Piezoelectric crystalline films and method of preparing the same
Assignee: Murata Manufacturing Co Ltd
•
Filing: 1978-02-02
•
Granted: 1979-05-22
•
Expires: 1998-02-02
Abstract
Abstract Piezoelectric crystalline films which consist essentially of a crystalline zinc oxide film with a c-axis perpendicular to a substrate surface, containing 0.01 to 20.0 atomic percent of vanadium. These films are prepared by radio-frequency sputtering.
Inventors
- 👤 Toshio Ogawa
- 👤 Tasuku Mashio
- 👤 Hiroshi Nishiyama
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 19:12
CPC Classifications
H; H10; H10N; H10N30/00; H10N30/01; H10N30/07; H10N30/074; H10N30/076; H10N30/80; H10N30/85; H10N30/853
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
51 words
A piezoelectric crystalline film having a smooth surface and disposed on a substrate, consisting essentially of a crystalline zinc oxide film with a hexagonal crystal structure and a c-axis substantially perpendicular to the substrate surface, characterized in that said crystalline zinc oxide film contains 0.01 to 20.0 atomic percent of vanadium.
Claim 2
Dependent Claim
51 words
A piezoelectric crystalline film having a smooth surface and disposed on a substrate, consisting essentially of a crystalline zinc oxide film with a hexagonal crystal structure and a c-axis substantially perpendicular to the substrate surface, characterized in that said crystalline zinc oxide film contains 0.01 to 20.0 atomic percent of vanadium.
Claim 3
Dependent Claim
20 words
The piezoelectric crystalline film of claim 1, wherein the substrate is selected from the group consisting of metal and glass.
Claim 4
Independent Claim
151 words
A method for making piezoelectric crystalline films having a smooth surface comprising simultaneously sputtering zinc oxide and vanadium from a film material source onto a metal or glass substrate to form a crystalline zinc oxide film with a hexagonal crystal structure and a c-axis substantially perpendicular to the substrate surface containing 0.01 to 20.0 atomic percent of vanadium, wherein said sputtering is effected by radio-frequency sputtering in an atmosphere of argon, or oxygen, or a mixture of argon and oxygen under a pressure of 1× 10 -1 to 1× 10 -3 Torr, and wherein said film material source consists essentially of ceramics of zinc oxide containing 0.01 to 20.0 atomic percent of vanadium, said substrate being positioned on an anode placed in parallel with a cathode on which said film material source is positioned, said film material source being supplied with an electric power of 2 to 8 w/cm 2 .
Claim 5
Independent Claim
151 words
A method for making piezoelectric crystalline films having a smooth surface comprising simultaneously sputtering zinc oxide and vanadium from a film material source onto a metal or glass substrate to form a crystalline zinc oxide film with a hexagonal crystal structure and a c-axis substantially perpendicular to the substrate surface containing 0.01 to 20.0 atomic percent of vanadium, wherein said sputtering is effected by radio-frequency sputtering in an atmosphere of argon, or oxygen, or a mixture of argon and oxygen under a pressure of 1× 10 -1 to 1× 10 -3 Torr, and wherein said film material source consists essentially of ceramics of zinc oxide containing 0.01 to 20.0 atomic percent of vanadium, said substrate being positioned on an anode placed in parallel with a cathode on which said film material source is positioned, said film material source being supplied with an electric power of 2 to 8 w/cm 2 .
Claim 6
Dependent Claim
26 words
The method for making piezoelectric crystalline films according to claim 3, wherein the substrate is heated to a temperature of 200° to 500° C. during sputtering.
References Cited (Backward Citations)
US3766041A
Cited
US3988232A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-05-21 | 1982-11-20 | 1983-05-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-05-21 | 1986-11-20 | 1987-05-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-05-21 | 1990-11-20 | 1991-05-22 | $7700.00 | Window Closed / Lapsed |