Method for production of printed circuits by electroless metal plating employing a solid solution of metal oxides of titanium, nickel, and antimony as a masking material
Assignee: Hitachi Ltd
•
Filing: 1978-03-08
•
Granted: 1979-04-24
•
Expires: 1998-03-08
Abstract
Abstract Printed circuits are produced on an insulating substrate by electroless metal plating according to a method comprising steps of: (I) forming a plating resist on a negative pattern of circuit with a masking material having an effect upon reducing the deposition of an initiator for electroless metal plating, and depositing the initiator onto the entire surface of the insulating substrate, (II) removing the initiator from the surface of said resist, and (III) dipping the insulating substrate in an electroless metal plating solution, thereby forming an electroless metal plating on a positive pattern of circuit, wherein a thermosetting resin containing a rutile type solid solution of metal oxides of titanium, nickel and antimony is employed as the masking material in said step (I), and the initiator is removed from the surface of the resist through contact with a hydrochloric acid solution of ammonium persulfate in said step (II).
Inventors
- 👤 Motoyo Wajima
- 👤 Mineo Kawamoto
- 👤 Kanji Murakami
- 👤 Hirosada Morishita
- 👤 Haruo Suzuki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 07:22
CPC Classifications
C; C23; C23C; C23C18/00; C23C18/16; C23C18/1601; C23C18/1603; C23C18/1605; H; H05; H05K; H05K3/00; H05K3/10; H05K3/18; H05K3/181; H05K3/182; H05K3/184; H05K2203/00; H05K2203/07; H05K2203/0703; H05K2203/0706; H05K2203/0713; H05K2203/14; H05K2203/1415
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
139 words
A method for producing a printed circuit comprising the following steps: (I) forming a plating resist on a negative pattern on circuit on a substrate with a masking material having an effect of reducing deposition and adhesion of a palladium initiator for electroless metal plating, and depositing a palladium initiator on an entire surface of substrate, (II) removing the initiator on the resist, and (III) dipping the substrate in an electroless metal plating solution, thereby forming electroless metal films on a positive pattern of the circuit, wherein an improvement comprises using a thermosetting resin containing a solid solution of oxides of titanium, nickel and antimony as the masking material in said step (I) and contacting the substrate with a hydrochloric acid solution of ammonium persulfate in said step (II) as a means for removing the initiator on the resist.
Claim 2
Independent Claim
139 words
A method for producing a printed circuit comprising the following steps: (I) forming a plating resist on a negative pattern on circuit on a substrate with a masking material having an effect of reducing deposition and adhesion of a palladium initiator for electroless metal plating, and depositing a palladium initiator on an entire surface of substrate, (II) removing the initiator on the resist, and (III) dipping the substrate in an electroless metal plating solution, thereby forming electroless metal films on a positive pattern of the circuit, wherein an improvement comprises using a thermosetting resin containing a solid solution of oxides of titanium, nickel and antimony as the masking material in said step (I) and contacting the substrate with a hydrochloric acid solution of ammonium persulfate in said step (II) as a means for removing the initiator on the resist.
Claim 3
Dependent Claim
92 words
A method according to claim 1, wherein a masking material containing 2 to 40 parts by weight of rutile type solid solution of TiO 2 --NiO--Sb 2 O 5 as the solid solution of oxides per 100 parts by weight of the thermo-setting resin was used in said step (I), and a solution containing 0.5 to 20 g of ammonium persulfate, 50 to 200 ml of 35% hydrochloric acid, and water to make the entire solution 1 l is used as the hydrochloric acid solution of ammonium persulfate in said step (II).
Claim 4
Dependent Claim
35 words
A method according to claim 2, wherein bisphenol A type epoxy resin having an epoxy equivalent amount of 900 or higher is used as the thermo-setting resin for the masking material in said step (I).
Claim 5
Dependent Claim
69 words
A method according to claim 2, wherein a mixture of bisphenol A type epoxy resin having an epoxy equivalent amount of 900 or higher with less than 40% by weight of bisphenol A type or novolak type epoxy resin having an epoxy equivalent amount of less than 500 on the basis of entire epoxy resins is used as the thermo-setting resin for the masking material in said step (I).
Claim 6
Dependent Claim
24 words
A method according to claim 2, wherein said solid solution is in the form of fine powders having a particle size not exceeding 10μm.
Claim 7
Dependent Claim
14 words
A method according to claim 5, wherein the particle size is less than 1.2μm.
Claim 8
Dependent Claim
32 words
A method according to claim 2, wherein said substrate is contacted with said hydrochloric acid solution in said step (II) at a solution temperature of 15° to 25° C. for 3-15 minutes.
References Cited (Backward Citations)
US3443988A
Cited
US3562038A
Cited
US3672925A
Cited
DE2506150A1
Cited
US3993799A
Cited
DE2628350A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-04-23 | 1982-10-23 | 1983-04-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-04-23 | 1986-10-23 | 1987-04-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-04-23 | 1990-10-23 | 1991-04-24 | $7700.00 | Window Closed / Lapsed |