Halogenated butyl interlayer for reinforced elastomeric hose articles
Assignee: Gates Corp
•
Filing: 1978-01-23
•
Granted: 1979-06-12
•
Expires: 1998-01-23
Abstract
Abstract A composite reinforced vulcanized elastomeric hose is disclosed including a tube, an outer cover, an interlayer interposed between the tube and cover, and a reinforcement embedded in the hose wall. The outer cover and inner tube are composed of dissimilar polymers not readily bondable to one another, one of which is an EPDM type, and the interlayer is composed of halogenated butyl which securely bonds the dissimilar polymers together and provides a low permeability internal fluid barrier for the hose article with protection to the embedded reinforcement.
Inventors
- 👤 Gene E. Stefano
- 👤 David N. Tally
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 10:29
CPC Classifications
B; B29; B29D; B29D23/00; B29D23/001; B29D23/18; F; F16; F16L; F16L11/00; F16L11/04; F16L11/08; F16L11/081; F16L11/11; F16L11/112; B29K; B29K2021/00; B29K2105/00; B29K2105/06
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
128 words
A method for making a textile layer reinforced composite hose article resistant to fluid penetration, comprising: forming a cylindrically shaped tube of vulcanizable elastomer comprising a terpolymer of mixed mono-olefins and polyolefins blended with ultrarapid accelerators and curing agent; applying to one side of a textile layer a gum layer of chlorinated butyl vulcanizable elastomer, said gum layer making direct adhering contact with fibers of said textile layer; positioning the textile layer about the tube with the gum layer of the chlorinated butyl elastomer interposed between the tube and textile layer to produce a preform; applying a cover over the textile preform composed of an elastomeric material dissimilar from and not readily bondable to said terpolymer; and vulcanizing the thus formed article to produce a composite unitary hose.
Claim 2
Independent Claim
128 words
A method for making a textile layer reinforced composite hose article resistant to fluid penetration, comprising: forming a cylindrically shaped tube of vulcanizable elastomer comprising a terpolymer of mixed mono-olefins and polyolefins blended with ultrarapid accelerators and curing agent; applying to one side of a textile layer a gum layer of chlorinated butyl vulcanizable elastomer, said gum layer making direct adhering contact with fibers of said textile layer; positioning the textile layer about the tube with the gum layer of the chlorinated butyl elastomer interposed between the tube and textile layer to produce a preform; applying a cover over the textile preform composed of an elastomeric material dissimilar from and not readily bondable to said terpolymer; and vulcanizing the thus formed article to produce a composite unitary hose.
Claim 3
Dependent Claim
38 words
The method of claim 1 wherein the gum layer of halogenated butyl is applied separately to both sides of the textile layer so as to directly bond together and embed the textile layer in the halogenated butyl elastomer.
Claim 4
Dependent Claim
22 words
The method of claim 2 wherein the textile layer has interstices therein, permitting flow of the halogenated butyl elastomer through such interstices.
Claim 5
Dependent Claim
34 words
The method of claim 1 wherein the gum layer of halogenated butyl has a cure rate, calculated on an equivalent basis, which is intermediate the cure rate of the tube and cover elastomeric materials.
Claim 6
Dependent Claim
20 words
The method of claim 4 wherein the ultrarapid accelerators comprise alkyl substituted thiuramsulfides, zinc alkyl substituted thiocarbamate, and substituted thiomorpholine.
Claim 7
Dependent Claim
32 words
The method of claim 1 wherein the gum layer of halogenated butyl is applied to the textile layer by calendering the gum layer on at least one side of the textile layer.
Claim 8
Dependent Claim
34 words
The method of claim 6 wherein the calendered textile layer is positioned about the tube by wrapping the calendered fabric about the tube with the calendered layer of halogenated butyl applied adjacent the tube.
Claim 9
Independent Claim
127 words
A method for making a textile layer reinforced composite hose article resistant to external gas penetration, comprising: extruding a tube of a heat setting elastomeric material other than butyl rubber or EPDM, and which does not normally bond to EPDM-type terpolymers; twining a textile layer reinforcement over the tube; applying a gum layer of chlorinated butyl elastomer over the textile layer and completely covering the same, said gum layer being in direct adhering contact with fibers of said textile layer; extruding or wrapping a cover layer of EPDM-type terpolymer over the chlorinated butyl layer whereby the interposed halogenated butyl layer acts as a premeability barrier between the textile layer reinforcement and cover of EPDM-type terpolymer; and vulcanizing the thus formed article to produce a composite unitary base.
Claim 10
Independent Claim
127 words
A method for making a textile layer reinforced composite hose article resistant to external gas penetration, comprising: extruding a tube of a heat setting elastomeric material other than butyl rubber or EPDM, and which does not normally bond to EPDM-type terpolymers; twining a textile layer reinforcement over the tube; applying a gum layer of chlorinated butyl elastomer over the textile layer and completely covering the same, said gum layer being in direct adhering contact with fibers of said textile layer; extruding or wrapping a cover layer of EPDM-type terpolymer over the chlorinated butyl layer whereby the interposed halogenated butyl layer acts as a premeability barrier between the textile layer reinforcement and cover of EPDM-type terpolymer; and vulcanizing the thus formed article to produce a composite unitary base.
Claim 11
Dependent Claim
28 words
The method of claim 8 wherein the textile reinforcement is calendered separately with the halogenated butyl elastomer to form a layer thereover, prior to positioning over said tube.
References Cited (Backward Citations)
US2968588A
Cited
US3106950A
Cited
US2933117A
Cited
US3039906A
Cited
US3076737A
Cited
US3091560A
Cited
US3712360A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-06-11 | 1982-12-11 | 1983-06-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-06-11 | 1986-12-11 | 1987-06-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-06-11 | 1990-12-11 | 1991-06-12 | $7700.00 | Window Closed / Lapsed |