Carboxylic acid in alkali metal carboxylate rubber solution
Assignee: Phillips Petroleum Co
•
Filing: 1978-03-20
•
Granted: 1979-06-19
•
Expires: 1998-03-20
Abstract
Abstract A mixture of a carboxylic acid and an alkali metal carboxylate-containing rubber in a vinyl monomer is provided. The resulting composition has a relatively low viscosity and is particularly adapted for preparing a thermosettable composition suitable for preparing reinforced plastic articles by combining an unsaturated polyester, the alkali metal carboxylate-containing rubber solution containing the carboxylic acid, a catalyst, and a reinforcing agent. The resulting composition when cured exhibits high impact strength and good surface finish.
Inventors
- 👤 George A. Moczygemba
- 👤 Aubrey South, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 18:20
CPC Classifications
C; C08; C08L; C08L13/00; C08L67/00; C08L67/06; C08K; C08K3/00; C08K3/18; C08K3/20; C08K3/22; C08K3/24; C08K3/26; C08K7/00; C08K7/02; C08K7/04; C08K7/14
Claims Analysis
Total Claims: 27
Claim 1
Independent Claim
45 words
A composition resulting from mixing ingredients comprising (a) an unsaturated polyester prepared by reacting an unsaturated dicarboxylic acid and a polyol; (b) a normally solid alkali metal carboxylate-containing rubber; (c) a carboxylic acid; (d) a vinyl monomer; (e) a catalyst; and (f) a reinforcing agent.
Claim 2
Dependent Claim
45 words
A composition resulting from mixing ingredients comprising (a) an unsaturated polyester prepared by reacting an unsaturated dicarboxylic acid and a polyol; (b) a normally solid alkali metal carboxylate-containing rubber; (c) a carboxylic acid; (d) a vinyl monomer; (e) a catalyst; and (f) a reinforcing agent.
Claim 3
Dependent Claim
32 words
A composition according to claim 1 wherein said rubber of (b) contains from 0.01 to 1 weight percent alkali metal carboxylate based on the total weight of said alkali metal carboxylate-containing rubber.
Claim 4
Dependent Claim
27 words
A composition according to claim 1 wherein said alkali metal is lithium and said rubber is a copolymer of a conjugated diene and a monovinyl-substituted aromatic compound.
Claim 5
Dependent Claim
29 words
A composition according to claim 3 wherein said rubber is prepared by contacting at least one monomer with an organo alkali metal compound and thereafter treating with carbon dioxide.
Claim 6
Dependent Claim
95 words
A composition according to claim 4 wherein said rubber is a copolymer of butadiene and styrene having a weight average molecular weight within the range of 50,000 to 250,000, said polyester is prepared by reacting fumaric acid and propylene glycol, said vinyl monomer is styrene, said catalyst is a peroxide, and wherein a ratio of (a) to (b) is within the range of 5:1 to 1:1 and wherein said vinyl monomer is present in an amount within the range of 30 to 200 parts by weight per 100 parts by weight of (a) plus (b).
Claim 7
Dependent Claim
33 words
A composition according to claim 5 wherein said reinforcing agent is glass fibers, said catalyst is tertiary butyl perbenzoate and wherein said composition contains in addition calcium carbonate, zinc stearate, and magnesium hydroxide.
Claim 8
Dependent Claim
13 words
A cured article produced by subjecting the composition of claim 6 to heat.
Claim 9
Dependent Claim
13 words
A cured article produced by subjecting the composition of claim 1 to heat.
Claim 10
Dependent Claim
23 words
A composition according to claim 1 wherein said rubber contains metal carboxylate groups distributed essentially randomly along the backbone of the molecules thereof.
Claim 11
Dependent Claim
57 words
A composition made up of ingredients consisting essentially of: (a) an unsaturated polyester prepared by reacting an unsaturated dicarboxylic acid and a polyol; (b) a normally solid alkali metal carboxylate-containing rubber; (c) a carboxylic acid; (d) a vinyl monomer; (e) a catalyst; (f) a fibrous reinforcing agent; (g) a lubricant; (h) a thickener; and (i) a filler.
Claim 12
Dependent Claim
57 words
A composition made up of ingredients consisting essentially of: (a) an unsaturated polyester prepared by reacting an unsaturated dicarboxylic acid and a polyol; (b) a normally solid alkali metal carboxylate-containing rubber; (c) a carboxylic acid; (d) a vinyl monomer; (e) a catalyst; (f) a fibrous reinforcing agent; (g) a lubricant; (h) a thickener; and (i) a filler.
Claim 13
Dependent Claim
36 words
A composition according to claim 10 wherein said lubricant is one of aluminum, barium, calcium, magnesium or zinc stearate, and wherein said thickener is selected from oxides and hydroxides of magnesium, calcium, strontium, barium, and zinc.
Claim 14
Independent Claim
57 words
A method of forming compositions suitable for preparing reinforced plastic articles comprising mixing together under conditions of moderate shear; (a) an unsatuated polyester prepared by reacting an unsaturated dicarboxylic acid and a polyol; (b) a normally solid alkali metal carboxylate-containing rubber; (c) a carboxylic acid; (d) a vinyl monomer; (e) a catalyst; and (f) a reinforcing agent;
Claim 15
Independent Claim
57 words
A method of forming compositions suitable for preparing reinforced plastic articles comprising mixing together under conditions of moderate shear; (a) an unsatuated polyester prepared by reacting an unsaturated dicarboxylic acid and a polyol; (b) a normally solid alkali metal carboxylate-containing rubber; (c) a carboxylic acid; (d) a vinyl monomer; (e) a catalyst; and (f) a reinforcing agent;
Claim 16
Dependent Claim
18 words
A method according to claim 12 wherein said mixing is done with a twin-rotor mixer using sigma blades.
Claim 17
Dependent Claim
16 words
A method according to claim 12 wherein said shear produces a temperature rise of 2°-30° C.
Claim 18
Dependent Claim
29 words
A method according to claim 12 wherein the resulting composition is subjected to curing conditions of 100° to 200° C. for a time within the range of 1-15 minutes.
Claim 19
Dependent Claim
141 words
A method according to claim 12 wherein said unsaturated polyester is produced by reacting fumaric acid and propylene glycol, said normally solid alkali metal carboxylate-containing rubber is provide by contacting 1,3-butadiene and styrene monomers with n-butyllithium, said vinyl monomer is styrene present in an amount within the range of 30 to 200 parts by weight per 100 parts by weight of (a) plus (b), said catalyst is tertiary butyl perbenzoate, said filler is calcium carbonate present in an amount within the range of 200 to 800 parts by weight of filler per 100 parts by weight of (a) plus (b), said lubricant is zinc stearate, said thickening agent is magnesium hydroxide and said reinforcing agent is glass fibers present in an amount within the range of 40 to 200 parts by weight per 100 parts by weight of (a) plus (b).
Claim 20
Dependent Claim
24 words
A composition formed by mixing ingredients comprising: (a) a normally solid alkali metal carboxylate-containing rubber; (b) a carboxylic acid; and (c) a vinyl monomer.
Claim 21
Dependent Claim
24 words
A composition formed by mixing ingredients comprising: (a) a normally solid alkali metal carboxylate-containing rubber; (b) a carboxylic acid; and (c) a vinyl monomer.
Claim 22
Dependent Claim
60 words
A composition according to claim 17 wherein said rubber is a copolymer of styrene and butadiene produced with an n-butyllithium initiator followed by treatment with carbon dioxide, said carboxylic acid is selected from acetic acid methacrylic acid, benzoic acid, capric acid, lauric acid, myristic acid, palimitic acid, elaidic acid, stearic acid, and arachidic acid, and said vinyl monomer is styrene.
Claim 23
Dependent Claim
31 words
A composition according to claim 17 wherein said acid is selected from methacrylic acid and stearic acid and wherein said rubber is present in an amount of about 30 weight percent.
Claim 24
Dependent Claim
13 words
A composition according to claim 1 wherein the carboxylic acid is stearic acid.
Claim 25
Dependent Claim
13 words
A composition according to claim 4 wherein the carboxylic acid is stearic acid.
Claim 26
Dependent Claim
13 words
A method according to claim 12 wherein the carboxylic acid is stearic acid.
Claim 27
Dependent Claim
13 words
A composition according to claim 17 wherein the carboxylic acid is stearic acid.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-06-18 | 1982-12-18 | 1983-06-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-06-18 | 1986-12-18 | 1987-06-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-06-18 | 1990-12-18 | 1991-06-19 | $7700.00 | Window Closed / Lapsed |