US4154714A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Adhesive repellent coatings and substrates coated therewith
Assignee: Wacker Chemie AG
•
Filing: 1978-01-26
•
Granted: 1979-05-15
•
Expires: 1998-01-26
Abstract
Abstract Coating compositions which impart adhesive repellent or non-adherent properties to substrates coated therewith comprising (1) vinyl endblocked diorganopolysiloxanes having an average viscosity in excess of 10 6 cP at 25° C. in which from 3 to 39 mole percent of the nonterminal siloxane units are diphenylsiloxane units and at least 50 mole percent of the remaining organic radicals on the siloxane units are methyl radicals, (2) organopolysiloxanes having at least 3 Si-bonded hydrogen atoms per molecule, (3) catalysts which promote the addition of Si-bonded hydrogen atoms to the vinyl groups and (4) an inert organic solvent. These coating compositions may be applied to cellulosic materials and other substrates to impart varying degrees of adhesive repellency thereto.
Inventors
- 👤 Friedrich Hockemeyer
- 👤 Wolfgang Hechtl
- 👤 Heinrich Marwitz
- 👤 Paul Hittmair
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 16:12
CPC Classifications
B; B05; B05D; B05D5/00; B05D5/08; C; C08; C08L; C08L83/00; C08L83/04; C09; C09D; C09D183/00; C09D183/04; D; D21; D21H; D21H17/00; D21H17/20; D21H17/33; D21H17/46; D21H17/59; D21H19/00; D21H19/10; D21H19/14; D21H19/24; D21H19/32; C08G; C08G77/00; C08G77/04; C08G77/12; C08G77/20; C08G77/70; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31652; Y10T428/31663
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
118 words
A coating composition which may be applied to substrates to impart adhesive repellent properties thereto which consisting essentially of (1) diorganopolysiloxanes having terminal Si-bonded vinyl groups in which 3 to 30 mole percent of the nonterminal siloxane units are diphenylsiloxane units and at least 50 mole percent of the remaining organic radicals on the siloxane units are methyl radicals, said diorganopolysiloxanes (1) having an mkp value of from 300 to 800 as determined in a Brabender Plastograph at 25° C. and at 60 revolutions per minute; (2) organopolysiloxanes having at least 3 Si-bonded hydrogen atoms per molecule; (3) a catalyst which promotes the addition of Si-bonded hydrogen atoms to the vinyl groups and (4) an inert organic solvent.
Claim 2
Dependent Claim
118 words
A coating composition which may be applied to substrates to impart adhesive repellent properties thereto which consisting essentially of (1) diorganopolysiloxanes having terminal Si-bonded vinyl groups in which 3 to 30 mole percent of the nonterminal siloxane units are diphenylsiloxane units and at least 50 mole percent of the remaining organic radicals on the siloxane units are methyl radicals, said diorganopolysiloxanes (1) having an mkp value of from 300 to 800 as determined in a Brabender Plastograph at 25° C. and at 60 revolutions per minute; (2) organopolysiloxanes having at least 3 Si-bonded hydrogen atoms per molecule; (3) a catalyst which promotes the addition of Si-bonded hydrogen atoms to the vinyl groups and (4) an inert organic solvent.
Claim 3
Dependent Claim
33 words
The composition of claim 1, wherein the diorganopolysiloxanes (1) have an mkp value of from 360 to 730 as determined by a Brabender Plastograph at 25° C. and at 60 revolutions per minute.
Claim 4
Dependent Claim
106 words
The composition of claim 1 wherein the diorganopolysiloxanes (1) have the general formula (CH.sub.2 ═RH)R.sub.2 SiO[(C.sub.6 H.sub.5).sub.2 SiO].sub.m (R.sub.2 SiO).sub.n SiR.sub.2 (CH═CH.sub.2) wherein R is selected from the group consisting of monovalent hydrocarbon radicals and substituted monovalent hydrocarbon radicals, in which at least 50 mole percent of the R radicals are methyl radicals, m and n each represent a number whose sum results in the diorganopolysiloxanes (1) having an mkp value of from 300 to 800 as determined by a Brabender Plastograph at 25° C. and at 60 revolutions per minute and furthermore m is from 3 to 30 mole percent of the sum of m+n.
Claim 5
Dependent Claim
25 words
The composition of claim 1 wherein the nonterminal diphenylsiloxane units are present in the diorganopolysiloxanes in an amount of from 5 to 20 mole percent.
Claim 6
Dependent Claim
27 words
The composition of claim 1 wherein at least 70 mole percent of the organic radicals on the remaining siloxane units of the diorganopolysiloxanes (1) are methyl radicals.
Claim 7
Dependent Claim
21 words
The composition of claim 1 wherein the organopolysiloxanes (2) have a viscosity of from 30 to 80 cP at 25° C.
Claim 8
Dependent Claim
70 words
The composition of claim 1 wherein the organopolysiloxanes (2) have the general formula ##STR2## wherein R' is selected from the group consisting of hydrogen, lower alkyl radicals and aryl radicals, in which the amount of silicon bonded hydrogen atoms ranges from 0.10 to 1.66 percent by weight, except that only one hydrogen atom is bonded to any one silicon atom and p is a number of from 20 to 500.
Claim 9
Dependent Claim
36 words
The composition of claim 1 wherein the siloxane units having one Si-bonded hydrocarbon radical to siloxane units having two Si-bonded hydrocarbon radicals in the organopolysiloxanes (2) are in a mole ratio of from 10:0 to 1:10.
Claim 10
Dependent Claim
30 words
The composition of claim 1 wherein the organopolysiloxanes (2) are present in an amount of from 1 to 20 percent by weight based on the weight of the diorganopolysiloxanes (1).
Claim 11
Dependent Claim
11 words
The composition of claim 1 wherein the catalyst (3) contains platinum.
Claim 12
Dependent Claim
33 words
The composition of claim 10 wherein the catalyst (3) is present in an amount of from 0.001 to 0.1 percent by weight of elemental platinum based on the weight of the diorganopolysiloxanes (1).
Claim 13
Dependent Claim
30 words
The composition of claim 1 wherein the organic solvent is present in an amount of from 200 to 5000 percent by weight based on the weight of the diorganopolysiloxanes (1).
Claim 14
Dependent Claim
130 words
A process for preparing a coating composition which may be applied to substrates to impart adhesive repellent properties thereto which comprises dissolving in an organic solvent diorganopolysiloxanes (1) having terminal Si-bonded vinyl groups in which 3 to 30 mole percent of the nonterminal siloxane units are diphenylsiloxane units and at least 50 mole percent of the remaining organic radicals on the siloxane units are methyl radicals, said diorganopolysiloxanes (1) having an mkp value of from 300 to 800 as determined in a Brabender Plastograph at 25° C. and at 60 revolutions per minute and a catalyst (3) capable of promoting the addition of Si-bonded hydrogen atoms to vinyl groups to form a solution and thereafter adding organopolysiloxanes (2) having at least 3 Si-bonded hydrogen atoms per molecule to the solution.
Claim 15
Dependent Claim
130 words
A process for preparing a coating composition which may be applied to substrates to impart adhesive repellent properties thereto which comprises dissolving in an organic solvent diorganopolysiloxanes (1) having terminal Si-bonded vinyl groups in which 3 to 30 mole percent of the nonterminal siloxane units are diphenylsiloxane units and at least 50 mole percent of the remaining organic radicals on the siloxane units are methyl radicals, said diorganopolysiloxanes (1) having an mkp value of from 300 to 800 as determined in a Brabender Plastograph at 25° C. and at 60 revolutions per minute and a catalyst (3) capable of promoting the addition of Si-bonded hydrogen atoms to vinyl groups to form a solution and thereafter adding organopolysiloxanes (2) having at least 3 Si-bonded hydrogen atoms per molecule to the solution.
Claim 16
Dependent Claim
33 words
The process of claim 13 wherein the diorganopolysiloxanes (1) have an mkp value of from 360 to 730 as determined by a Brabender Plastograph at 25° C. and at 60 revolutions per minute.
Claim 17
Dependent Claim
106 words
The process of claim 13 wherein the diorganopolysiloxanes (1) have the general formula (CH.sub.2 ═RH)R.sub.2 SiO[(C.sub.6 H.sub.5).sub.2 SiO].sub.m (R.sub.2 SiO).sub.n SiR.sub.2 (CH═CH.sub.2) wherein R is selected from the group consisting of monovalent hydrocarbon radicals and substituted monovalent hydrocarbon radicals, in which at least 50 mole percent of the R radicals are methyl radicals, m and n each represent a number whose sum results in the diorganopolysiloxanes (1) having an mkp value of from 300 to 800 as determined by a Brabender Plastograph at 25° C. and at 60 revolutions per minute and furthermore m is from 3 to 30 mole percent of the sum of m+n.
Claim 18
Dependent Claim
25 words
The process of claim 13 wherein the nonterminal diphenylsiloxane units are present in the diorganopolysiloxanes in an amount of from 5 to 20 mole percent.
Claim 19
Dependent Claim
27 words
The process of claim 13 wherein at least 70 mole percent of the organic radicals on the remaining siloxane units of the diorganopolysiloxanes (1) are methyl radicals.
Claim 20
Dependent Claim
30 words
The process of claim 13 wherein the organopolysiloxanes (2) are present in an amount of from 1 to 20 percent by weight based on the weight of the diorganopolysiloxanes (1).
Claim 21
Dependent Claim
11 words
The process of claim 13 wherein the catalyst (3) contains platinum.
Claim 22
Dependent Claim
30 words
The process of claim 13 wherein the organic solvent is present in an amount of from 200 to 5000 percent by weight based on the weight of the diorganopolysiloxanes (1).
Claim 23
Dependent Claim
30 words
The process of claim 15 wherein the organopolysiloxanes (2) are present in an amount of from 1 to 20 percent by weight based on the weight of the diorganopolysiloxanes (1).
Claim 24
Dependent Claim
11 words
The process of claim 15 wherein the catalyst (3) contains platinum.
Claim 25
Dependent Claim
30 words
The process of claim 15 wherein the organic solvent is present in an amount of from 200 to 5000 percent by weight based on the weight of the diorganopolysiloxanes (1).
References Cited (Backward Citations)
US3814731A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-05-14 | 1982-11-13 | 1983-05-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-05-14 | 1986-11-13 | 1987-05-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-05-14 | 1990-11-13 | 1991-05-15 | $7700.00 | Window Closed / Lapsed |