Hydrothermal alkali metal catalyst recovery process
Assignee: ExxonMobil Technology and Engineering Co
•
Filing: 1978-01-27
•
Granted: 1979-06-05
•
Expires: 1998-01-27
Abstract
Abstract In a coal gasification operation or similar conversion process carried out in the presence of an alkali metal-containing catalyst wherein solid particles containing alkali metal residues are produced, alkali metal constituents are recovered from the particles primarily in the form of water soluble alkali metal formates by treating the particles with a calcium or magnesium-containing compound in the presence of water at a temperature between about 250 DEG F. and about 700 DEG F. and in the presence of added carbon monoxide. During the treating process the water insoluble alkali metal compounds comprising the insoluble alkali metal residues are converted into water soluble alkali metal formates. The resultant aqueous solution containing water soluble alkali metal formates is then separated from the treated particles and any insoluble materials formed during the treatment process, and recycled to the gasification process where the alkali metal formates serve as at least a portion of the alkali metal constituents which comprise the alkali metal-containing catalyst. This process permits increased recovery of alkali metal constituents, thereby decreasing the overall cost of the gasification process by reducing the amount of makeup alkali metal compounds necessary.
Inventors
- 👤 James M. Eakman
- 👤 LeRoy R. Clavenna
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 20:14
CPC Classifications
C; C10; C10G; C10G1/00; C10G1/08; C10G1/086; C10J; C10J3/00; C10J3/46; C10J3/48; C10J3/482; C10J3/54; C10J3/58; C10J3/60; C10J3/64; C10J3/66; C10J3/72; C10J3/723; C10J3/74; C10J3/78; C10J3/82; C10J3/84; C10J2300/00; C10J2300/09; C10J2300/0913; C10J2300/093; C10J2300/0943; C10J2300/0946; C10J2300/0953; C10J2300/0959; C10J2300/0966; C10J2300/0973; C10J2300/0976; C10J2300/0983; C10J2300/0996; C10J2300/18; C10J2300/1807; C10J2300/1846; Y; Y10; Y10S; Y10S208/00; Y10S208/951
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
143 words
In a process for the conversion of a solid carbonaceous feed material in the presence of an alkali metal-containing catalyst into liquids and/or gases wherein particles containing alkali metal residues are produced, the improvement which comprises: (a) treating said particles containing said alkali metal residues in a reaction zone with a calcium or magnesium-containing compound in the presence of liquid water at a temperature between about 250° F. and about 700° F. and in the presence of added carbon monoxide thereby converting water insoluble alkali metal constituents in said residues into water soluble alkali metal formates and producing an aqueous solution containing water soluble alkali metal constituents consisting primarily of alkali metal formates; and (b) using said alkali metal constituents from said aqueous solution in said conversion process as at least a portion of the alkali metal constituents comprising said alkali metal-containing catalyst.
Claim 2
Dependent Claim
143 words
In a process for the conversion of a solid carbonaceous feed material in the presence of an alkali metal-containing catalyst into liquids and/or gases wherein particles containing alkali metal residues are produced, the improvement which comprises: (a) treating said particles containing said alkali metal residues in a reaction zone with a calcium or magnesium-containing compound in the presence of liquid water at a temperature between about 250° F. and about 700° F. and in the presence of added carbon monoxide thereby converting water insoluble alkali metal constituents in said residues into water soluble alkali metal formates and producing an aqueous solution containing water soluble alkali metal constituents consisting primarily of alkali metal formates; and (b) using said alkali metal constituents from said aqueous solution in said conversion process as at least a portion of the alkali metal constituents comprising said alkali metal-containing catalyst.
Claim 3
Dependent Claim
13 words
A process as defined in claim 1 wherein said conversion process comprises gasification.
Claim 4
Dependent Claim
13 words
A process as defined in claim 1 wherein said conversion process comprises liquefaction.
Claim 5
Dependent Claim
20 words
A process as defined in claim 1 wherein at least a portion of said alkali metal-containing catalyst comprises potassium carbonate.
Claim 6
Dependent Claim
21 words
A process as defined in claim 1 wherein said particles containing said alkali metal residues are treated with a calcium-containing compound.
Claim 7
Dependent Claim
14 words
A process as defined in claim 5 wherein said calcium-containing compound comprises calcium hydroxide.
Claim 8
Dependent Claim
14 words
A process as defined in claim 1 wherein said carbonaceous feed material comprises coal.
Claim 9
Dependent Claim
39 words
A process as defined in claim 1 wherein said aqueous solution is recycled to said conversion process where said alkali metal formates are used as at least a portion of said alkali metal constituents comprising said alkali metal-containing catalyst.
Claim 10
Dependent Claim
30 words
A process as defined in claim 1 wherein an alkali metal sulfate is added to said reaction zone to produce additional water soluble alkali metal formate in said aqueous solution.
Claim 11
Dependent Claim
142 words
In a process for the gasification of coal in the presence of a carbon-alkali metal catalyst wherein particles containing akali metal residues are produced, the improvement which comprises: (a) treating said particles containing said alkali metal residues in a reaction zone with a calcium-containing compound in the presence of liquid water at a temperature between about 250° F. and about 700° F. and in the presence of added carbon monoxide, thereby converting water insoluble alkali metal constituents in said residues into water soluble alkali metal formates and producing an aqueous solution containing water soluble alkali metal constituents consisting primarily of alkali metal formates; and (b) recycling said aqueous solution containing said water soluble alkali metal constituents to said gasification process where said alkali metal constituents are used as at least a portion of the alkali metal constituents comprising said carbon-alkali metal catalyst.
Claim 12
Dependent Claim
142 words
In a process for the gasification of coal in the presence of a carbon-alkali metal catalyst wherein particles containing akali metal residues are produced, the improvement which comprises: (a) treating said particles containing said alkali metal residues in a reaction zone with a calcium-containing compound in the presence of liquid water at a temperature between about 250° F. and about 700° F. and in the presence of added carbon monoxide, thereby converting water insoluble alkali metal constituents in said residues into water soluble alkali metal formates and producing an aqueous solution containing water soluble alkali metal constituents consisting primarily of alkali metal formates; and (b) recycling said aqueous solution containing said water soluble alkali metal constituents to said gasification process where said alkali metal constituents are used as at least a portion of the alkali metal constituents comprising said carbon-alkali metal catalyst.
Claim 13
Dependent Claim
34 words
A process as defined in claim 10 wherein said particles are treated in the presence of said water and said added carbon monoxide at a temperature between about 300° F. and about 450° F.
Claim 14
Dependent Claim
30 words
A process as defined in claim 10 wherein an alkali metal sulfate is added to said reaction zone to produce additional water soluble alkali metal formates in said aqueous solution.
Claim 15
Dependent Claim
25 words
A process as defined in claim 12 wherein said carbon-alkali metal catalyst comprises a carbon-potassium reaction product and said alkali metal sulfate comprises potassium sulfate.
Claim 16
Dependent Claim
14 words
A process as defined in claim 10 wherein said calcium-containing compound comprises calcium hydroxide.
Claim 17
Dependent Claim
14 words
A process as defined in claim 10 wherein said calcium-containing compound comprises calcium oxide.
References Cited (Backward Citations)
US820374A
Cited
GB190609008A
Cited
US1574875A
Cited
US2043534A
Cited
GB415871A
Cited
US4057512A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-06-04 | 1982-12-04 | 1983-06-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-06-04 | 1986-12-04 | 1987-06-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-06-04 | 1990-12-04 | 1991-06-05 | $7700.00 | Window Closed / Lapsed |