Method of electroplating and treating electroplated ferrous based wire
Assignee: Goodyear Tire and Rubber Co
•
Filing: 1978-09-29
•
Granted: 1979-05-22
•
Expires: 1998-09-29
Abstract
Abstract Method of treating ferrous based wire comprised of (A) electroplating a negatively charged ferrous based wire in a prescribed aqueous electrolyte solution containing a positively charged stationary anode and, in combination, simultaneously, in the same electrolyte solution, (B) deplating a similarly electroplated ferrous based wire by passing said plated wire as a supplemental, additional, positively charged, moving anode through said solution to effect a removal of its electroplated outer metal coating.
Inventors
- 👤 Karol Marencak
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 20:32
CPC Classifications
C; C25; C25D; C25D7/00; C25D7/06; C25D7/0607; C25F; C25F5/00
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
135 words
A method of treating a ferrous based wire which comprises (A) electroplating an outer metal coating onto a ferrous based wire by continuously passing said wire, as a negatively charged cathode, through at least one aqueous electrolyte solution having a basic pH in the range of about 9 to about 14, containing a positively charged, stationary anode immersed therein and containing a water soluble salt of the electroplating metal, to effect the plating of said metal onto said ferrous based wire as an outer layer and in combination, simultaneously, and in the same electrolyte solution, (B) deplating a similarly electroplated ferrous based wire by continuously passing said plated wire as a supplemental, additional, positively charged anode, through said electrolyte solution to effect a removal of said electroplated outer metal coating from the base metal wire.
Claim 2
Independent Claim
135 words
A method of treating a ferrous based wire which comprises (A) electroplating an outer metal coating onto a ferrous based wire by continuously passing said wire, as a negatively charged cathode, through at least one aqueous electrolyte solution having a basic pH in the range of about 9 to about 14, containing a positively charged, stationary anode immersed therein and containing a water soluble salt of the electroplating metal, to effect the plating of said metal onto said ferrous based wire as an outer layer and in combination, simultaneously, and in the same electrolyte solution, (B) deplating a similarly electroplated ferrous based wire by continuously passing said plated wire as a supplemental, additional, positively charged anode, through said electrolyte solution to effect a removal of said electroplated outer metal coating from the base metal wire.
Claim 3
Dependent Claim
72 words
The method of claim 1 where the aqueous electrolyte solution has a temperature in the range of about 35° C. to about 65° C., where said positively charged, stationary, immersed anode is comprised of the electroplating metal and where a cathodic current density, from the applied negative voltage to the wire being plated, is in the range of about 5 to about 30 amperes per square decimeter of immersed wire surface area.
Claim 4
Dependent Claim
55 words
The method of claim 2 as a method of treating a ferrous based wire where said immersed stationary anode is a metal selected from at least one of copper, zinc, tin, cadmium, silver, nickel, chrome or their alloy, and and where said electrolyte solution contains at least one corresponding water soluble salt of said metal.
Claim 5
Dependent Claim
84 words
The method of claim 2 as a method of treating steel wire where said anode is optionally comprised of at least one of copper, zinc, tin, nickel or their alloy and where said electrolyte solution contains at least one water soluble salt of copper, zinc, tin, nickel or mixture of said salts, in an amount of about 15 to about 150 grams per liter of said metal, and said salts corresponding to said metal or alloy of said anode if its is comprised thereof.
Claim 6
Dependent Claim
27 words
The method of claim 3 where said ferrous based wire is a steel wire having a diameter in the range of about 0.75 to about 1.4 millimeters.
Claim 7
Dependent Claim
100 words
The method of claim 3 or 4 as a method of treating steel wire which comprises (A) brass electroplating a traveling negatively charged steel wire in said aqueous electrolyte solution containing water soluble copper and zinc salts in a copper/zinc mole ratio in the range of about 2/l to about 1/1 in an amount of about 10 to about 50 grams of copper per liter, said solution having a stationary, positively charged anode immersed therein comprised of brass and (B) simultaneously and in the same solution debrassing a similarly brass electroplated steel wire as a supplemental, positively charged traveling anode.
Claim 8
Independent Claim
49 words
The method of claims 1 or 3 where the positive voltage applied to said stationary anode is higher or lower than the positive voltage applied to said traveling electroplated wire anode to optionally favorably enhance the plating of said traveling wire cathode or deplating of said traveling wire anode.
References Cited (Backward Citations)
US2424173A
Cited
US2725352A
Cited
US2686859A
Cited
US3178305A
Cited
US3394063A
Cited
US3471338A
Cited
US3959099A
Cited
US3988216A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-05-21 | 1982-11-20 | 1983-05-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-05-21 | 1986-11-20 | 1987-05-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-05-21 | 1990-11-20 | 1991-05-22 | $7700.00 | Window Closed / Lapsed |