US4156654A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for making crude boric acid from borate and sulfuric acid
Assignee: NO-TOX PRODUCTS Inc A CORP OF
•
Filing: 1978-03-31
•
Granted: 1979-05-29
•
Expires: 1998-03-31
Abstract
Abstract For the conversion of sodium tetraborate (e.g. "5 mole borax" or sodium tetraborate pentahydrate) to a solid, particulate mass of flame-retardant chemical, a slurrying amount of water (e.g. 3-5 moles per mole of tetraborate) is first added, so that a stable slurry can be formed. Then 0.95 to 0.98 mole of sulfuric acid is added to the slurry, and the tetraborate is substantially converted to a moist, particulate mixture of boric acid and sodium sulfate, the water in the slurry having been largely driven off as steam. The moist particulate mixture is suitable for imparting flame retardency to cellulosic insulation; preferably, however, it is first dried to <20 wt.-% moisture.
Inventors
- 👤 James R. Blasius
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 12:47
CPC Classifications
C; C09; C09K; C09K21/00; C09K21/02; C01; C01B; C01B35/00; C01B35/08; C01B35/10; C01B35/1045; C01B35/1054; C01B35/1063
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
166 words
A method for converting sodium tetraborate to a solid, particulate fire retardant mixture containing solid, particulate boric acid and sodium sulfate, said method comprising the steps of: a. adding a slurrying amount of water to said sodium tetraborate, said slurrying amount being sufficient to suspend substantially -3 U.S. mesh particles of sodium tetraborate in a uniform slurry comprising a continuous aqueous suspension medium but not sufficient to completely dissolve said sodium tetraborate, said amount of water being less than about 15 moles per mole of sodium tetraborate; b. agitating the undissolved particles of sodium tetraborate so as to form a uniform aqueous slurry of said particles; c. adding to said aqueous slurry about 0.95 to about 0.98 moles of sulfuric acid per mole of said sodium tetraborate, thereby obtaining said fire retardant mixture, and permitting the resulting exotherm to drive off sufficient water vapor from said continuous aqueous suspension medium to convert said medium to a moisture residue on discrete particles of said fire retardant mixture.
Claim 2
Independent Claim
166 words
A method for converting sodium tetraborate to a solid, particulate fire retardant mixture containing solid, particulate boric acid and sodium sulfate, said method comprising the steps of: a. adding a slurrying amount of water to said sodium tetraborate, said slurrying amount being sufficient to suspend substantially -3 U.S. mesh particles of sodium tetraborate in a uniform slurry comprising a continuous aqueous suspension medium but not sufficient to completely dissolve said sodium tetraborate, said amount of water being less than about 15 moles per mole of sodium tetraborate; b. agitating the undissolved particles of sodium tetraborate so as to form a uniform aqueous slurry of said particles; c. adding to said aqueous slurry about 0.95 to about 0.98 moles of sulfuric acid per mole of said sodium tetraborate, thereby obtaining said fire retardant mixture, and permitting the resulting exotherm to drive off sufficient water vapor from said continuous aqueous suspension medium to convert said medium to a moisture residue on discrete particles of said fire retardant mixture.
Claim 3
Dependent Claim
166 words
A method according to claim 1 comprising the steps of: a. blending, in a blending zone, about 3 to about 10 moles of water with each mole of said sodium tetraborate, said sodium tetraborate being a hydrate having 5 to 10 moles of water of hydration; b. forming a said uniform aqueous slurry in said blending zone, said blending zone having an initial temperature, at the beginning of said blending step, below 175° C.; c. adding to said uniform aqueous slurry, over a period of 1-60 minutes, less than 0.98 moles of sulfuric acid per mole of said sodium tetraborate; d. maintaining the temperature of the mixture resulting from said step (c) at a temperature above 100° C. but below 175° C.; e. drying the said fire retardant mixture to recover a generally dry, free-flowing particulate fire-retardant mass containing sodium sulfate and at least 30% by weight B 2 O 3 , generally as boric acid, and having a moisture content below about 20% by weight.
Claim 4
Dependent Claim
31 words
A method according to claim 2 comprising the further step of packaging said dry, free-flowing particulate mixture without further drying and without separation of said sodium sulfate from said boric acid.
Claim 5
Dependent Claim
163 words
A method according to claim 2 wherein: a. the amount of water added in said step (a) is 3-5 moles per mole of said sodium tetraborate; said sodium tetraborate being sodium borate pentahydrate of greater than 99 weight-% purity; b. the formation of said aqueous slurry is carried out semi-continuously by utilizing a plurality of mixing zones, whereby formation of a first batch of said aqueous slurry is completed in a first mixing zone before completion of formation of a second batch of aqueous slurry in a second mixing zone; c. said sulfuric acid is added to said aqueous slurry in each said mixing zone, accompanied by agitation of said aqueous slurry, over a period of time longer than 5 minutes and agitation of the resulting mixture is continued after addition of said sulfuric acid has been completed; and d. the said temperature of said mixture is kept below about 150° C. by cooling said mixing zones at least during said step (c).
Claim 6
Independent Claim
161 words
A method for making an essentially dry, free-flowing particulate mixture consisting essentially of boric acid, a generally negligible amount of boric acid degradation products, and sodium sulfate, said method comprising the steps of: a. introducing sodium tetraborate pentahydrate into a mixing zone; b. introducing 3 to 10 moles, per mole of said pentahydrate, of liquid ambient temperature water into said mixing zone over a period of 1 to 60 minutes, whereby an aqueous slurry of said pentahydrate in said water is formed; c. introducing 0.95-0.98 mole of 90-100 weight-% sulfuric acid over a period of at least 5 minutes and exothermically reacting said sulfuric acid with said pentahydrate to obtain mixture of sodium sulfate and boric acid; d. maintaining the temperature of said mixing zone above 100° C. but below about 150° C. until a generally free-flowing, moist, particulate mixture is obtained; and e. drying the said generally free-flowing, moist, particulate mixture to a moisture content below about 20% by weight.
Claim 7
Independent Claim
161 words
A method for making an essentially dry, free-flowing particulate mixture consisting essentially of boric acid, a generally negligible amount of boric acid degradation products, and sodium sulfate, said method comprising the steps of: a. introducing sodium tetraborate pentahydrate into a mixing zone; b. introducing 3 to 10 moles, per mole of said pentahydrate, of liquid ambient temperature water into said mixing zone over a period of 1 to 60 minutes, whereby an aqueous slurry of said pentahydrate in said water is formed; c. introducing 0.95-0.98 mole of 90-100 weight-% sulfuric acid over a period of at least 5 minutes and exothermically reacting said sulfuric acid with said pentahydrate to obtain mixture of sodium sulfate and boric acid; d. maintaining the temperature of said mixing zone above 100° C. but below about 150° C. until a generally free-flowing, moist, particulate mixture is obtained; and e. drying the said generally free-flowing, moist, particulate mixture to a moisture content below about 20% by weight.
Claim 8
Dependent Claim
71 words
A method according to claim 5 comprising the additional step of packaging the product of said step (e), said product of said step (e) consisting essentially of 30-40% by weight B 2 O 3 , essentially as boric acid, and 30 to 40% by weight sodium sulfate, a 2 weight-% solution of said product in water having a pH at 23° C. which is greater than 7 but less than 8.
Claim 9
Dependent Claim
25 words
A method according to claim 5 wherein said method is carried out semi-continuously by means of the alternating use of a plurality of mixing zones.
Claim 10
Dependent Claim
20 words
A method according to claim 1, wherein said steps (a) and (b) are carried out substantially at the same time.
Claim 11
Dependent Claim
20 words
A method according to claim 2 wherein said steps (a) and (b) are carried out substantially at the same time.
References Cited (Backward Citations)
BE631217A
Cited
US3917801A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-05-28 | 1982-11-27 | 1983-05-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-05-28 | 1986-11-27 | 1987-05-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-05-28 | 1990-11-27 | 1991-05-29 | $7700.00 | Window Closed / Lapsed |