Resin rich polybutadiene-mica flexible high voltage insulation
Assignee: Westinghouse Electric Corp
•
Filing: 1977-05-26
•
Granted: 1979-06-05
•
Expires: 1997-05-26
Abstract
Abstract A resinous composition useful for impregnating flexible electrical winding tape is made by mixing: (a) 100 parts of polybutadiene, (b) about 0.25 part to about 25 parts of a solid, organic, aromatic, vinyl monomer coreactive with polybutadiene, (c) a solvent for the polybutadiene and (d) an effective amount of organic reaction catalyst.
Inventors
- 👤 James D. B. Smith
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 16:56
CPC Classifications
H; H02; H02K; H02K3/00; H02K3/30; C; C08; C08K; C08K5/00; C08K5/01; H01; H01B; H01B13/00; H01B13/30; H01B3/00; H01B3/02; H01B3/04; H01B3/18; H01B3/30; H01B3/44; H01B3/441; H01F; H01F27/00; H01F27/28; H01F27/32; H01F27/323; H01F27/327; Y; Y10; Y10T; Y10T428/00; Y10T428/25; Y10T428/251; Y10T428/29; Y10T428/2911; Y10T428/31504; Y10T428/31855; Y10T428/31931; Y10T442/00; Y10T442/30; Y10T442/3382; Y10T442/3415; Y10T442/3455; Y10T442/3927; Y10T442/3935
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
147 words
A void free high voltage capability electrical pre-preg winding insulation tape, comprising mica, and a contacting polymerizable resinous composition consisting essentially of a homogeneous, substantially unreacted mixture of polybutadiene consisting of from about 20 weight percent to about 98 weight percent of 1,2-polybutadiene and from about 2 weight percent to about 80 weight percent of 1,4-polybutadiene; about 0.25 part to about 25 parts per 100 parts of total polybutadiene of a solid vinyl monomer coreactive with polybutadiene selected from the group consisting of vinyl carbazole, 1-vinyl naphthalene, 2-vinyl naphthalene, vinyl anthracene, N-vinyl phthalimide and mixtures thereof; up to about 5 weight percent of solvent for the polybutadiene and an amount of an organic reaction catalyst effective to cure the resinous mixture, at resin composition temperatures of at least about 130° C., said pre-preg being dry and highly flexible, having a shelf life of at least 6 months.
Claim 2
Dependent Claim
147 words
A void free high voltage capability electrical pre-preg winding insulation tape, comprising mica, and a contacting polymerizable resinous composition consisting essentially of a homogeneous, substantially unreacted mixture of polybutadiene consisting of from about 20 weight percent to about 98 weight percent of 1,2-polybutadiene and from about 2 weight percent to about 80 weight percent of 1,4-polybutadiene; about 0.25 part to about 25 parts per 100 parts of total polybutadiene of a solid vinyl monomer coreactive with polybutadiene selected from the group consisting of vinyl carbazole, 1-vinyl naphthalene, 2-vinyl naphthalene, vinyl anthracene, N-vinyl phthalimide and mixtures thereof; up to about 5 weight percent of solvent for the polybutadiene and an amount of an organic reaction catalyst effective to cure the resinous mixture, at resin composition temperatures of at least about 130° C., said pre-preg being dry and highly flexible, having a shelf life of at least 6 months.
Claim 3
Dependent Claim
62 words
The highly flexible winding tape of claim 1, wherein the reaction catalyst is a free radical catalyst selected from the group consisting of catalytic peroxides, azo compounds having the structural formula R--N═N--R where R can be alkyl or aryl, and mixtures thereof, and wherein the catalyst is added at between about 0.25 part to about 5 parts per 100 parts of polybutadiene.
Claim 4
Dependent Claim
59 words
The highly flexible winding tape of claim 1, wherein the vinyl monomer coreactive with polybutadiene is selected from the group consisting of vinyl carbazole, 1-vinyl naphthalene, and mixtures thereof, the reaction catalyst is selected from the group consisting of benzoyl peroxide; dicumyl peroxide; lauroyl peroxide, methyl ethyl ketone peroxide; 2,5-dimethyl-2,5 bis(benzoylperoxy hexane); 2-(tert-butylazo) isobutryonitrile; 2-tert-butylazo-2,4-dimethylpentane; 1-tert-butylazo-1-phenylcyclohexane and mixtures thereof.
Claim 5
Dependent Claim
42 words
The highly flexible winding tape of claim 1, wherein the winding tape, is non-tacky and can be wound onto a reel without sticking to itself, and the power factor values of the winding tape upon cure are below 2% at 150° C.
Claim 6
Dependent Claim
63 words
The highly flexible winding tape of claim 1, wherein the tape comprises mica supported by a backing selected from the groups consisting of cellulose paper, cotton fabric, linen fabric, asbestos paper, glass cloth, glass fibers, mica paper, nylon fabric, polyethylene fabric and polyethylene terephthalate mat, said winding tape containing from about 2 weight percent to about 40 weight percent of the resinous composition.
Claim 7
Dependent Claim
44 words
The highly flexible winding tape of claim 1 containing from about 2 weight percent to about 25 weight percent of the resinous composition and also further impregnated with a resin selected from the group consisting of catalyzed epoxy resin, polyester resin and polybutadiene resin.
Claim 8
Dependent Claim
31 words
The highly flexible winding tape of claim 1 wrapped around an electrical conductor consisting of copper and aluminum, and cured at a resin composition temperature of at least about 130° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-06-04 | 1982-12-04 | 1983-06-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-06-04 | 1986-12-04 | 1987-06-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-06-04 | 1990-12-04 | 1991-06-05 | $7700.00 | Window Closed / Lapsed |