Siliceous filled vulcanizates
Assignee: Polysar Ltd
•
Filing: 1978-03-07
•
Granted: 1979-05-01
•
Expires: 1998-03-07
Abstract
Abstract There is provided a process, and the product of that process, for the production of improved silica or calcium silicate filled rubbery vulcanizates which comprises the preparation of a mixture comprising a vulcanizable hydrocarbyl polymer containing hydroxyl groups, silica or calcium silicate and an organic acid or salt thereof, shearing the mixture at an elevated temperature, incorporating vulcanization active compounds and vulcanizing to produce the improved vulcanizates. Such improved vulcanizates may be used generally in the rubber industry.
Inventors
- 👤 Douglas C. Edwards
- 👤 Kyosaku Sato
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 21:03
CPC Classifications
C; C08; C08K; C08K3/00; C08K3/34
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
168 words
A process for the production of improved silica or calcium silicate filled rubbery vulcanizates which process comprises preparing a mixture comprising 100 parts by weight of a vulcanizable hydrocarbyl polymer containing from about 1.5 to about 80 millimoles of hydroxyl groups per 100 grams of polymer, from about 5 to about 100 parts by weight of silica or calcium silicate, and from about 1 to about 5 parts by weight of an organic acid or a salt thereof, subjecting said mixture to a treatment wherein it is sheared at a temperature of from about 100° C. to about 175° C., cooling said mixture, incorporating into said mixture vulcanization active compounds, and vulcanizing by heating at an elevated temperature to produce the improved vulcanizate, said organic acid or salt thereof being selected from the C 15 -C 20 fatty acids, the C 15 -C 20 unsaturated fatty acids and the aromatic carboxylic acids, or the alkali metal, alkaline earth metal or ammonium salts thereof, and from aryl sulphonic acids.
Claim 2
Dependent Claim
168 words
A process for the production of improved silica or calcium silicate filled rubbery vulcanizates which process comprises preparing a mixture comprising 100 parts by weight of a vulcanizable hydrocarbyl polymer containing from about 1.5 to about 80 millimoles of hydroxyl groups per 100 grams of polymer, from about 5 to about 100 parts by weight of silica or calcium silicate, and from about 1 to about 5 parts by weight of an organic acid or a salt thereof, subjecting said mixture to a treatment wherein it is sheared at a temperature of from about 100° C. to about 175° C., cooling said mixture, incorporating into said mixture vulcanization active compounds, and vulcanizing by heating at an elevated temperature to produce the improved vulcanizate, said organic acid or salt thereof being selected from the C 15 -C 20 fatty acids, the C 15 -C 20 unsaturated fatty acids and the aromatic carboxylic acids, or the alkali metal, alkaline earth metal or ammonium salts thereof, and from aryl sulphonic acids.
Claim 3
Dependent Claim
24 words
The process of claim 1 wherein the silica or calcium silicate has an average particle size of from about 0.01 to about 0.1 microns.
Claim 4
Dependent Claim
16 words
The process of claim 1 wherein the shearing is for about 0.25 to about 10 minutes.
Claim 5
Dependent Claim
19 words
The process of claim 3 in which the shearing is on a rubber mill or in an internal mixer.
Claim 6
Dependent Claim
68 words
The process of claim 1 wherein the hydrocarbyl polymer is a C 4 -C 6 conjugated diolefin polymer containing hydroxyl groups, a polymer containing hydroxyl groups of a C 4 -C 6 conjugated diolefin and at least one other copolymerizable vinyl or vinylidene-containing monomer, a polymer containing hydroxyl groups comprising a C 4 -C 6 isoolefin or a polymer containing hydroxyl groups comprising one or two alpha olefins.
Claim 7
Dependent Claim
26 words
The process of claim 1 in which the vulcanization is by heating at 125° to 200° C. for times of from 1 minute to 10 hours.
Claim 8
Dependent Claim
144 words
Improved silica or calcium silicate filled rubbery vulcanizates obtained by the vulcanization of a mixture comprising 100 parts by weight of a vulcanizable hydrocarbyl polymer containing from about 1.5 to about 80 millimoles of hydroxyl groups per 100 grams of polymer, from 5 to about 100 parts by weight of silica or calcium silicate, and from about 1 to about 5 parts by weight of an organic acid or a salt thereof, said mixture having been subjected to shearing at a temperature of from about 100° to about 175° C. prior to incorporation of vulcanization active compounds and vulcanization, said organic acid or salt thereof being selected from the C 15 -C 20 fatty acids, the C 15 -C 20 unsaturated fatty acids and the aromatic carboxylic acids, or the alkali metal, alkaline earth metal or ammonium salts thereof, and from aryl sulphonic acids.
Claim 9
Dependent Claim
144 words
Improved silica or calcium silicate filled rubbery vulcanizates obtained by the vulcanization of a mixture comprising 100 parts by weight of a vulcanizable hydrocarbyl polymer containing from about 1.5 to about 80 millimoles of hydroxyl groups per 100 grams of polymer, from 5 to about 100 parts by weight of silica or calcium silicate, and from about 1 to about 5 parts by weight of an organic acid or a salt thereof, said mixture having been subjected to shearing at a temperature of from about 100° to about 175° C. prior to incorporation of vulcanization active compounds and vulcanization, said organic acid or salt thereof being selected from the C 15 -C 20 fatty acids, the C 15 -C 20 unsaturated fatty acids and the aromatic carboxylic acids, or the alkali metal, alkaline earth metal or ammonium salts thereof, and from aryl sulphonic acids.
Claim 10
Dependent Claim
35 words
The vulcanizate of claim 7 wherein the shearing is for about 0.25 to about 10 minutes and the silica or calcium silicate has an average particle size of from about 0.01 to about 0.1 microns.
Claim 11
Dependent Claim
69 words
The vulcanizate of claim 7 in which the hydrocarbyl polymer is a C 4 -C 6 conjugated diolefin polymer containing hydroxyl groups, a polymer containing hydroxyl groups of a C 4 -C 6 conjugated diolefin and at least one other copolymerizable vinyl or vinylidene-containing monomer, or polymer containing hydroxyl groups comprising a C 4 -C 6 isoolefin or a polymer containing hydroxyl groups comprising one or two alpha olefins.
Claim 12
Dependent Claim
33 words
The vulcanizate of claim 9 wherein the hydrocarbyl polymer is selected from butadiene-styrene polymers containing hydroxyl groups, butadiene-acrylonitrile polymers containing hydroxyl groups, isoprene-acrylonitrile polymers containing hydroxyl groups and butadiene-methacrylonitrile polymer containing hydroxyl groups.
Claim 13
Dependent Claim
50 words
The vulcanizate of claim 10 in which the hydroxyl groups have been incorporated into the polymer by emulsion free radical copolymerization with a monomer selected from hydroxyethyl acrylate, hydroxyethyl methacrylate, hydroxypropyl acrylate, hydroxypropyl methacrylate, hydroxypropyl cortonate, di-(2-hydroxyethyl)maleate, di-(2-hydroxy ethyl) fumarate, N-ethanol acrylamide, hydroxyethyl vinyl ether and diethylene glycol vinyl ether.
Claim 14
Dependent Claim
42 words
The vulcanizate of claim 9 wherein the hydrocarbyl polymer is selected from polybutadiene containing hydroxyl groups, isobutylene-isoprene polymers containing hydroxyl groups, chlorinated or brominated isobutyleneisoprene polymers containing hydroxyl groups, ethylenepropylene polymers containing hydroxyl groups, and ethylenepropylene- non-conjugated diolefin polymers containing hydroxyl groups.
Claim 15
Dependent Claim
28 words
The vulcanizate of claim 10 wherein the organic acid or salt thereof is palmitic acid or stearic acid, or the sodium, potassium, calcium, zinc or ammonium salt thereof.
Claim 16
Dependent Claim
27 words
The vulcanizate of claim 10 wherein the organic acid or salt thereof is oleic or linoleic acid, or the sodium, potassium, calcium, zinc or ammonium salt thereof.
Claim 17
Dependent Claim
29 words
The vulcanizate of claim 10 wherein the organic acid or salt thereof is benzoic, phthalic, cinnamic or hydroxybenzoic acid, or the sodium, potassium, calcium, zinc or ammonium salt thereof.
Claim 18
Dependent Claim
21 words
The vulcanizate of claim 10 in which the organic acid is benzene sulphonic acid, toluene sulphonic acid or xylene sulphonic acid.
Claim 19
Dependent Claim
43 words
The vulcanizate of claim 8 wherein the hydrocarbyl polymer is a butadiene-acrylonitrile polymer containing copolymerized therewith hydroxyethyl acrylate or methacrylate or hydroxypropyl acrylate or methacrylate and the organic acid or salt thereof is stearic acid or the sodium, potassium or zinc salt thereof.
Claim 20
Dependent Claim
43 words
The vulcanizate of claim 8 wherein the hydrocarbyl polymer is a styrene-butadiene polymer containing copolymerized therewith hydroxyethyl acrylate or methacrylate or hydroxypropyl acrylate or methacrylate and the organic acid or salt thereof is stearic acid or the sodium, potassium or zinc salt thereof.
Claim 21
Dependent Claim
45 words
The vulcanizate of claim 17 in which the polymer is mixed with a butadiene-acrylonitrile polymer containing no hydroxyl groups in such a proportion that the concentration of hydroxyl groups is from about 4 to about 60 millimoles per 100 grams of the mixture of polymers.
Claim 22
Dependent Claim
45 words
The vulcanizate of claim 18 in which the polymer is mixed with a styrene-butadiene polymer containing no hydroxyl groups in such a proportion that the concentration of hydroxyl groups is from about 4 to about 60 millimoles per 100 grams of the mixture of polymers.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-04-30 | 1982-10-30 | 1983-05-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-04-30 | 1986-10-30 | 1987-05-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-04-30 | 1990-10-30 | 1991-05-01 | $7700.00 | Window Closed / Lapsed |