US4152482A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Anisotropic fibrous thermal insulator of relatively thick cross section and method for making same
Assignee: United States Department of Energy
•
Filing: 1978-05-10
•
Granted: 1979-05-01
•
Expires: 1998-05-10
Abstract
Abstract The present invention is directed to an anisotropic thermal insulator formed of carbon-bonded organic or inorganic fibers and having a thickness or cross section greater than about 3 centimeters. Delaminations and deleterious internal stresses generated during binder curing and carbonizing operations employed in the fabrication of thick fibrous insulation of thicknesses greater than 3 centimeters are essentially obviated by the method of the present invention. A slurry of fibers, thermosetting resin binder and water is vacuum molded into the selected insulator configuration with the total thickness of the molded slurry being less than about 3 centimeters, the binder is thermoset to join the fibers together at their nexaes, and then the binder is carbonized to form the carbon bond. A second slurry of the fibers, binder and water is then applied over the carbonized body with the vacuum molding, binder thermosetting and carbonizing steps being repeated to form a layered insulator with the binder providing a carbon bond between the layers. The molding, thermosetting and carbonizing steps may be repeated with additional slurries until the thermal insulator is of the desired final thickness. An additional feature of the present invention is provided by incorporating opacifying materials in any of the desired layers so as to provide different insulating properties at various temperatures. Concentration and/or type of additive can be varied from layer-to-layer.
Inventors
- 👤 Carl D. Reynolds
- 👤 Zane L. Ardary
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 22:19
CPC Classifications
C; C04; C04B; C04B30/00; C04B30/02; C04B35/00; C04B35/515; C04B35/52; C04B35/71; C04B35/78; C04B35/80; C04B35/83; Y; Y10; Y10S; Y10S428/00; Y10S428/91; Y10S428/92; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982; Y10T428/30; Y10T442/00; Y10T442/60; Y10T442/659; Y10T442/67
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
319 words
A method for fabricating a thermal insulating composite comprising an array of oriented fibers joined together by a carbonized binder and characterized by having anisotropic thermal properties and a wall thickness greater than about 3 centimeters, comprising the steps of: (a) forming a slurry of fibers of a carbonaceous or refractory material, a particulate thermosetting resin binder in a binder-to-fiber ratio of about 0.5 to 1.0, and water in a solids-to-water ratio of about 0.005 to 1.0 into a desired configuration by contacting a perforated mold of said configuration with a sufficient quantity of the slurry to provide a composite with a wall thickness less than about three centimeters; (b) subjecting the molded slurry to a pressure less than atmospheric through the perforated mold for forming the slurry into the desired insulation configuration and for removing excess water from the slurry while aligning the fibers predominantly in a plane parallel to the surface of the perforated mold; (c) heating the molded slurry to a temperature sufficient to remove residual water from the slurry and to thermoset the binder for joining the fibers together primarily at the nexae of the fibers; (d) removing the joined fiber body from the mold and heating the body in an inert atmosphere to a temperature sufficient to carbonize the binder; (e) repeating steps (a) though (d) with this repetition of steps including replacing the body of carbon-bonded fibers on the perforated mold and thereafter applying a further quantity of slurry as in step (a) but modified by placing said further quantity of the slurry onto the surface of the previously carbonized carbon-bonded fiber body opposite the surface in contact with the perforated mold; thereafter repeating steps (b) through (d) to also provide a carbon bond with the previously formed carbon-bonded fiber body; and, repeating (e) a sufficient number of times to provide a multilayered composite of said wall thickness between three and nine centimeters.
Claim 2
Independent Claim
319 words
A method for fabricating a thermal insulating composite comprising an array of oriented fibers joined together by a carbonized binder and characterized by having anisotropic thermal properties and a wall thickness greater than about 3 centimeters, comprising the steps of: (a) forming a slurry of fibers of a carbonaceous or refractory material, a particulate thermosetting resin binder in a binder-to-fiber ratio of about 0.5 to 1.0, and water in a solids-to-water ratio of about 0.005 to 1.0 into a desired configuration by contacting a perforated mold of said configuration with a sufficient quantity of the slurry to provide a composite with a wall thickness less than about three centimeters; (b) subjecting the molded slurry to a pressure less than atmospheric through the perforated mold for forming the slurry into the desired insulation configuration and for removing excess water from the slurry while aligning the fibers predominantly in a plane parallel to the surface of the perforated mold; (c) heating the molded slurry to a temperature sufficient to remove residual water from the slurry and to thermoset the binder for joining the fibers together primarily at the nexae of the fibers; (d) removing the joined fiber body from the mold and heating the body in an inert atmosphere to a temperature sufficient to carbonize the binder; (e) repeating steps (a) though (d) with this repetition of steps including replacing the body of carbon-bonded fibers on the perforated mold and thereafter applying a further quantity of slurry as in step (a) but modified by placing said further quantity of the slurry onto the surface of the previously carbonized carbon-bonded fiber body opposite the surface in contact with the perforated mold; thereafter repeating steps (b) through (d) to also provide a carbon bond with the previously formed carbon-bonded fiber body; and, repeating (e) a sufficient number of times to provide a multilayered composite of said wall thickness between three and nine centimeters.
Claim 3
Dependent Claim
46 words
A method for fabricating a thermal insulating composite as claimed in claim 1, including the additional step of incorporating graphite flakes in the slurry employed in step (e) with said flakes being in the concentration of about 10 to 30 wt.% of the fiber-binder-graphite flake mixture.
Claim 4
Dependent Claim
24 words
A method for fabricating a thermal insulating composite as claimed in claim 2, wherein the concentration of graphite flakes selectively increased in successive steps.
Claim 5
Dependent Claim
89 words
A multi-layer thermal insulating composite of a cross-sectional thickness greater than 3 centimeters, comprising in each layer a plurality of discrete fibers of a carbonaceous or refractory material with said fibers disposed predominantly in a common plane essentially perpendicular to the expected direction of heat transference through the composite for providing the composite with anisotropic thermal properties, and with said fibers being joined together primarily at the nexae thereof by a binder consisting of a carbonized thermosettng resin, and a binder of carbonized thermosetting resing joining said layers together.
Claim 6
Dependent Claim
89 words
A multi-layer thermal insulating composite of a cross-sectional thickness greater than 3 centimeters, comprising in each layer a plurality of discrete fibers of a carbonaceous or refractory material with said fibers disposed predominantly in a common plane essentially perpendicular to the expected direction of heat transference through the composite for providing the composite with anisotropic thermal properties, and with said fibers being joined together primarily at the nexae thereof by a binder consisting of a carbonized thermosettng resin, and a binder of carbonized thermosetting resing joining said layers together.
Claim 7
Dependent Claim
80 words
A multi-layer thermal insulating composite as claimed in claim 4, wherein the layer of the thermal insulating composite nearest one surface of the composite consists of the carbon-bonded fibers, and wherein at least one other layer of the thermal insulating composite including the layer nearest the surface opposite to said one surface contains graphite flakes with the maximum dimension of said flakes being disposed in parallel planes essentially perpendicular to the expected direction of radiant heat transfer through said composite.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-04-30 | 1982-10-30 | 1983-05-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-04-30 | 1986-10-30 | 1987-05-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-04-30 | 1990-10-30 | 1991-05-01 | $7700.00 | Window Closed / Lapsed |