layer circuits, subjected to a plane-parallel pressure of about 9,000 to 12,000 N/cm 2 and then fired or sintered into rigid ceramic substrates.
Inventors
- 👤 Michael Mazzuchelli
- 👤 Christian Stein
- 👤 Manfred Wintzer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 01:18
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/622; C04B35/626; C04B35/63; C04B35/632; C04B35/634; C04B35/63404; C04B35/6342; C04B35/01; C04B35/10; C04B35/111; C04B35/63424; C04B35/63444; C04B35/63448; C04B35/63452; C04B35/63488; H; H10; H10W; H10W99/00
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
164 words
In a process for producing a ceramic substrate wherein a substantially homogeneous extrudable ceramic mass comprised of aluminum, an organic bonding agent, a plasticizing agent, an emulsifying agent and water is transformed by extrusion into a cohesive flat strip, the strip is green dried and cut into desired size bodies which are then sintered, the improvement comprising wherein said ceramic mass consists essentially of about 48 to 88 wt. % of alumina; about 4 to 12 wt. % of polyvinyl butyral; about 0.5 to 5 wt. % of polypropylene oxide-ethylene oxide block polymer; about 3 to 10 wt. % of a polymer solution containing a polymer selected from a group consisting of acrylic acid esters, methacrylic acid esters and mixed polymers thereof; about 3 to 10 wt. % of an alcohol selected from a group consisting of a polyvalent alcohol and mixtures of polyvalent alcohols; and about 1 to 5 wt. % of triethylene glycol and about 0.5 to 10 wt. % of water.
Claim 2
Dependent Claim
164 words
In a process for producing a ceramic substrate wherein a substantially homogeneous extrudable ceramic mass comprised of aluminum, an organic bonding agent, a plasticizing agent, an emulsifying agent and water is transformed by extrusion into a cohesive flat strip, the strip is green dried and cut into desired size bodies which are then sintered, the improvement comprising wherein said ceramic mass consists essentially of about 48 to 88 wt. % of alumina; about 4 to 12 wt. % of polyvinyl butyral; about 0.5 to 5 wt. % of polypropylene oxide-ethylene oxide block polymer; about 3 to 10 wt. % of a polymer solution containing a polymer selected from a group consisting of acrylic acid esters, methacrylic acid esters and mixed polymers thereof; about 3 to 10 wt. % of an alcohol selected from a group consisting of a polyvalent alcohol and mixtures of polyvalent alcohols; and about 1 to 5 wt. % of triethylene glycol and about 0.5 to 10 wt. % of water.
Claim 3
Dependent Claim
114 words
In a process as defined in claim 1 wherein said ceramic mass consists essentially of about 76 to 84 wt. % of alumina; about 6 to 8 wt. % of polyvinyl butyral; about 0.7 to 0.9 wt. % of polypropylene oxide-ethylene oxide block polymer; about 3 to 4 wt. % of a polymer solution containing a polymer selected from a group consisting of acrylic acid esters, methacrylic acid esters and mixed polymers thereof; about 5 to 7 wt. % of an alcohol selected from a group consisting of a polyvalent alcohol and mixtures of polyvalent alcohols; about 1 to 1.4 wt. % of triethylene glycol and about 1 to 2 wt. % of water.
Claim 4
Dependent Claim
20 words
In a process as defined in claim 1 wherein said polymer solution contains a solvent comprised of an aromatic/butanol mixture.
Claim 5
Dependent Claim
17 words
A process as defined in claim 3 wherein said polymer solution comprises about a 50% polymer solution.
Claim 6
Dependent Claim
24 words
A process as defined in claim 1 wherein said alcohol is selected from the group consisting of polyether polyol and mixtures of polyether polyols.
Claim 7
Dependent Claim
24 words
In a process as defined in claim 1 wherein said ceramic mass contains alumina having an average maximum particle size of about 1 μm.
Claim 8
Dependent Claim
21 words
In a process as defined in claim 1 wherein said ceramic mass is transformed into said flat strip via vacuum extrusion.
Claim 9
Dependent Claim
37 words
In a process as defined in claim 1 wherein said strip is green dried at a temperature ranging between about 80° C. to 90° C. over a period of time ranging between about 5 to 10 hours.
Claim 10
Dependent Claim
32 words
In a process as defined in claim 1 wherein said bodies, prior to sintering, are subjected to a pressure ranging between about 9,000 and 12,000 N/cm 2 between highly polished plane-parallel surfaces.
Claim 11
Dependent Claim
25 words
In a process as defined in claim 9 wherein said pressure is maintained for a period of time ranging between about 1 to 5 minutes.
Claim 12
Dependent Claim
36 words
In a process as defined in claim 1 wherein said bodies are sintered at a temperature ranging between about 1480° C. to 1570° C. over a period of time ranging between about 2 to 5 hours.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-06-25 | 1982-12-25 | 1983-06-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-06-25 | 1986-12-25 | 1987-06-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-06-25 | 1990-12-25 | 1991-06-26 | $7700.00 | Window Closed / Lapsed |