US4151122A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Reduction and reoxidation of cogel or self-reduced catalyst
Assignee: Phillips Petroleum Co
•
Filing: 1977-12-05
•
Granted: 1979-04-24
•
Expires: 1997-12-05
Abstract
Abstract {PG,1 High melt flow olefin polymers suitable for such applications as injection molding, and the like requiring a narrow molecular weight distribution are produced using a catalyst made by reducing and reoxidizing a chromium catalyst on either a titanium-silica cogel or a self-reduced silica-containing composition. In the first embodiment, a cogel formed by coprecipitating silica and titania, and containing a chromium compound, is treated in a nonoxidizing atmosphere, such as CO, hydrogen, N{HD 2 {L or a material decomposable to these materials, and thereafter reoxidized. In the second embodiment, a titanium-free chromium containing catalyst is first heated in air or the like to dry the catalyst and oxidize the chromium after which it is heated in an inert atmosphere wherein the composition is self-reduced to give chromium in a lower valence state. The resulting self-reduced composition is then heated in a reducing ambient and then reoxidized as in the first embodiment.
Inventors
- 👤 Max P. McDaniel
- 👤 Melvin B. Welch
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 07:41
CPC Classifications
B; B01; B01J; B01J37/00; B01J37/12; B01J23/00; B01J23/16; B01J23/24; B01J23/26; C; C08; C08F; C08F10/00
Claims Analysis
Total Claims: 34
Claim 1
Independent Claim
63 words
A process for activating a chromium-containing catalyst prepared by coprecipitating a titanium compound and silica to form a cogel comprising a first step wherein said catalyst is contacted with a nonoxidizing ambient at a temperature of at least 600° C. and a subsequent second step where it is contacted with an oxygen-containing oxidizing ambient at a temperature within the range of 450°-1000° C.
Claim 2
Dependent Claim
63 words
A process for activating a chromium-containing catalyst prepared by coprecipitating a titanium compound and silica to form a cogel comprising a first step wherein said catalyst is contacted with a nonoxidizing ambient at a temperature of at least 600° C. and a subsequent second step where it is contacted with an oxygen-containing oxidizing ambient at a temperature within the range of 450°-1000° C.
Claim 3
Dependent Claim
80 words
A method according to claim 1 wherein prior to said first step said catalyst composition containing at least a portion of said chromium in the form of CrO 3 is treated at a temperature of 600°-1100° C. in an inert atmosphere for a time sufficient to achieve at least partial self-reduction of said chromium to a lower valence state and wherein said nonoxidizing ambient of said first step is a reducing agent under the conditions employed in said first step.
Claim 4
Dependent Claim
19 words
A method according to claim 2 wherein said reducing agent comprises carbon monoxide and said inert ambient is nitrogen.
Claim 5
Dependent Claim
26 words
A method according to claim 2 wherein said CrO 3 is obtained by heating said catalyst in the presence of oxygen prior to said self-reduction step.
Claim 6
Dependent Claim
26 words
A method according to claim 2 wherein said CrO 3 is obtained by introducing said chromium onto said cogel in the form of CrO 3 initially.
Claim 7
Dependent Claim
110 words
A method according to claim 2 wherein said cogel is heated in air to a temperature within the range of 250°-1000° C. over a time period of 20 minutes to 10 hours and thereafter said self-reduction is carried out in nitrogen at a temperature within the range of 700°-925° C. for at least 5 minutes and wherein said reduction step is carried out in an ambient comprising 2-100% carbon monoxide at a temperature of 700°-925° C. for a time within the range of 1/2 to 24 hours and wherein said reoxidation is carried out in air at a temperature within the range of 500°-925° C. for 1/2 to 10 hours.
Claim 8
Dependent Claim
19 words
A method according to claim 6 wherein said nonoxidizing ambient is 2-100% carbon monoxide and 98-0% N 2 .
Claim 9
Dependent Claim
54 words
A method according to claim 7 wherein said chromium is present in an amount within the range of 0.1 to 5 weight percent based on the weight of said cogel and said titanium is present in an amount within the range of 0.5 to 5 weight percent based on the weight of said cogel.
Claim 10
Dependent Claim
12 words
A method according to claim 8 wherein said nonoxidizing ambient is nitrogen.
Claim 11
Dependent Claim
91 words
A method according to claim 9 wherein said cogel is formed by adding a titanium compound to a mineral acid, introducing an alkali metal silicate into the acid containing said titanium compound to form a hydrogel, aging the hydrogel for a time of greater than one hour, washing the thus aged hydrogel to produce a substantially alkali metal free hydrogel, forming a mixture comprising the thus washed hydrogel and a normally liquid oxygen-containing water soluble organic compound, and separating said organic compound and water from said mixture to form a xerogel.
Claim 12
Dependent Claim
22 words
A method according to claim 10 wherein said chromium is added as an aqueous solution of a chromium compound to said hydrogel.
Claim 13
Dependent Claim
27 words
A method according to claim 1 wherein said contact with said non-oxidizing ambient and said contact with said oxidizing ambient is carried out in a continuous activator.
Claim 14
Dependent Claim
37 words
A method according to claim 1 wherein said contact with said oxygen-containing ambient is carried out at a temperature at least 100° C. below the temperature of which said contact with said nonoxidizing ambient is carried out.
Claim 15
Dependent Claim
9 words
A catalyst produced by the method of claim 11.
Claim 16
Dependent Claim
9 words
A catalyst produced by the method of claim 1.
Claim 17
Dependent Claim
92 words
A process for producing a catalyst active for olefin polymerization comprising subjecting a titanium-free silica composition containing chromium wherein at least a portion of said chromium is in the form of CrO 3 to an inert ambient for a time and at a temperature sufficient to self-reduce at least a portion of said CrO 3 to a lower valence state, and thereafter subjecting the thus self-reduced composition to a reducing ambient at a temperature sufficient to further reduce at least a portion of said chromium, and thereafter reoxidizing the thus reduced composition.
Claim 18
Dependent Claim
92 words
A process for producing a catalyst active for olefin polymerization comprising subjecting a titanium-free silica composition containing chromium wherein at least a portion of said chromium is in the form of CrO 3 to an inert ambient for a time and at a temperature sufficient to self-reduce at least a portion of said CrO 3 to a lower valence state, and thereafter subjecting the thus self-reduced composition to a reducing ambient at a temperature sufficient to further reduce at least a portion of said chromium, and thereafter reoxidizing the thus reduced composition.
Claim 19
Dependent Claim
37 words
A method according to claim 16 wherein said self-reduction is carried out in a nitrogen ambient and said further reduction is carried out in an ambient comprising carbon monoxide and said reoxidation is carried out in air.
Claim 20
Dependent Claim
22 words
A method according to claim 16 wherein said CrO 3 is obtained by initially impregnating the titanium-free silica with CrO 3 .
Claim 21
Dependent Claim
26 words
A method according to claim 17 wherein said CrO 3 is obtained by heating said silica composition to said self-reduction temperature in the presence of air.
Claim 22
Dependent Claim
9 words
A catalyst produced by the method of claim 19.
Claim 23
Dependent Claim
9 words
A catalyst produced by the method of claim 16.
Claim 24
Independent Claim
99 words
A method of producing a catalyst active for olefin polymerization comprising subjecting a titanium-free silica composition containing chromium at least a portion of which is in the form of CrO 3 to an inert ambient at a temperature within the range of 600°-1100° C. for a time of at least 5 minutes, and thereafter contacting the resulting composition with a reducing ambient at a temperature within the range of 650°-1100° C. for a time of at least 5 minutes, and thereafter contacting the thus reduced composition with an oxygen-containing ambient at a temperature within the range of 450°-1000° C.
Claim 25
Independent Claim
99 words
A method of producing a catalyst active for olefin polymerization comprising subjecting a titanium-free silica composition containing chromium at least a portion of which is in the form of CrO 3 to an inert ambient at a temperature within the range of 600°-1100° C. for a time of at least 5 minutes, and thereafter contacting the resulting composition with a reducing ambient at a temperature within the range of 650°-1100° C. for a time of at least 5 minutes, and thereafter contacting the thus reduced composition with an oxygen-containing ambient at a temperature within the range of 450°-1000° C.
Claim 26
Dependent Claim
25 words
A method according to claim 22 wherein said inert ambient is nitrogen, said reducing ambient is 2-100% carbon monoxide, and said oxygen-containing ambient is air.
Claim 27
Dependent Claim
24 words
A method according to claim 22 wherein said CrO 3 is obtained by incorporating said chromium onto said silica base as CrO 3 initially.
Claim 28
Dependent Claim
27 words
A method according to claim 22 wherein said CrO 3 is obtained by heating said catalyst to said temperature of 600°-1100° C. in the presence of oxygen.
Claim 29
Dependent Claim
23 words
A method according to claim 22 wherein said heating to said temperature of 600°-1100° C. is carried out in the presence of air.
Claim 30
Dependent Claim
31 words
A method according to claim 22 wherein said chromium is present in an amount within the range of 0.1 to 10 weight percent based on the weight of said silica composition.
Claim 31
Dependent Claim
31 words
A method according to claim 22 wherein said chromium is present in an amount within the range of 0.1 to 5 weight percent based on the weight of said silica composition.
Claim 32
Dependent Claim
15 words
A method according to claim 22 wherein said oxygen-containing ambient for said reoxidation is air.
Claim 33
Dependent Claim
35 words
A method according to claim 22 wherein said subjecting to an inert atmosphere and said contacting with a reducing ambient and said contacting with an oxygen-containing ambient are all carried out in a continuous activator.
Claim 34
Dependent Claim
37 words
A method according to claim 22 wherein said contact with said oxygen-containing ambient is carried out at a temperature at least 100° C. below the temperature at which said contact with said reducing ambient is carried out.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-04-23 | 1982-10-23 | 1983-04-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-04-23 | 1986-10-23 | 1987-04-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-04-23 | 1990-10-23 | 1991-04-24 | $7700.00 | Window Closed / Lapsed |