Hydrocarbon conversion catalyst containing a co-oxidation promoter
Assignee: ExxonMobil Technology and Engineering Co
•
Filing: 1977-12-22
•
Granted: 1979-04-24
•
Expires: 1997-12-22
Abstract
Abstract A cracking catalyst for promoting the oxidation of carbon monoxide to carbon dioxide during regeneration of the catalyst by the burning of coke therefrom, which comprises a crystalline aluminosilicate zeolite, an inorganic porous oxide matrix material and a CO oxidation promoter, such as a Group VIII metal or compound thereof. The catalyst is preferably prepared by first supporting the CO oxidation promoter on an inorganic porous oxide base, such as alumina, and thereafter embedding the supported CO oxidation promoter and a crystalline aluminosilicate zeolite, such as rare earth metal exchanged Y-type zeolite, in an inorganic porous oxide matrix material, such as silica-alumina.
Inventors
- 👤 Elroy M. Gladrow
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 07:07
CPC Classifications
C; C10; C10G; C10G11/00; C10G11/02; C10G11/04; B; B01; B01J; B01J23/00; B01J23/38; B01J29/00; B01J29/04; B01J29/06; B01J29/061; B01J29/08; C10G11/05; B01J29/70
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
86 words
A hydrocarbon conversion catalyst which comprises particles of crystalline aluminosilicate zeolite and particles of a porous oxide support containing a CO oxidation promoter, which particles are each embedded in a porous oxide matrix to produce a catalyst composite thereof containing 2 to 20 wt. % of the zeolite and 2 to 100 ppm of a CO oxidation promoter comprising a metal or a compound of a metal selected from Periods 5 and 6 of Group VIII of the Periodic Table, rhenium, chromium, manganese and combinations thereof.
Claim 2
Dependent Claim
86 words
A hydrocarbon conversion catalyst which comprises particles of crystalline aluminosilicate zeolite and particles of a porous oxide support containing a CO oxidation promoter, which particles are each embedded in a porous oxide matrix to produce a catalyst composite thereof containing 2 to 20 wt. % of the zeolite and 2 to 100 ppm of a CO oxidation promoter comprising a metal or a compound of a metal selected from Periods 5 and 6 of Group VIII of the Periodic Table, rhenium, chromium, manganese and combinations thereof.
Claim 3
Dependent Claim
25 words
The catalyst of claim 1 wherein said CO oxidation promoter is selected from the group consisting of platinum, palladium, rhodium, rhenium, iridium, and combinations thereof.
Claim 4
Dependent Claim
26 words
The catalyst of claim 2 wherein said matrix is selected from the group consisting of silica, alumina, magnesium, zirconia, kaolin and montmorillonite, clays and combinations thereof.
Claim 5
Dependent Claim
25 words
The composition of claim 3 wherein said CO oxidation promoter is selected from the group consisting of platinum, palladium, rhodium, iridium, rhenium, and combinations thereof.
Claim 6
Dependent Claim
15 words
The composition of claim 4 wherein said support is alumina and said matrix is silica-alumina.
Claim 7
Dependent Claim
26 words
The composition of claim 5 wherein said crystalline aluminosilicate zeolite has an Na 2 O level below 4 weight percent and contains rare earth metal ions.
Claim 8
Dependent Claim
88 words
A cracking catalyst for promoting the oxidation of CO to CO 2 during regeneration of the catalyst by the burning of coke therefrom, prepared by first supporting a CO oxidation promoter selected from Periods 5 and 6 of Group VIII of the Periodic Table, rhenium, chromium, manganese, and combinations thereof on a porous oxide support and thereafter dispersing the supported CO oxidation promoter and a crystalline aluminosilicate zeolite in a porous oxide matrix to form a composite thereof containing 2 to 100 ppm of said CO oxidation promoter.
Claim 9
Dependent Claim
88 words
A cracking catalyst for promoting the oxidation of CO to CO 2 during regeneration of the catalyst by the burning of coke therefrom, prepared by first supporting a CO oxidation promoter selected from Periods 5 and 6 of Group VIII of the Periodic Table, rhenium, chromium, manganese, and combinations thereof on a porous oxide support and thereafter dispersing the supported CO oxidation promoter and a crystalline aluminosilicate zeolite in a porous oxide matrix to form a composite thereof containing 2 to 100 ppm of said CO oxidation promoter.
Claim 10
Dependent Claim
36 words
The cracking catalyst of claim 7 wherein said CO oxidation promoter is selected from the group consisting of platinum, palladium, rhodium, rhenium, iridium and combinations thereof and said crystalline aluminosilicate zeolite contains rare earth metal ions.
Claim 11
Dependent Claim
16 words
The cracking catalyst of claim 8 wherein said support is aluminum and said matrix is silica-alumina.
Claim 12
Dependent Claim
22 words
The cracking catalyst of claim 9 wherein said supported CO oxidation promoter is calcined prior to combination with said zeolite and matrix.
References Cited (Backward Citations)
US3364136A
Cited
US4072600A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-04-23 | 1982-10-23 | 1983-04-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-04-23 | 1986-10-23 | 1987-04-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-04-23 | 1990-10-23 | 1991-04-24 | $7700.00 | Window Closed / Lapsed |