Process for producing a mixed-shrinkage heat-bulkable polyester yarn
Assignee: EIDP Inc
•
Filing: 1977-10-28
•
Granted: 1979-05-08
•
Expires: 1997-10-28
Abstract
Abstract The disclosure relates to cospinning and drawing polyester filaments to produce a composite yarn which develops bulk due to differential shrinkage of the filaments when heated. Filaments of ethylene terephthalate synthetic linear condensation polymer are melt spun to form two separate filament bundles, a water-based spring finish is applied to the filaments of one bundle and a substantially non-volatile spin finish is applied to filaments of the other filament bundle, the filament bundles are drawn under identical treatment conditions during passage along separate paths and the filaments are then combined and intermingled during passage around draw rolls. The product is a mixed-shrinkage yarn wherein the filaments treated with aqueous-based finish have a higher heat-shrinkage than the filaments treated with non-volatile finish, even though both are otherwise processed in the same manner.
Inventors
- 👤 Cecil E. Reese
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 10:50
CPC Classifications
D; D02; D02G; D02G1/00; D02G1/16; D02G1/164; D01; D01D; D01D5/00; D01D5/22; Y; Y10; Y10S; Y10S57/00; Y10S57/908
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
137 words
In the production of continuous-filament textile yarns by a continuous process wherein polyester filaments are melt-spun from spinneret orifices, quenched, converged into a filament bundle, and drawn with draw rolls to at least the natural draw ratio; the improvement for producing a mixed-shrinkage, heat-bulkable yarn which comprises melt-spinning filaments of ethylene terephthalate synthetic linear condensation polymer to form two filament bundles, applying a water-based spin finish to one filament bundle and applying a spin finish to the other filament bundle which contains less than 10 percent water and is substantially non-volatile at temperatures up to at least 130° C., drawing the separate bundles under identical treatment conditions during passage through a zone of dry heat, and then combining the drawn filament bundles before or on the draw rolls to intermingle the filaments and provide a mixed-shrinkage yarn.
Claim 2
Dependent Claim
137 words
In the production of continuous-filament textile yarns by a continuous process wherein polyester filaments are melt-spun from spinneret orifices, quenched, converged into a filament bundle, and drawn with draw rolls to at least the natural draw ratio; the improvement for producing a mixed-shrinkage, heat-bulkable yarn which comprises melt-spinning filaments of ethylene terephthalate synthetic linear condensation polymer to form two filament bundles, applying a water-based spin finish to one filament bundle and applying a spin finish to the other filament bundle which contains less than 10 percent water and is substantially non-volatile at temperatures up to at least 130° C., drawing the separate bundles under identical treatment conditions during passage through a zone of dry heat, and then combining the drawn filament bundles before or on the draw rolls to intermingle the filaments and provide a mixed-shrinkage yarn.
Claim 3
Dependent Claim
25 words
A process as defined in claim 1 wherein the filaments are spun from different orifices of the same spinneret to form the two filament bundles.
Claim 4
Dependent Claim
22 words
A process as defined in claim 1 wherein the separate bundles are drawn at a draw ratio of about 2X to 5X.
Claim 5
Dependent Claim
40 words
A process as defined in claim 1 wherein the separate bundles are drawn in jets of dry steam supplied with steam from a common source at 30 to 150 pounds per square inch gage pressure and 170° to 375° C.
Claim 6
Dependent Claim
23 words
A process as defined in claim 1 wherein the intermingled filaments are interlaced after the draw rolls by passage through an interlacing jet.
Claim 7
Dependent Claim
21 words
A process as defined in claim 1 wherein the filaments are spun from molten polyethylene terephthalate supplied from the same source.
Claim 8
Dependent Claim
24 words
A process as defined in claim 1 wherein the water-based spin finish comprises an aqueous emulsion of about 2 to 10 percent filament lubricants.
Claim 9
Dependent Claim
37 words
A process as defined in claim 1 wherein the substantially non-volatile spin finish comprises a solution or dispersion of filament lubricants in an organic liquid which is substantially non-volatile at temperatures up to at least 160° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-05-07 | 1982-11-06 | 1983-05-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-05-07 | 1986-11-06 | 1987-05-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-05-07 | 1990-11-06 | 1991-05-08 | $7700.00 | Window Closed / Lapsed |