Polymeric optical element having antireflecting surface
Assignee: 3M Co
•
Filing: 1978-05-03
•
Granted: 1979-05-08
•
Expires: 1998-05-03
Abstract
Abstract An optical element of polymeric material is provided with a microstructured surface, thereby rendering the surface substantially non-reflecting while maintaining a high degree of transmissivity. The element is formed via replication from a stamper prepared from a glass original having a similar microstructured surface which is formed by etching a cleaned surface of the glass in vapors of hydrofluoric acid followed by sputter etching with inert gas ions.
Inventors
- 👤 Kent N. Maffitt
- 👤 Hubert U. Brueckner
- 👤 Dean R. Lowrey
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 12:49
CPC Classifications
B; B29; B29D; B29D11/00; B29D11/00605; B29C; B29C37/00; B29C37/0053; B29C41/00; B29C41/02; B29C41/12; B29C59/00; B29C59/02; B29C59/022; C; C03; C03C; C03C23/00; G; G02; G02B; G02B1/00; G02B1/10; G02B1/11; G02B1/12; G02B3/00; G02B3/02; G02B3/08; B29C2059/023; B29K; B29K2995/00; B29K2995/0018; B29K2995/0026
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
218 words
A method of forming an antireflecting surface on a polymeric optical element, said method comprising the steps of: (a) providing a glass article having a uniform and homogeneous glass surface through which the transmission of visible light in a predetermined direction is at least 10 5 greater than the transmission measured 5° off the predetermined direction. (b) vapor etching the homogeneous glass surface by exposing said surface of vapors of an acid to etch into the surface a plurality of peaks, a predominant number of which range in amplitude between approximately 10 and 50 nm, the ratio of visible light transmission in a predetermined direction to that transmitted 5° off the predetermined direction being substantially unchanged, (c) sputter etching the acid etched surface with inert gas ions to remove approximately 200-300 nm of the glass surface and to increase the amplitude of the peaks such that a predominant number thereof range in amplitude between 20 and 160 nm, the separation of adjacent peaks being not greater than three times the maximum amplitude of said peaks, and (d) replicating the sputter etched surface into a surface of a polymeric material to form in the polymeric surface a replica of said plurality of peaks, whereby the total reflectance of visible light incident normal to said surface is less than 2%.
Claim 2
Independent Claim
218 words
A method of forming an antireflecting surface on a polymeric optical element, said method comprising the steps of: (a) providing a glass article having a uniform and homogeneous glass surface through which the transmission of visible light in a predetermined direction is at least 10 5 greater than the transmission measured 5° off the predetermined direction. (b) vapor etching the homogeneous glass surface by exposing said surface of vapors of an acid to etch into the surface a plurality of peaks, a predominant number of which range in amplitude between approximately 10 and 50 nm, the ratio of visible light transmission in a predetermined direction to that transmitted 5° off the predetermined direction being substantially unchanged, (c) sputter etching the acid etched surface with inert gas ions to remove approximately 200-300 nm of the glass surface and to increase the amplitude of the peaks such that a predominant number thereof range in amplitude between 20 and 160 nm, the separation of adjacent peaks being not greater than three times the maximum amplitude of said peaks, and (d) replicating the sputter etched surface into a surface of a polymeric material to form in the polymeric surface a replica of said plurality of peaks, whereby the total reflectance of visible light incident normal to said surface is less than 2%.
Claim 3
Dependent Claim
32 words
A method according to claim 1, wherein step (a) further comprises treating the glass article to remove a surface layer therefrom to provide a homogeneous glass surface substantially free from internal stress.
Claim 4
Dependent Claim
37 words
A method according to claim 1, wherein step (a) comprises washing the glass surface in a solution of detergent and distilled H 2 O, followed by a distilled H 2 O rinse and subsequent rinse in ethanol.
Claim 5
Dependent Claim
27 words
A method according to claim 1, wherein step (a) further comprises bombarding the glass surface with ions to sputter away an outer portion of the glass surface.
Claim 6
Dependent Claim
35 words
A method according to claim 4, wherein the glass surface is bombared with noble gas ions to promote preferential sputtering of oxygen atoms from the glass surface to result in a silicon rich glass surface.
Claim 7
Dependent Claim
28 words
A method according to claim 5, wherein the silicon rich glass surface is bombarded with reactive gas ions to control the extent of excess silicon on the surface.
Claim 8
Dependent Claim
52 words
A method according to claim 4, wherein the glass surface is bombarded with argon ions at a pressure of between 2-5 millitorr for a period ranging between 4 and 13 hours to remove as much as one micrometer of surface layer to ensure the presence of said uniform and homogeneous glass surface.
Claim 9
Dependent Claim
20 words
A method according to claim 1, wherein step (b) comprises exposing said glass surface to vapors of an inorganic acid.
Claim 10
Dependent Claim
56 words
A method according to claim 8, wherein step (b) comprises maintaining said glass surface at a temperature of approximately 20°-21° C. and exposing said glass surface to vapors of HF having a concentration ranging between 1% and 4% at a bath temperature between 13° and 15° C. for a period ranging between 16 and 30 hours.
Claim 11
Dependent Claim
25 words
A method according to claim 1, wherein step (c) comprises bombarding the etched glass surface with argon ions at a pressure ranging between 1-15 millitorr.
Claim 12
Dependent Claim
34 words
A method according to claim 10, wherein step (c) comprises bombarding the etched glass surface with argon ions at a pressure of approximately 5 millitorr for a period ranging between 0.5 and one hour.
Claim 13
Dependent Claim
59 words
A method according to claim 1, wherein step (d) comprises the steps of depositing a metal layer onto the sputter etched surface to form on an inner surface of said layer a replica of said plurality of peaks and removing the glass article from the layer to expose the replica of said plurality of peaks on the inner surface.
Claim 14
Dependent Claim
60 words
A method according to claim 12, wherein step (d) comprises evaporating a first metal layer onto the sputter etched surface to form a said replica of said plurality of peaks, preparing said replica for electroplating, and electroplating a second metal layer onto said replica to provide a thick body adapted for use as a stamper apart from the glass article.
Claim 15
Dependent Claim
73 words
A method according to claim 13, wherein step (d) comprises evaporating as the first metal layer a layer of chromium to provide a hard, wear-resistant replicated surface, evaporating a layer of nickel to promote adhesion of additional layers to the chromium layer, evaporating a copper layer onto the nickel layer to provide a high conductivity layer useful as an electroplating electrode, and electroplating nickel onto the copper layer to form said thick body.
References Cited (Backward Citations)
US2461840A
Cited
GB677784A
Cited
US2854337A
Cited
US2875543A
Cited
US3490982A
Cited
US3565978A
Cited
US3962495A
Cited
US4013465A
Cited
US4019884A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-05-07 | 1982-11-06 | 1983-05-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-05-07 | 1986-11-06 | 1987-05-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-05-07 | 1990-11-06 | 1991-05-08 | $7700.00 | Window Closed / Lapsed |