Assignee: General Electric Co
•
Filing: 1978-02-21
•
Granted: 1979-05-22
•
Expires: 1998-02-21
Abstract
Abstract The leakage current in metal oxide varistor bodies is found to vary as a function of applied pressure in the 0.5 kbar to 10 kbar range. A pressure sensing device is conditioned by first prestressing a metal oxide varistor to a pressure above the range of measurement and then releasing the prestress pressure. Upon application of subsequent pressures equal or less than the prestress pressure, the leakage current in the device is found to vary as a function of pressure.
Inventors
- 👤 Joe Wong
- 👤 Francis P. Bundy
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 12:29
CPC Classifications
H; H01; H01C; H01C10/00; H01C10/10
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
61 words
An electrical pressure sensor for continuously measuring pressure in a predefined range between approximately 0.5 kbar and approximately 10 kbar comprising a body of metal oxide varistor material, including a sintered mixture of zinc oxide with other metal oxides, which has been processed by first prestressing said body to a pressure above said predefined range and subsequently relieving said prestressing pressure.
Claim 2
Dependent Claim
61 words
An electrical pressure sensor for continuously measuring pressure in a predefined range between approximately 0.5 kbar and approximately 10 kbar comprising a body of metal oxide varistor material, including a sintered mixture of zinc oxide with other metal oxides, which has been processed by first prestressing said body to a pressure above said predefined range and subsequently relieving said prestressing pressure.
Claim 3
Dependent Claim
50 words
The sensor of claim 1 wherein said varistor comprises a reaction product formed by sintering a mixture consisting essentially of approximately 97 mol percent ZnO, 1/2 mol percent Bi 2 O 3 with Co 3 O 4 , MnO 2 , Sb 2 O 3 , and SnO 2 .
Claim 4
Dependent Claim
45 words
The sensor of claim 1 wherein said varistor comprises a reaction product formed by sintering a mixture consisting essentially of approximately 98 mol percent ZnO, 1/2 mol percent Bi 2 O 3 with Co 3 O 4 , MnO 2 , and TiO 2 .
Claim 5
Independent Claim
111 words
A method for determining an unknown pressure previously applied to a sintered metal oxide varistor body having a given composition, said unknown pressure being in the range from approximately 0.5 kbar to approximately 10 kbar comprising the steps of: determining as a function of known applied pressure the leakage current in sample metal oxide varistor bodies having the same composition as said body, said leakage current being measured at atmospheric pressure after said sample bodies have been subjected to and relieved from said known applied pressure; applying and thereafter removing said unknown pressure from said body; and subsequently determining said unknown pressure by measuring the leakage current through said varistor body.
Claim 6
Independent Claim
111 words
A method for determining an unknown pressure previously applied to a sintered metal oxide varistor body having a given composition, said unknown pressure being in the range from approximately 0.5 kbar to approximately 10 kbar comprising the steps of: determining as a function of known applied pressure the leakage current in sample metal oxide varistor bodies having the same composition as said body, said leakage current being measured at atmospheric pressure after said sample bodies have been subjected to and relieved from said known applied pressure; applying and thereafter removing said unknown pressure from said body; and subsequently determining said unknown pressure by measuring the leakage current through said varistor body.
Claim 7
Dependent Claim
40 words
The method of claim 4 wherein said varistor comprises from approximately 97 mol percent to approximately 98 mol percent ZnO, approximately 1/2 mol percent Bi 2 O 3 with Co 3 O 4 , MnO 2 and other metal oxides.
Claim 8
Independent Claim
68 words
A method for continuously measuring un unknown pressure in the range from approximately 0.5 kbar to approximately 10 kbar comprising: applying said unknown pressure to a body of metal oxide varistor material which has been prestressed to a pressure above said predefined range, said prestressing pressure subsequently having been removed, and concurrent with the application of said later applied unknown pressure, measuring electrical leakage current in said material.
Claim 9
Independent Claim
68 words
A method for continuously measuring un unknown pressure in the range from approximately 0.5 kbar to approximately 10 kbar comprising: applying said unknown pressure to a body of metal oxide varistor material which has been prestressed to a pressure above said predefined range, said prestressing pressure subsequently having been removed, and concurrent with the application of said later applied unknown pressure, measuring electrical leakage current in said material.
References Cited (Backward Citations)
US3682841A
Cited
US3790870A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-05-21 | 1982-11-20 | 1983-05-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-05-21 | 1986-11-20 | 1987-05-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-05-21 | 1990-11-20 | 1991-05-22 | $7700.00 | Window Closed / Lapsed |