Fire protection covering for small diameter missiles
Assignee: National Aeronautics and Space Administration
•
Filing: 1977-11-25
•
Granted: 1979-05-29
•
Expires: 1997-11-25
Abstract
Abstract New, flexible intumescent protection sheeting of unusually uniform thickness have been prepared from epoxy-polysulfide compositions containing microfibers and the ammonium salt of 1,4-nitroaniline-2-sulfonic acid, as disclosed in U.S. Pat. No. 3,663,464, except that an ammonium salt particle size in the order of 5 to 8 microns and a fiber size of about 1/128th inch in length and 3 to 5 microns in diameter have been found critical to obtain the required density of 1.46 to 1.50 g/cc. The insulation sheeting is prepared by a continuous process involving vacuum mixing, calendering, and curing under very strict conditions which depend to some extent upon the thickness of the sheet produced.
Inventors
- 👤 Salvatore R. Riccitiello
- 👤 Paul M. Sawko
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 16:54
CPC Classifications
F; F42; F42B; F42B39/00; F42B39/14; F42B39/18; C; C08; C08L; C08L63/00; F42B12/00; F42B12/72; F42B12/76; F42B12/80; Y; Y10; Y10S; Y10S428/00; Y10S428/92; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31511; Y10T428/31515; Y10T428/31529; Y10T428/3154
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
201 words
A process for the manufacture of thermal protection sheeting of uniform composition and thickness, which comprises: preparing by vacuum mixing an intumescent paste which comprises: (a) an epoxy resin and (b) a mercaptan-terminated polysulfide polymer having a molecular weight within the range of 600 to 8000, said resin and polymer being present in proportions such that the glass transition temperature of the mixture is at or below room temperature, (c) 20 to 95% by weight, based on the resin-polymer mixture, of ammonium 4-nitroaniline-2-sulfonate having a particle size not greater than about 10 microns; (d) about 2 to 10 parts by weight of microfibers having an average length of within the range of about 1/64 to 1/128 inch and an average diameter of 3 to 5 microns; and (e) up to about 12% of the epoxy resin weight of an amine curing agent; calendering the paste to form a sheet having a thickness within the range of about 0.010 to 0.100 inch; cutting the sheet obtained into missile wrapping lengths; and within 20 minutes of the amine curing agent addition, heating the sheet rapidly to 90° C. and keeping it at 90° C. for a period of exactly 5 to 5.5 minutes.
Claim 2
Dependent Claim
201 words
A process for the manufacture of thermal protection sheeting of uniform composition and thickness, which comprises: preparing by vacuum mixing an intumescent paste which comprises: (a) an epoxy resin and (b) a mercaptan-terminated polysulfide polymer having a molecular weight within the range of 600 to 8000, said resin and polymer being present in proportions such that the glass transition temperature of the mixture is at or below room temperature, (c) 20 to 95% by weight, based on the resin-polymer mixture, of ammonium 4-nitroaniline-2-sulfonate having a particle size not greater than about 10 microns; (d) about 2 to 10 parts by weight of microfibers having an average length of within the range of about 1/64 to 1/128 inch and an average diameter of 3 to 5 microns; and (e) up to about 12% of the epoxy resin weight of an amine curing agent; calendering the paste to form a sheet having a thickness within the range of about 0.010 to 0.100 inch; cutting the sheet obtained into missile wrapping lengths; and within 20 minutes of the amine curing agent addition, heating the sheet rapidly to 90° C. and keeping it at 90° C. for a period of exactly 5 to 5.5 minutes.
Claim 3
Dependent Claim
40 words
The process of claim 1 wherein the epoxy resin and the polysulfide polymer contents of the paste before addition of the amine curing agent are within the range of about 19.2 to 22.5% and 16.0 to 19.0 by weight, respectively.
Claim 4
Dependent Claim
61 words
The process of claim 1 where the intumescent paste comprises, on a weight basis, about 37 to 39% of the epoxy resinpolysulfide polymer mixture, about 51.5 to 59.5% of the ammonium salt and about 2 to 10% of the microfibers, said last two ingredients constituting about 61 to 63% of the composition dry weight before addition of the amine curing agent.
Claim 5
Dependent Claim
74 words
The process of claim 1 wherein the intumescent paste comprises on a weight basis: about 21.4 parts of the epoxy resin, about 17.1 parts of the polysulfide polymer, about 56.5 parts of the ammonium salt at an average particle size of 5 to 8 microns, about 5 parts of the microfibers having an average length of 1/128 inch and an average diameter of 3-5 microns and about 2.5 parts of the amine curing agent.
Claim 6
Dependent Claim
39 words
The process of claim 4 wherein the epoxy resin is an epichlorohydrin-bisphenol A type having a molecular weight of about 400, and the polysulfide has the formula HS--(C.sub.2 H.sub.4 --O--CH.sub.2 --O--C.sub.2 H.sub.4 --S--S).sub.6 C.sub.2 H.sub.4 O--CH.sub.2 --O--C.sub.2 H.sub.4 --SH.
Claim 7
Dependent Claim
19 words
The process of claim 5 wherein the microfibers are made of silica and the curing agent is tris-(dimethyl-aminomethyl) phenol.
Claim 8
Dependent Claim
17 words
Fire protection intumescent sheeting of very uniform thickness and composition prepared by the process of claim 1.
Claim 9
Dependent Claim
20 words
The sheeting of claim 7 covered on one of its surfaces of a thin environmentally resistant and mechanically polymeric film.
Claim 10
Dependent Claim
20 words
The sheeting of claim 8 where the film consists of a polyvinyl fluoride having a thickness of about 0.002 inch.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-05-28 | 1982-11-27 | 1983-05-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-05-28 | 1986-11-27 | 1987-05-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-05-28 | 1990-11-27 | 1991-05-29 | $7700.00 | Window Closed / Lapsed |