Method of drawing glass optical waveguides
Assignee: Corning Glass Works
•
Filing: 1978-02-21
•
Granted: 1979-06-12
•
Expires: 1998-02-21
Abstract
Abstract A method of making glass optical waveguides by the flame hydrolysis technique. Particles of glass soot produced by flame hydrolysis are deposited on the outside surface of a mandrel to form a porous preform. The soot particles closer to the mandrel have a refractive index greater than that of the soot disposed toward the outer surface of the preform. The mandrel is removed and the resultant hollow soot preform is supported in a draw furnace through which a helium-rich gas flows. The preform is heated to a temperature sufficient to cause said soot to consolidate and simultaneously permit an optical waveguide filament to be drawn therefrom.
Inventors
- 👤 Alan C. Bailey
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 12:42
CPC Classifications
C; C03; C03B; C03B37/00; C03B37/01; C03B37/02; C03B37/025; C03B37/027; C03B37/012; C03B37/014; C03B37/01446; C03B37/01486; C03B37/02736; C03B2201/00; C03B2201/06; C03B2201/08; C03B2201/10; C03B2201/20; C03B2201/28; C03B2201/30; C03B2201/31; C03B2201/32; C03B2201/34; C03B2201/40; C03B2201/42; Y; Y10; Y10S; Y10S65/00; Y10S65/90
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
96 words
A method of forming a high purity glass filament comprising the steps of providing a substantially cylindrical mandrel, applying a first coating of glass soot to the outside peripheral surface of said mandrel, removing said mandrel to form a soot preform having an aperture therein, heating said preform to a sufficiently high temperature for a sufficient period of time to permit the soot at at least one end thereof to consolidate, and simultaneously drawing the consolidated portion of said preform to reduce the cross-sectional area thereof and close said aperture, thereby forming an optical waveguide filament.
Claim 2
Independent Claim
96 words
A method of forming a high purity glass filament comprising the steps of providing a substantially cylindrical mandrel, applying a first coating of glass soot to the outside peripheral surface of said mandrel, removing said mandrel to form a soot preform having an aperture therein, heating said preform to a sufficiently high temperature for a sufficient period of time to permit the soot at at least one end thereof to consolidate, and simultaneously drawing the consolidated portion of said preform to reduce the cross-sectional area thereof and close said aperture, thereby forming an optical waveguide filament.
Claim 3
Dependent Claim
61 words
A method in accordance with claim 1 wherein the step of applying a first coating of glass soot comprises applying a plurality of distinct and successive layers of glass soot, each distinct layer having a substantially uniform composition therethrough but having a progressively different composition from the preceding layer so as to form a structure having a stepped, radially varying composition.
Claim 4
Dependent Claim
57 words
A method in accordance with claim 1 wherein, prior to the step of removing said mandrel, said method comprises applying a second coating of glass soot over the outside peripheral surface of said first coating, the glass soot of said second coating having a refractive index less than that of the glass soot of said first coating.
Claim 5
Dependent Claim
22 words
A method in accordance with claim 1 wherein, prior to the time that said aperture closes, helium is bled into said aperture.
Claim 6
Dependent Claim
23 words
A method in accordance with claim 1 wherein, during the step of heating said preform, said preform is subjected to a helium-rich atmosphere.
Claim 7
Dependent Claim
41 words
A method in accordance with claim 5 wherein the step of heating said preform to a sufficient temperature comprises heating said preform to a temperature at which the viscosity of said core glass is between 10 8 and 10 3 poise.
Claim 8
Dependent Claim
31 words
A method in accordance with claim 6 wherein, prior to the step of drawing, helium is bled into said aperture to purge residual gases from the interstices of said soot preform.
Claim 9
Independent Claim
150 words
A method of forming a glass optical waveguide comprising the steps of providing a substantially cylindrical mandrel, applying a first coating of glass soot to the outside peripheral surface of said mandrel, applying a second coating of glass soot over the outside peripheral surface of said first coating, the glass soot of said second coating having a refractive index less than that of the glass soot of the first coating, removing said mandrel to form a soot preform having an aperture therein, affixing a handle to one end of said preform, supporting said preform by said handle in a draw furnace, heating said preform to a sufficiently high temperature for a sufficient period of time to permit the soot at one end thereof to consolidate, and simultaneously drawing the consolidated portion of said preform to reduce the cross-sectional area thereof and close said aperture, thereby forming an optical waveguide filament.
Claim 10
Independent Claim
150 words
A method of forming a glass optical waveguide comprising the steps of providing a substantially cylindrical mandrel, applying a first coating of glass soot to the outside peripheral surface of said mandrel, applying a second coating of glass soot over the outside peripheral surface of said first coating, the glass soot of said second coating having a refractive index less than that of the glass soot of the first coating, removing said mandrel to form a soot preform having an aperture therein, affixing a handle to one end of said preform, supporting said preform by said handle in a draw furnace, heating said preform to a sufficiently high temperature for a sufficient period of time to permit the soot at one end thereof to consolidate, and simultaneously drawing the consolidated portion of said preform to reduce the cross-sectional area thereof and close said aperture, thereby forming an optical waveguide filament.
Claim 11
Dependent Claim
21 words
A method in accordance with claim 8 wherein, during the step of drawing, said preform is disposed in a helium-rich atmosphere.
Claim 12
Dependent Claim
47 words
A method in accordance with claim 9 wherein the step of affixing a handle comprises inserting into an end of said aperture a hollow tube having at least one protrusion thereon, and twisting said tube to cause said protrusion to engage the aperture-forming wall of said preform.
Claim 13
Dependent Claim
25 words
A method in accordance with claim 10 wherein loose soot is blown from said preform by an inert gas after said tube is inserted therein.
Claim 14
Dependent Claim
46 words
A method in accordance with claim 11 wherein, prior to the time that said drawing step is initiated, helium is bled through said tube into said aperture, the flow of helium into said aperture being terminated prior to the time that said drawing step is intiated.
Claim 15
Independent Claim
77 words
A method of forming a high purity glass filament comprising the steps of providing a substrate, applying a first coating of glass soot to a surface of said substrate, heating the resultant combination to a sufficiently high temperature for a sufficient period of time to permit the soot at at least one end thereof to consolidate, and simultaneously drawing the consolidated portion of said combination to reduce the cross-sectional area thereof, thereby forming an optical waveguide filament.
Claim 16
Independent Claim
77 words
A method of forming a high purity glass filament comprising the steps of providing a substrate, applying a first coating of glass soot to a surface of said substrate, heating the resultant combination to a sufficiently high temperature for a sufficient period of time to permit the soot at at least one end thereof to consolidate, and simultaneously drawing the consolidated portion of said combination to reduce the cross-sectional area thereof, thereby forming an optical waveguide filament.
Claim 17
Dependent Claim
14 words
A method in accordance with claim 13 wherein said substrate is a glass rod.
Claim 18
Dependent Claim
14 words
A method in accordance with claim 13 wherein said substrate is a glass tube.
References Cited (Backward Citations)
US3737292A
Cited
US3737293A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-06-11 | 1982-12-11 | 1983-06-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-06-11 | 1986-12-11 | 1987-06-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-06-11 | 1990-12-11 | 1991-06-12 | $7700.00 | Window Closed / Lapsed |