Abstract
Abstract Metal alloy filaments having improved surface characteristics and enhanced mechanical properties are extracted from a source of molten metal alloy using a quenching wheel in a partial vacuum.
Inventors
- 👤 Ranjan Ray
- 👤 Carl F. Cline
- 👤 Donald E. Polk
- 👤 Lance A. Davis
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 12:29
CPC Classifications
B; B22; B22D; B22D11/00; B22D11/06; B22D11/0637; B22D11/0697; B22D11/005; C; C22; C22C; C22C45/00; C22C45/008
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
77 words
A process for forming an amorphous metal alloy filament comprising: (a) forming a melt of an alloy composition which, upon rapid quenching from the melt, forms an amorphous solid; and (b) depositing a stream of the molten metal alloy on a rapidly moving chill surface under partial vacuum with pressure not higher than about 5.5 cm. Hg. to quench the molten metal to form an amorphous metal alloy filament having reduced surface irregularities and improved tensile strength.
Claim 2
Dependent Claim
77 words
A process for forming an amorphous metal alloy filament comprising: (a) forming a melt of an alloy composition which, upon rapid quenching from the melt, forms an amorphous solid; and (b) depositing a stream of the molten metal alloy on a rapidly moving chill surface under partial vacuum with pressure not higher than about 5.5 cm. Hg. to quench the molten metal to form an amorphous metal alloy filament having reduced surface irregularities and improved tensile strength.
Claim 3
Dependent Claim
20 words
The process of claim 1 in which the absolute pressure ranges from about 100 μm to 1 cm of Hg.
Claim 4
Dependent Claim
26 words
The process of claim 1 in which the molten metal alloy is quenched at a rate of about 10 5 ° to 10 6 ° C./sec.
Claim 5
Dependent Claim
84 words
The process of claim 3 in which the metal alloy comprises T.sub.i X.sub.j where T is at least one transition metal selected from the group consisting of elements listed in Groups IB to VIIB and VIII of the Periodic Table, X is at least one of the elements selected from the group consisting of aluminum, antimony, beryllium, boron, germanium, carbon, indium, phosphorus, silicon and tin, "i" ranges from about 70 to 87 atom percent, and "j" ranges from about 13 to 30 atom percent.
Claim 6
Dependent Claim
66 words
The process of claim 4 in which T is at least one of the elements selected from the group consisting of vanadium, iron, cobalt, nickel and chromium, X is at least one of the elements selected from the group consisting of aluminum, boron, carbon, phosphorus and silicon, "i" ranges from about 75 to 85 atom percent and "j" ranges from about 15 to 25 atom percent.
References Cited (Backward Citations)
GB736310A
Cited
US3862658A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-05-14 | 1982-11-13 | 1983-05-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-05-14 | 1986-11-13 | 1987-05-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-05-14 | 1990-11-13 | 1991-05-15 | $7700.00 | Window Closed / Lapsed |