US4152224A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Inorganic additives for zinc-alkaline secondary batteries and alkaline zinc-plating baths
Assignee: Scientific Research Foundation
•
Filing: 1977-08-22
•
Granted: 1979-05-01
•
Expires: 1997-08-22
Abstract
Abstract The invention relates to an additive, to be added to conventional electrolytes of alkaline secondary zinc cells or to alkaline zinc plating baths, adapted to establish in said liquids a minimum concentration of 10-6 M per liter of cobalt ions and a minimum concentration of 5.10-6 M per liter of cadmium ions, said additive being a coprecipitate of cobalt hydroxide and cadmium hydroxide and either magnesium hydroxide or calcium hydroxide, to electrolytes for alkaline secondary zinc cells and alkaline zinc plating baths containing such additives and to a process for the production of such additives.
Inventors
- 👤 Yitzchak Klein
- 👤 Jonathan G. Goldstein
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 11:49
CPC Classifications
B; B01; B01J; B01J13/00; B01J13/0052; B01J13/0056; B01J13/006; C; C25; C25D; C25D3/00; C25D3/02; C25D3/22; H; H01; H01M; H01M10/00; H01M10/24; H01M10/26; Y; Y02; Y02E; Y02E60/00; Y02E60/10
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
73 words
An additive, to be added to conventional electrolytes of alkaline secondary zinc cells or to alkaline zinc plating baths adapted to establish in said liquids a minimum concentrate of 10 -6 M per liter of cobalt ions and a minimum concentration of 5.10 -6 M per liter of cadmium ions being a coprecipitated hydroxide gel of cobalt hydroxide and of cadmium hydroxide and with at least one of magnesium hydroxide and calcium hydroxide.
Claim 2
Dependent Claim
73 words
An additive, to be added to conventional electrolytes of alkaline secondary zinc cells or to alkaline zinc plating baths adapted to establish in said liquids a minimum concentrate of 10 -6 M per liter of cobalt ions and a minimum concentration of 5.10 -6 M per liter of cadmium ions being a coprecipitated hydroxide gel of cobalt hydroxide and of cadmium hydroxide and with at least one of magnesium hydroxide and calcium hydroxide.
Claim 3
Dependent Claim
17 words
An additive according to claim 1, wherein part of the cobalt hydroxide is replaced by nickel hydroxide.
Claim 4
Dependent Claim
25 words
An additive according to claim 1 which is a Co-Cd-Mg-hydroxide gel wherein the ratio of Co and Cd to Mg varies from 1:10 to 10:1.
Claim 5
Dependent Claim
20 words
An additive according to claim 1, wherein the ratio of Co ions to Cd ions varies from 1:3 to 3:1.
Claim 6
Dependent Claim
25 words
An additive according to claim 1, wherein the hydroxide is a Co--Ni--Cd--Mg, a Co--Ni--Cd--Mg--Ca; a Co--Ni--Cd--Ca; a Co--Cd--Mg--Ca; a Co--Cd--Ca or a Co-Ni-Cd coprecipitated hydroxide.
Claim 7
Dependent Claim
29 words
A method of inhibiting corrosion of zinc electrodes which comprises adding an effective quantity of an additive according to claim 5 in the vicinity of the said zinc electrode.
Claim 8
Dependent Claim
26 words
A process for electroplating with zinc or for cladding with zinc, which consists of electroplating from an electrolyte which contains an additive according to claim 1.
Claim 9
Dependent Claim
23 words
An electrolyte for alkaline secondary zinc cells containing 0.1 g or more of an additive according to claim 1 per liter of electrolyte.
Claim 10
Dependent Claim
11 words
Alkaline secondary zinc cells containing an electrolyte according to claim 8.
Claim 11
Dependent Claim
27 words
An alkaline zinc electroplating bath containing a quantity of 0.1 g or more per liter of an additive according to claim 1 per liter of plating bath.
Claim 12
Dependent Claim
73 words
Additives to be added to conventional electrolytes of alkaline secondary zinc cells or to alkaline zinc plating baths, adapted to establish a steady-state minimum concentration of at least 10 -6 M Co-ions and 5.10 -6 M Cd-ions, in combination with Mg or Ca-ions, said additive being a mixture of very sparingly soluble compounds of the required metals in the form of a coprecipitate consisting mainly of hydroxides of the metals in gel form.
Claim 13
Dependent Claim
73 words
Additives to be added to conventional electrolytes of alkaline secondary zinc cells or to alkaline zinc plating baths, adapted to establish a steady-state minimum concentration of at least 10 -6 M Co-ions and 5.10 -6 M Cd-ions, in combination with Mg or Ca-ions, said additive being a mixture of very sparingly soluble compounds of the required metals in the form of a coprecipitate consisting mainly of hydroxides of the metals in gel form.
Claim 14
Dependent Claim
85 words
A process for the production of additives for use in electrolytes of secondary alkaline zinc cells and for use in electroplating baths for electroplating with zinc, which comprises preparing a solution of water-soluble salts of cobalt and cadmium and of magnesium or calcium; precipitating a coprecipitate gel of the hydroxides of same by adding to said solution an aqueous solution of an alkali metal hydroxide until a hydroxide gel precipitate is obtained; separating the precipitate and removing from same soluble impurities by washing with water.
Claim 15
Dependent Claim
85 words
A process for the production of additives for use in electrolytes of secondary alkaline zinc cells and for use in electroplating baths for electroplating with zinc, which comprises preparing a solution of water-soluble salts of cobalt and cadmium and of magnesium or calcium; precipitating a coprecipitate gel of the hydroxides of same by adding to said solution an aqueous solution of an alkali metal hydroxide until a hydroxide gel precipitate is obtained; separating the precipitate and removing from same soluble impurities by washing with water.
Claim 16
Dependent Claim
17 words
A process according to claim 12, wherein the hydroxide gel is aerated and heated after its precipitation.
Claim 17
Dependent Claim
18 words
A process according to claim 12, wherein the coprecipitation is effected at a temperature of about 0° C.
Claim 18
Dependent Claim
18 words
A process according to claim 12, wherein the hydroxide gel is heated to about 100° C. after aeration.
References Cited (Backward Citations)
US3816178A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-04-30 | 1982-10-30 | 1983-05-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-04-30 | 1986-10-30 | 1987-05-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-04-30 | 1990-10-30 | 1991-05-01 | $7700.00 | Window Closed / Lapsed |