Metal neutralized sulfonated EPDM terpolymers and compositions thereof
Assignee: ExxonMobil Technology and Engineering Co
•
Filing: 1977-11-29
•
Granted: 1979-05-08
•
Expires: 1997-11-29
Abstract
Abstract This invention relates to plasticized metal neutralized sulfonated EPDM terpolymers having at least 65 wt. % of ethylene in the backbone of the EPDM terpolymer and extended compositions of these metal neutralized sulfonated EPDM terpolymers having 100 parts of a neutralized sulfonated EPDM terpolymer; less than about 100 parts per hundred of a non-polar process oil; less than about 300 parts per hundred of a filler; and a preferential plasticizer at about less than 60 parts per hundred based on 100 parts of the sulfonated elastomeric polymer. These compositions can be readily processed due to their superior rheological properties on conventional plastic fabrication equipment, especially on low pressure injection molding and extrusion equipment into elastomeric articles having improved physical properties.
Inventors
- 👤 Henry S. Makowski
- 👤 Robert R. Klein
- 👤 Robert D. Lundberg
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 20:11
CPC Classifications
C; C08; C08L; C08L23/00; C08L23/26; C08L23/32; Y; Y10; Y10S; Y10S260/00; Y10S260/31
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
132 words
An elastomeric composition which consists essentially of: (a) a metal neutralized sulfonated EPDM terpolymer having at least about 65 wt. % ethylene in the backbone of said metal neutralized sulfonated EPDM terpolymer, about 10 to about 60 meq. of metal sulfonate groups per 100 grams of said metal neutralized sulfonated EPDM terpolymer, a metal of said metal sulfonate groups being selected from the group consisting of aluminum, iron, antimony, mercury and Groups IA, IIA and IB of the Periodic Table of Elements and mixtures thereof; and (b) at least 8 parts by weight of a preferential plasticizer per 100 parts of said metal neutralized sulfonated EPDM terpolymer, said preferential plasticizer being selected from the group consisting of stearamides and zinc salts of carboxylic acids having about 12 to about 30 carbon atoms.
Claim 2
Dependent Claim
132 words
An elastomeric composition which consists essentially of: (a) a metal neutralized sulfonated EPDM terpolymer having at least about 65 wt. % ethylene in the backbone of said metal neutralized sulfonated EPDM terpolymer, about 10 to about 60 meq. of metal sulfonate groups per 100 grams of said metal neutralized sulfonated EPDM terpolymer, a metal of said metal sulfonate groups being selected from the group consisting of aluminum, iron, antimony, mercury and Groups IA, IIA and IB of the Periodic Table of Elements and mixtures thereof; and (b) at least 8 parts by weight of a preferential plasticizer per 100 parts of said metal neutralized sulfonated EPDM terpolymer, said preferential plasticizer being selected from the group consisting of stearamides and zinc salts of carboxylic acids having about 12 to about 30 carbon atoms.
Claim 3
Dependent Claim
13 words
A polymer according to claim 1, wherein said preferential plasticizer is zinc stearate.
Claim 4
Dependent Claim
12 words
A polymer according to claim 1, wherein said preferential plasticizer is stearamide.
Claim 5
Dependent Claim
155 words
An elastomeric composition which consists essentially of: (a) a metal neutralized sulfonated EPDM terpolymer having at least about 65 wt. % ethylene in the backbone of said metal neutralized sulfonated EPDM terpolymer, about 10 to about 60 meq. of metal sulfonate groups per 100 grams of said metal neutralized sulfonated EPDM terpolymer, a metal of said metal sulfonate groups being selected from the group consisting of aluminum, iron, antimony, mercury and Groups IA, IIA and IB of the Periodic Table of Elements and mixtures thereof; (b) at least 8 parts by weight of a preferential plasticizer per 100 parts of said metal neutralized sulfonated EPDM terpolymer, said preferential plasticizer being selected from the group consisting of stearamides and zinc salts of carboxylic acids having about 12 to about 30 carbon atoms; and (c) about 20 to about 100 parts by weight of a crystalline polyolefin per 100 parts of said metal neutralized sulfonated EPDM terpolymer.
Claim 6
Dependent Claim
155 words
An elastomeric composition which consists essentially of: (a) a metal neutralized sulfonated EPDM terpolymer having at least about 65 wt. % ethylene in the backbone of said metal neutralized sulfonated EPDM terpolymer, about 10 to about 60 meq. of metal sulfonate groups per 100 grams of said metal neutralized sulfonated EPDM terpolymer, a metal of said metal sulfonate groups being selected from the group consisting of aluminum, iron, antimony, mercury and Groups IA, IIA and IB of the Periodic Table of Elements and mixtures thereof; (b) at least 8 parts by weight of a preferential plasticizer per 100 parts of said metal neutralized sulfonated EPDM terpolymer, said preferential plasticizer being selected from the group consisting of stearamides and zinc salts of carboxylic acids having about 12 to about 30 carbon atoms; and (c) about 20 to about 100 parts by weight of a crystalline polyolefin per 100 parts of said metal neutralized sulfonated EPDM terpolymer.
Claim 7
Dependent Claim
13 words
A polymer according to claim 4, wherein said preferential plasticizer is zinc stearate.
Claim 8
Dependent Claim
215 words
An elastomeric composition which consists essentially of: (a) a metal neutralized sulfonated EPDM terpolymer having at least about 65 wt. % ethylene in the backbone of said metal neutralized sulfonated EPDM terpolymer, about 10 to about 60 meq. of metal sulfonate groups per 100 grams of said metal neutralized sulfonated EPDM terpolymer, a metal of said metal sulfonate groups being selected from the group consisting of aluminum, iron, antimony, mercury and Groups IA, IIA and IB of the Periodic Table of Elements and mixtures thereof; (b) at least 8 parts by weight of a preferential plasticizer per 100 parts of said metal neutralized sulfonated EPDM terpolymer, said preferential plasticizer being selected from the group consisting of stearamides and zinc salts of carboxylic acids having about 12 to about 30 carbon atoms; (c) about 50 to about 300 parts by weight of an inorganic filler per 100 parts of said metal neutralized sulfonated EPDM terpolymer, said inorganic filler being selected from the group consisting of clay, talc and calcium carbonate and mixtures thereof; and (d) about 50 to about 100 parts by weight of a non-polar process oil having less than about 2 wt. % polar type compounds, said non-polar process oil being selected from the group consisting of paraffinics, naphthenics and aromatics and mixtures thereof.
Claim 9
Dependent Claim
215 words
An elastomeric composition which consists essentially of: (a) a metal neutralized sulfonated EPDM terpolymer having at least about 65 wt. % ethylene in the backbone of said metal neutralized sulfonated EPDM terpolymer, about 10 to about 60 meq. of metal sulfonate groups per 100 grams of said metal neutralized sulfonated EPDM terpolymer, a metal of said metal sulfonate groups being selected from the group consisting of aluminum, iron, antimony, mercury and Groups IA, IIA and IB of the Periodic Table of Elements and mixtures thereof; (b) at least 8 parts by weight of a preferential plasticizer per 100 parts of said metal neutralized sulfonated EPDM terpolymer, said preferential plasticizer being selected from the group consisting of stearamides and zinc salts of carboxylic acids having about 12 to about 30 carbon atoms; (c) about 50 to about 300 parts by weight of an inorganic filler per 100 parts of said metal neutralized sulfonated EPDM terpolymer, said inorganic filler being selected from the group consisting of clay, talc and calcium carbonate and mixtures thereof; and (d) about 50 to about 100 parts by weight of a non-polar process oil having less than about 2 wt. % polar type compounds, said non-polar process oil being selected from the group consisting of paraffinics, naphthenics and aromatics and mixtures thereof.
Claim 10
Dependent Claim
13 words
A polymer according to claim 6, wherein said preferential plasticizer is zinc stearate.
Claim 11
Dependent Claim
148 words
A polymeric formed article formed by a low pressure injection molding process which comprises essentially of an elastomeric composition which consists essentially of: (a) a metal neutralized sulfonated EPDM terpolymer having at least about 65 wt. % ethylene in the backbone of said metal neutralized sulfonated EPDM terpolymer, about 10 to about 60 meq. of metal sulfonate groups per 100 grams of said metal neutralized sulfonated EPDM terpolymer, a metal of said metal sulfonate groups being selected from the group consisting of aluminum, iron, antimony, mercury and Groups IA, IIA and IB of the Periodic Table of Elements and mixtures thereof; and (b) at least 8 parts by weight of a preferential plasticizer per 100 parts of said metal neutralized sulfonated EPDM terpolymer, said preferential plasticizer being selected from the group consisting of stearamides and zinc salts of carboxylic acids having about 12 to about 30 carbon atoms.
Claim 12
Dependent Claim
148 words
A polymeric formed article formed by a low pressure injection molding process which comprises essentially of an elastomeric composition which consists essentially of: (a) a metal neutralized sulfonated EPDM terpolymer having at least about 65 wt. % ethylene in the backbone of said metal neutralized sulfonated EPDM terpolymer, about 10 to about 60 meq. of metal sulfonate groups per 100 grams of said metal neutralized sulfonated EPDM terpolymer, a metal of said metal sulfonate groups being selected from the group consisting of aluminum, iron, antimony, mercury and Groups IA, IIA and IB of the Periodic Table of Elements and mixtures thereof; and (b) at least 8 parts by weight of a preferential plasticizer per 100 parts of said metal neutralized sulfonated EPDM terpolymer, said preferential plasticizer being selected from the group consisting of stearamides and zinc salts of carboxylic acids having about 12 to about 30 carbon atoms.
Claim 13
Dependent Claim
16 words
A polymer formed article according to claim 8, wherein said elastomeric article is a ski boot.
Claim 14
Dependent Claim
15 words
A polymeric formed article according to claim 9, wherein said preferential plasticizer is zinc stearate.
Claim 15
Dependent Claim
163 words
A polymeric article formed by a low pressure injection molding process which consists essentially of: (a) a metal neutralized sulfonated EPDM terpolymer having at least about 65 wt. % ethylene in the backbone of said metal neutralized sulfonated EPDM terpolymer, about 10 to about 60 meq. of metal sulfonate groups per 100 grams of said metal neutralized sulfonated EPDM terpolymer, a metal of said metal sulfonate groups being selected from the group consisting of aluminum, iron, antimony, mercury and Groups IA, IIA and IB of the Periodic Table of Elements and mixtures thereof; (b) at least 8 parts by weight of a preferential plasticizer per 100 parts of said metal neutralized sulfonated EPDM terpolymer, said preferential plasticizer being selected from the group consisting of stearamides and zinc salts of carboxylic acids having about 12 to about 30 carbon atoms; and (c) about 20 to about 100 parts by weight of a crystalline polyolefin per 100 parts of said metal neutralized sulfonated EPDM terpolymer.
Claim 16
Dependent Claim
163 words
A polymeric article formed by a low pressure injection molding process which consists essentially of: (a) a metal neutralized sulfonated EPDM terpolymer having at least about 65 wt. % ethylene in the backbone of said metal neutralized sulfonated EPDM terpolymer, about 10 to about 60 meq. of metal sulfonate groups per 100 grams of said metal neutralized sulfonated EPDM terpolymer, a metal of said metal sulfonate groups being selected from the group consisting of aluminum, iron, antimony, mercury and Groups IA, IIA and IB of the Periodic Table of Elements and mixtures thereof; (b) at least 8 parts by weight of a preferential plasticizer per 100 parts of said metal neutralized sulfonated EPDM terpolymer, said preferential plasticizer being selected from the group consisting of stearamides and zinc salts of carboxylic acids having about 12 to about 30 carbon atoms; and (c) about 20 to about 100 parts by weight of a crystalline polyolefin per 100 parts of said metal neutralized sulfonated EPDM terpolymer.
Claim 17
Dependent Claim
16 words
A polymer formed article according to claim 11, wherein said elastomeric article is a ski boot.
Claim 18
Dependent Claim
15 words
A polymeric formed article according to claim 11, wherein said preferential plasticizer is zinc stearate.
Claim 19
Dependent Claim
230 words
A polymeric article formed by a low pressure injection molding process which consists essentially of an elastomeric composition which consists essentially of: (a) a metal neutralized sulfonated EPDM terpolymer having at least about 65 wt. % ethylene in the backbone of said metal neutralized sulfonated EPDM terpolymer, about 10 to about 60 meq. of metal sulfonate groups per 100 grams of said metal neutralized sulfonated EPDM terpolymer, a metal of said metal sulfonate groups being selected from the group consisting of aluminum, iron, antimony, mercury and Groups IA, IIA and IB of the Periodic Table of Elements and mixtures thereof; (b) at least 8 parts by weight of a preferential plasticizer per 100 parts of said metal neutralized sulfonated EPDM terpolymer, said preferential plasticizer being selected from the group consisting of stearamides and zinc salts of carboxylic acids having about 12 to about 30 carbon atoms; (c) about 50 to about 300 parts by weight of an inorganic filler per 100 parts of said metal neutralized sulfonated EPDM terpolymer, said inorganic filler being selected from the group consisting of clay, talc and calcium carbonate and mixtures thereof; and (d) about 50 to about 100 parts by weight of a nonpolar process oil having less than about 2 wt. % polar type compounds, said non-polar process oil being selected from the group consisting of paraffinics, naphthenics and aromatics and mixtures thereof.
Claim 20
Dependent Claim
230 words
A polymeric article formed by a low pressure injection molding process which consists essentially of an elastomeric composition which consists essentially of: (a) a metal neutralized sulfonated EPDM terpolymer having at least about 65 wt. % ethylene in the backbone of said metal neutralized sulfonated EPDM terpolymer, about 10 to about 60 meq. of metal sulfonate groups per 100 grams of said metal neutralized sulfonated EPDM terpolymer, a metal of said metal sulfonate groups being selected from the group consisting of aluminum, iron, antimony, mercury and Groups IA, IIA and IB of the Periodic Table of Elements and mixtures thereof; (b) at least 8 parts by weight of a preferential plasticizer per 100 parts of said metal neutralized sulfonated EPDM terpolymer, said preferential plasticizer being selected from the group consisting of stearamides and zinc salts of carboxylic acids having about 12 to about 30 carbon atoms; (c) about 50 to about 300 parts by weight of an inorganic filler per 100 parts of said metal neutralized sulfonated EPDM terpolymer, said inorganic filler being selected from the group consisting of clay, talc and calcium carbonate and mixtures thereof; and (d) about 50 to about 100 parts by weight of a nonpolar process oil having less than about 2 wt. % polar type compounds, said non-polar process oil being selected from the group consisting of paraffinics, naphthenics and aromatics and mixtures thereof.
Claim 21
Dependent Claim
16 words
A polymer formed article according to claim 14, wherein said elastomeric article is a ski boot.
Claim 22
Dependent Claim
15 words
A polymeric formed article according to claim 14, wherein said preferential plasticizer is zinc stearate.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-05-07 | 1982-11-06 | 1983-05-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-05-07 | 1986-11-06 | 1987-05-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-05-07 | 1990-11-06 | 1991-05-08 | $7700.00 | Window Closed / Lapsed |