Water-soluble films from polyvinyl alcohol compositions
Assignee: EIDP Inc
•
Filing: 1978-08-11
•
Granted: 1979-05-22
•
Expires: 1998-08-11
Abstract
Abstract Films prepared by melt extrusion or aqueous casting from compositions consisting essentially of a (i) resin mixture containing a low molecular weight polyvinyl alcohol and a medium molecular weight polyvinyl alcohol, and optionally, a copolymer of vinyl alcohol and an ethylenically unsaturated ester and (ii) as a plasticizer a polyethylene glycol. The films are suitable for use as packaging film in automatic packaging equipment. They can be used to package pulverulent materials, and the film package containing the pulverulent material can be charged directly to water in which the film will dissolve, thus eliminating the problem of user contact and exact measuring of the package contents, as well as disposal of containers in which the pulverulent materials would otherwise be packaged. Moreover, the films provide enhanced resistance to breakage of packages made therefrom when such packages are handled or shipped, even under cold or dry conditions.
Inventors
- 👤 Robert D. Wysong
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 01:00
CPC Classifications
C; C11; C11D; C11D17/00; C11D17/04; C11D17/041; C11D17/042; C11D17/044; C08; C08L; C08L29/00; C08L29/02; C08L29/04
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
204 words
Cold water-soluble films having a thickness in the range between 0.5 and 10 mils and made from a polymeric composition consisting essentially of (i) a resin mixture consisting essentially of 40 to 55 parts by weight of a low molecular weight polyvinyl alcohol containing acyl groups having 1 to 4 carbon atoms, and having a viscosity in the range between 3 and 10 cps and a degree of hydrolysis in the range between 85 and 90 mol percent; 25 to 60 parts by weight of a medium molecular weight polyvinyl alcohol containing acyl groups having 1 to 4 carbon atoms, and having a viscosity in the range between 10 and 35 cps and a degree of hydrolysis in the range between 85 and 90 mol percent; and 0 to 20 parts by weight of a copolymer made up of 90 to 98 weight percent polymerized vinyl alcohol units and 10 to 2 weight percent of polymerized ester units which in monomeric form have the formula: ##STR5## wherein A is H or --CH 3 ; A' is H or --COO Alkyl; R is H, ##STR6## provided that when R is ##STR7## both A and A' are H; R' is H or --CH 3 ; and
Claim 2
Dependent Claim
204 words
Cold water-soluble films having a thickness in the range between 0.5 and 10 mils and made from a polymeric composition consisting essentially of (i) a resin mixture consisting essentially of 40 to 55 parts by weight of a low molecular weight polyvinyl alcohol containing acyl groups having 1 to 4 carbon atoms, and having a viscosity in the range between 3 and 10 cps and a degree of hydrolysis in the range between 85 and 90 mol percent; 25 to 60 parts by weight of a medium molecular weight polyvinyl alcohol containing acyl groups having 1 to 4 carbon atoms, and having a viscosity in the range between 10 and 35 cps and a degree of hydrolysis in the range between 85 and 90 mol percent; and 0 to 20 parts by weight of a copolymer made up of 90 to 98 weight percent polymerized vinyl alcohol units and 10 to 2 weight percent of polymerized ester units which in monomeric form have the formula: ##STR5## wherein A is H or --CH 3 ; A' is H or --COO Alkyl; R is H, ##STR6## provided that when R is ##STR7## both A and A' are H; R' is H or --CH 3 ; and
Claim 3
Dependent Claim
100 words
Alkyl contains 1 to 4 carbon; which copolymer has a viscosity in the range between 10 and 60 cps and a degree of hydrolysis in the range between 95 and 100 mol percent; and (ii) as a plasticizer, 10 to 30 parts by weight of a polyethylene glycol per 100 parts by weight of said resin mixture, said polyethylene glycol having an average molecular weight in the range between 285 and 420; for each of said polymers, the viscosity being determined by the Hoeppler Falling Ball Method ASTM-D 1343-56, Part 8 and the degree of hydrolysis being determined by saponification.
Claim 4
Dependent Claim
100 words
Alkyl contains 1 to 4 carbon; which copolymer has a viscosity in the range between 10 and 60 cps and a degree of hydrolysis in the range between 95 and 100 mol percent; and (ii) as a plasticizer, 10 to 30 parts by weight of a polyethylene glycol per 100 parts by weight of said resin mixture, said polyethylene glycol having an average molecular weight in the range between 285 and 420; for each of said polymers, the viscosity being determined by the Hoeppler Falling Ball Method ASTM-D 1343-56, Part 8 and the degree of hydrolysis being determined by saponification.
Claim 5
Dependent Claim
21 words
The film of claim 1 wherein said polyethylene glycol has an average molecular weight in the range between 380 and 420.
Claim 6
Dependent Claim
48 words
The film of claim 1 wherein said resin mixture consists essentially of 40 to 55 parts by weight of said low molecular weight polyvinyl alcohol, 25 to 50 parts by weight of said medium molecular weight polyvinyl alcohol, and 10 to 20 parts by weight of said copolymer.
Claim 7
Dependent Claim
33 words
The film of claim 3 wherein said plasticizer is present in an amount in the range between 15 and 25 parts by weight thereof per 100 parts by weight of said resin mixture.
Claim 8
Dependent Claim
21 words
The film of claim 4 wherein said polyethylene glycol has an average molecular weight in the range between 380 and 420.
Claim 9
Dependent Claim
48 words
The film of claim 1 wherein said resin mixture consists essentially of 40 to 50 parts by weight of said low molecular weight polyvinyl alcohol, 30 to 45 parts by weight of said medium molecular weight polyvinyl alcohol, and 15 to 20 parts by weight of said copolymer.
Claim 10
Dependent Claim
21 words
The film of claim 6 wherein said polyethylene glycol has an average molecular weight in the range between 380 and 420.
Claim 11
Dependent Claim
35 words
The film of claim 6 wherein said plasticizer is present in an amount in the range between 20 and 25 parts by weight thereof per 100 parts by weight of said vinyl alcohol polymer component.
Claim 12
Dependent Claim
21 words
The film of claim 8 wherein said polyethylene glycol has an average molecular weight in the range between 380 and 420.
Claim 13
Dependent Claim
41 words
The film of claim 1 containing 5 parts or less by weight of an adjuvant per 100 parts by weight of said vinyl alcohol polymer component; said adjuvant being selected from antioxidants, release agents, antiblock agents, surfactants, dispersants, and slip agents.
References Cited (Backward Citations)
FR1201957A
Cited
US2948697A
Cited
US3157611A
Cited
US3365413A
Cited
US3374195A
Cited
US3510542A
Cited
US3607812A
Cited
GB1330745A
Cited
US3882196A
Cited
US3997489A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-05-21 | 1982-11-20 | 1983-05-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-05-21 | 1986-11-20 | 1987-05-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-05-21 | 1990-11-20 | 1991-05-22 | $7700.00 | Window Closed / Lapsed |