Matrix forming composition
Assignee: Set Products Inc
•
Filing: 1978-01-31
•
Granted: 1979-05-01
•
Expires: 1998-01-31
Abstract
Abstract A matrix forming composition is provided which when mixed with water is capable of setting to form a solidified mass which comprises, in weight percent, from about 30 to about 66 percent basic material, from about 25 to about 59 percent water soluble monoammonium phosphate, and from about 1 to about 27 percent water soluble polyphosphate. This matrix forming composition can be utilized to bond various materials together. For example, it is ideal for bonding aggregate materials together to form a solidified mass which is characterized by its high strength.
Inventors
- 👤 Howard J. Horvitz
- 👤 Anthony P. Gray
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 03:46
CPC Classifications
C; C04; C04B; C04B28/00; C04B28/34; C04B35/00; C04B35/622; C04B35/626; C04B35/63; C04B35/6303; C04B35/6306
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
96 words
A dry matrix forming composition capable, when mixed with water of setting to form a solidified mass characterized by its high compressive strength which, in weight percent consists essentially of: (a) form about 30 to about 66 percent basic material containing at least about 85 percent magnesium oxide; (b) from about 25 to about 59 percent water soluble monoammonium phosphate; and (c) from about 1 to about 27 percent water soluble polyphosphate having the formula M.sub.(n + 2) P n O.sub.(3n + 1) wherein M is a cation and n is the integer 2 or 3.
Claim 2
Dependent Claim
96 words
A dry matrix forming composition capable, when mixed with water of setting to form a solidified mass characterized by its high compressive strength which, in weight percent consists essentially of: (a) form about 30 to about 66 percent basic material containing at least about 85 percent magnesium oxide; (b) from about 25 to about 59 percent water soluble monoammonium phosphate; and (c) from about 1 to about 27 percent water soluble polyphosphate having the formula M.sub.(n + 2) P n O.sub.(3n + 1) wherein M is a cation and n is the integer 2 or 3.
Claim 3
Dependent Claim
14 words
The matrix forming composition of claim 1 wherein said basic material is deadburned magnesite.
Claim 4
Dependent Claim
21 words
The matrix forming composition of claim 2 wherein said magnesite comprises from about 85 to about 99 weight percent magnesium oxide.
Claim 5
Dependent Claim
21 words
The matrix forming composition of claim 1 wherein said polyphosphate is sodium tripolyphosphate, sodium acid pyrophosphate, tetrasodium pyrophosphate or mixtures thereof.
Claim 6
Dependent Claim
108 words
A cry composition capable, when mixed with water of setting to form a solidified mass characterized by its high compressive strength comprising in weight percent, up to about 85 percent of a filler material with the remainder being a matrix material consisting of from about 30 to about 66 percent of a basic material containing at least about 85 percent magnesium oxide, from about 25 to about 59 percent water soluble monoammonium phosphate, and from about 1 to about 27 percent water soluble polyphosphate having the formula M.sub.(n + 2) P n O.sub.(3n + 1) wherein M is a cation and n is the integer 2 or 3.
Claim 7
Dependent Claim
108 words
A cry composition capable, when mixed with water of setting to form a solidified mass characterized by its high compressive strength comprising in weight percent, up to about 85 percent of a filler material with the remainder being a matrix material consisting of from about 30 to about 66 percent of a basic material containing at least about 85 percent magnesium oxide, from about 25 to about 59 percent water soluble monoammonium phosphate, and from about 1 to about 27 percent water soluble polyphosphate having the formula M.sub.(n + 2) P n O.sub.(3n + 1) wherein M is a cation and n is the integer 2 or 3.
Claim 8
Dependent Claim
43 words
The composition of claim 5 wherein said filler material is selected from the group consisting of dolomitic limestone, silica, zircon, zirconia, fused alumina, kyanite, aluminosilicate minerals, rutile, feldspar, granites, chromites, ilmenite, barite, iron particles, limestone, blast furnace slag, fly ash and mixtures thereof.
Claim 9
Dependent Claim
11 words
The composition of claim 6 wherein said filler material is silica.
Claim 10
Dependent Claim
28 words
The composition of claim 7 wherein said silica is present, in weight percent, in an amount ranging from about 55 to about 77 percent of said total composition.
Claim 11
Dependent Claim
12 words
The compositin of claim 5 wherein said basic material is deadburned magnesite.
Claim 12
Dependent Claim
25 words
The composition of claim 5 wherein the polyphosphate is selected from the group consisting of sodium acid pyrophosphate, sodium tripolyphosphate, tetrasodium pyrophosphate and mixtures thereof.
Claim 13
Dependent Claim
134 words
A process for forming a solidified cementitious mass which is characterized by its high compressive strength which process comprises the steps of: (a) providing in dry powdered form a matrix forming composition consisting essentially of; (i) from about 30 to about 66 percent of basic material containing at least about 85 percent magnesium oxide; (ii) from about 25 to about 59 percent by weight of water soluble monoammonium phosphate; (iii) from about 1 to about 27 percent by weight of water soluble polyphosphate having the formula M.sub.(n + 2) P n O.sub.(3n + 1) wherein M is a cation and n is the integer 2 to 3; (b) adding water to said matrix composition form a wetted mass, and (c) forming said wetted mass into the desired shape and subsequently permitting it to solidify.
Claim 14
Dependent Claim
134 words
A process for forming a solidified cementitious mass which is characterized by its high compressive strength which process comprises the steps of: (a) providing in dry powdered form a matrix forming composition consisting essentially of; (i) from about 30 to about 66 percent of basic material containing at least about 85 percent magnesium oxide; (ii) from about 25 to about 59 percent by weight of water soluble monoammonium phosphate; (iii) from about 1 to about 27 percent by weight of water soluble polyphosphate having the formula M.sub.(n + 2) P n O.sub.(3n + 1) wherein M is a cation and n is the integer 2 to 3; (b) adding water to said matrix composition form a wetted mass, and (c) forming said wetted mass into the desired shape and subsequently permitting it to solidify.
Claim 15
Dependent Claim
29 words
The process of claim 11 which further includes the steps of adding a filler material to said wetted mass prior to forming said wetted mass into the desired shape.
Claim 16
Dependent Claim
43 words
The process of claim 12 wherein said filler material is selected from the group consisting of dolomite limestone, silica, zircon, zirconia, fused alumina, kyanite, aluminosilicate minerals, rutile, feldspar, granites, chromites, ilmenite, barite, iron particles, limestone, blast furnace slag, fly ash and mixtures thereof.
Claim 17
Dependent Claim
11 words
The process of claim 13 wherein said filler material is silica.
Claim 18
Dependent Claim
28 words
The process of claim 14 wherein said silica is present, in weight percent, in an amount ranging from about 55 to about 77 percent of said total composition.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-04-30 | 1982-10-30 | 1983-05-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-04-30 | 1986-10-30 | 1987-05-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-04-30 | 1990-10-30 | 1991-05-01 | $7700.00 | Window Closed / Lapsed |