Process for preparing multifunctional acrylate-modified vinyl ester-alkyl acrylate/methacrylate copolymer coagulum-free latex
Assignee: Shell USA Inc
•
Filing: 1977-12-01
•
Granted: 1979-04-24
•
Expires: 1997-12-01
Abstract
Abstract A process for preparing multifunctional acrylate modified-vinyl ester-alkyl acrylate/methacrylate copolymer coagulum-free latex is disclosed which comprises emulsion-polymerizing a non-pre-emulsified mixture of: (i) from about 40% to about 95% based on total weight of comonomers of a vinyl ester, (ii) from about 5% to about 35% based on total weight of comonomers of an ester derived from the reaction of a monohydric alcohol and acrylic acid or methacrylic acid, and (iii) from about 0.5% to about 10.0% based on total weight of comonomers of an ester derived from the reaction of a polyhydric alcohol and an acid selected from the group consisting of acrylic acid and methacrylic acid, there being at least two hydroxyl groups of the alcohol esterified with the acid, In the presence of a free radical polymerization catalyst and a chain transfer agent.
Inventors
- 👤 Ralph F. Patella
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 09:09
CPC Classifications
C; C08; C08F; C08F218/00; C08F218/02; C08F218/04
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
157 words
A process for preparing multifunctional acrylate modified-vinyl ester-alkyl acrylate/methacrylate copolymer latex, highly stable and substantially coagulum-free, which comprises emulsion-polymerizing a non-pre-emulisified mixture of: (i) from about 40% to about 95%, based on the total weight of comonomers, of a vinyl ester selected from the group consisting of vinyl acetate, vinyl propionate and vinyl butyrate (ii) from about 5% to about 35%, based on the total weight of comonomers, of an ester derived from the reaction of a monohydric alcohol and acrylic acid or methacrylic acid, and (iii) from about 0.5% to about 10%, based on the total weight of comonomers, of an ester derived from the reaction of a polyhydric alcohol and an acid selected from the group consisting of acrylic acid and methacrylic acid, there being at least two hydroxyl groups of the alcohol esterified with the acid, in the presence of water, a free radical polymerization catalyst and a normally liquid mercaptan chain transfer agent.
Claim 2
Dependent Claim
157 words
A process for preparing multifunctional acrylate modified-vinyl ester-alkyl acrylate/methacrylate copolymer latex, highly stable and substantially coagulum-free, which comprises emulsion-polymerizing a non-pre-emulisified mixture of: (i) from about 40% to about 95%, based on the total weight of comonomers, of a vinyl ester selected from the group consisting of vinyl acetate, vinyl propionate and vinyl butyrate (ii) from about 5% to about 35%, based on the total weight of comonomers, of an ester derived from the reaction of a monohydric alcohol and acrylic acid or methacrylic acid, and (iii) from about 0.5% to about 10%, based on the total weight of comonomers, of an ester derived from the reaction of a polyhydric alcohol and an acid selected from the group consisting of acrylic acid and methacrylic acid, there being at least two hydroxyl groups of the alcohol esterified with the acid, in the presence of water, a free radical polymerization catalyst and a normally liquid mercaptan chain transfer agent.
Claim 3
Dependent Claim
13 words
The process of claim 1 wherein the vinyl ester (i) is vinyl acetate.
Claim 4
Dependent Claim
25 words
The process of claim 1 wherein the vinyl ester (i) is employed at from 45% to about 70% based on the total weight of comonomers.
Claim 5
Dependent Claim
12 words
The process of claim 1 wherein the ester (ii) is butyl acrylate.
Claim 6
Dependent Claim
24 words
The process of claim 1 wherein ester (ii) is employed at from about 10% to about 30% based on the total weight of comonomers.
Claim 7
Dependent Claim
14 words
The process of claim 1 wherein ester (iii) is trimethylolpropane triacrylate or pentaerythritol triacrylate.
Claim 8
Dependent Claim
23 words
The process of claim 1 wherein ester (iii) is employed at from about 0.5% to about 10.0% based on total weight of comonomers.
Claim 9
Dependent Claim
33 words
The process of claim 1 wherein the total comonomer contains up to 10% by weight of a copolymerizable composition which will contribute pendant carboxylic acid groups in the backbone of the resulting copolymer.
Claim 10
Dependent Claim
15 words
The process of claim 8 wherein the copolymerizable composition is acrylic acid or methacrylic acid.
Claim 11
Dependent Claim
32 words
The process of claim 1 wherein the total comonomer contains up to 10% by weight of a copolymerizable composition which will contribute pendant hydroxyl groups in the backbone of the resulting copolymer.
Claim 12
Dependent Claim
12 words
The process of claim 10 wherein the copolymerizable composition is 2-hydroxyethyl methacrylate.
Claim 13
Dependent Claim
12 words
The process of claim 1 wherein the catalyst is a redox catalyst.
Claim 14
Dependent Claim
11 words
The process of claim 1 wherein the mercaptan is n-dodecyl mercaptan.
Claim 15
Dependent Claim
10 words
The process of claim 1 wherein the mercaptan is isooctythioglycolate.
Claim 16
Dependent Claim
28 words
The process of claim 1 wherein the chain transfer agent is employed at a level of from about 0.1% to about 1.0% based on total weight of comonomers.
Claim 17
Dependent Claim
104 words
A process for preparing multifunctional acrylate modified-vinyl ester-alkyl acrylate/methacrylate copolymer latex, highly stable and substantially coagulum free, which comprises emulsion-polymerizing a non-pre-emulsified mixture of: (i) from about 40 to about 95% based on total weight comonomers, of vinyl acetate (ii) from about 5% to about 35%, based on total weight of comonomers, of butyl acrylate (iii) from about 0.5% to about 10%, based on total weight of comonomers, of trimethylolpropane triacrylate or pentaerythritol triacrylate, in the presence of water, a redox catalyst and about 0.1% to about 1.0%, by weight based on total weight of comonomers of a normally liquid mercaptan chain transfer agent.
Claim 18
Dependent Claim
104 words
A process for preparing multifunctional acrylate modified-vinyl ester-alkyl acrylate/methacrylate copolymer latex, highly stable and substantially coagulum free, which comprises emulsion-polymerizing a non-pre-emulsified mixture of: (i) from about 40 to about 95% based on total weight comonomers, of vinyl acetate (ii) from about 5% to about 35%, based on total weight of comonomers, of butyl acrylate (iii) from about 0.5% to about 10%, based on total weight of comonomers, of trimethylolpropane triacrylate or pentaerythritol triacrylate, in the presence of water, a redox catalyst and about 0.1% to about 1.0%, by weight based on total weight of comonomers of a normally liquid mercaptan chain transfer agent.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-04-23 | 1982-10-23 | 1983-04-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-04-23 | 1986-10-23 | 1987-04-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-04-23 | 1990-10-23 | 1991-04-24 | $7700.00 | Window Closed / Lapsed |