Method for forming intermetallic layers in thin films for improved electromigration resistance
Assignee: International Business Machines Corp
•
Filing: 1977-02-04
•
Granted: 1979-05-15
•
Expires: 1997-02-04
Abstract
Abstract A method for forming narrow intermetallic stripes which will carry high currents on bodies such as semiconductors, integrated circuits, magnetic bubbles structures, etc. The conductive stripe includes aluminum or aluminum copper with at least one transition metal. The aluminum and at least one transition metal are deposited onto a supporting body at a very low pressure in a substantially oxygen-free high vacuum. The composite is then annealed at a temperature between about 200 DEG C. and 525 DEG C. for a time sufficient to form an aluminum and transition metal compound within the aluminum. The conductive stripes are then formed by masking and removing portions of the annealed metallic material. The resulting conductive stripes, which may be of a width of about 6x10-4 inches or less, have a significantly improved electromigration performance without significantly increasing resistance in the conductive stripe.
Inventors
- 👤 James K. Howard
- 👤 Paul S. Ho
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 11:40
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/06; C23C14/14; C23C14/16; C23C14/58; C23C14/5806; C23C14/5893; H; H01; H01B; H01B1/00; H01B1/02; H01B1/023; H01F; H01F10/00; H01F10/06; H10; H10P; H10P14/00; H10P14/40; H10P14/412; H10W; H10W20/00; H10W20/40; H10W20/41; H10W20/425; H10W20/44; H10W20/4403; H10W20/4405; H10W20/4407; H10W20/45; H10W20/48; Y; Y10; Y10S; Y10S148/00; Y10S148/02; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49117; Y10T29/49121; Y10T29/49204; Y10T428/00; Y10T428/12; Y10T428/12486
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
118 words
A method for forming narrow intermetallic conductive stripes on the surface of a body, comprising: co-depositing aluminum and at least one transition metal over said body within an enclosure having a pressure of less than about 1×10 -15 torr in a substantially oxygenfree vacuum; annealing the structure at a temperature between about 200° C. and 525° C. for time sufficient to form at least one region of aluminum and transition metal compound; the amount of said transition metal is chosen so that the proportion of said aluminum and transition metal compound is between 2 and 25 percent by weight of the said stripes; and forming said conductive stripes by masking and removing portions of the annealed metallic material.
Claim 2
Independent Claim
118 words
A method for forming narrow intermetallic conductive stripes on the surface of a body, comprising: co-depositing aluminum and at least one transition metal over said body within an enclosure having a pressure of less than about 1×10 -15 torr in a substantially oxygenfree vacuum; annealing the structure at a temperature between about 200° C. and 525° C. for time sufficient to form at least one region of aluminum and transition metal compound; the amount of said transition metal is chosen so that the proportion of said aluminum and transition metal compound is between 2 and 25 percent by weight of the said stripes; and forming said conductive stripes by masking and removing portions of the annealed metallic material.
Claim 3
Dependent Claim
20 words
The method of claim 1 wherein said body is a magnetic material which is capable of forming magnetic bubbles therein.
Claim 4
Dependent Claim
17 words
The method of claim 1 wherein said body is a semiconductor material which contains semiconductor devices therein.
Claim 5
Dependent Claim
22 words
The method of claim 1 wherein the transition metal is chromium; and the annealing temperature is between about 250 and 525° C.
Claim 6
Dependent Claim
22 words
The method of claim 1 wherein the transition metal is hafnium; and the annealing temperature is between about 350° and 525° C.
Claim 7
Dependent Claim
22 words
The method of claim 1 wherein the entire thickness of said conductive stripe was co-deposited aluminum and at least one transition metal.
Claim 8
Dependent Claim
31 words
The method of claim 1 wherein a portion of the entire thickness of said conductive stripe was co-deposited aluminum and at least one transition metal and the remaining portion is aluminum.
Claim 9
Dependent Claim
23 words
The method of either claim 6 wherein the said co-deposition was by simultaneously evaporating said aluminum and said at least one transition metal.
Claim 10
Dependent Claim
22 words
The method of claim 7 wherein said co-deposited portion is a stoichiometric ratio between aluminum and said at least one transition metal.
Claim 11
Dependent Claim
15 words
The method of claim 1 wherein copper is co-deposited with said aluminum and transition metal.
Claim 12
Dependent Claim
23 words
The method of claim 1 wherein said narrow conductive stripes each have a minimum physical dimension of less than about 6×10 -4 inch.
Claim 13
Dependent Claim
30 words
The method of claim 1 wherein the said co-deposition is accomplished at a rate between about 0.02 to 60 Angstroms per second so as to produce a fine grain structure.
Claim 14
Dependent Claim
19 words
The method of claim 1 wherein the said conductive stripe is supported upon a material which is an insulator.
References Cited (Backward Citations)
US3343254A
Cited
US3725309A
Cited
US3830657A
Cited
US3743894A
Cited
US3858304A
Cited
US4042954A
Cited
US4035526A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-05-14 | 1982-11-13 | 1983-05-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-05-14 | 1986-11-13 | 1987-05-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-05-14 | 1990-11-13 | 1991-05-15 | $7700.00 | Window Closed / Lapsed |