Method of joining metal parts
Assignee: Safran Aircraft Engines SAS
•
Filing: 1978-02-22
•
Granted: 1979-04-24
•
Expires: 1998-02-22
Abstract
Abstract The procedure according to the invention, for joining together stainless el or superalloy parts, consists of placing an interface material, chosen from a group containing tin, indium, antimony, gallium and germanium or consisting of a combination of these elements, between the contacting surfaces of the parts, and then subjecting the entire assembly to heat treatment in a controlled atmosphere at a temperature greater than 900° C. but in every case less than the solidus point of the parts to be joined together. If the parts are not of the same nature, the lower solidus point will be the limiting temperature. The treatment lasts as long as necessary to permit the interface material to migrate and compounds or solutions to form, ensuring the diffusion brazing of the parts to be joined. The parts are held together under a moderate pressure during at least part of the treatment, so as to maintain their positions relative to each other and to promote the diffusion without causing deformation.
Inventors
- 👤 Jacques Lesgourgues
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 14:55
CPC Classifications
B; B23; B23K; B23K20/00; B23K20/22; B23K35/00; B23K35/001; B23K35/004; B23K35/22; B23K35/24
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
137 words
The method of solidly joining parts made of stainless steel or of superalloy, comprising the steps of: interposing a layer of an interface material of at least one selected from a group containing tin, indium, antimony, gallium and germanium between contacting surfaces of the parts, subjecting the assembly to a heat treatment under a controlled atmosphere, at a temperature higher than 900° C. but lower than the solidus point of the parts to be joined, for an interval of time sufficient to permit the migration of the interface material and the formation of compounds or solutions which ensure the diffusion brazing of the parts to be joined, and during at least a portion of the treatment, subjecting the parts to a moderate holding pressure to maintain their relative position and to promote the diffusion without causing deformation.
Claim 2
Independent Claim
137 words
The method of solidly joining parts made of stainless steel or of superalloy, comprising the steps of: interposing a layer of an interface material of at least one selected from a group containing tin, indium, antimony, gallium and germanium between contacting surfaces of the parts, subjecting the assembly to a heat treatment under a controlled atmosphere, at a temperature higher than 900° C. but lower than the solidus point of the parts to be joined, for an interval of time sufficient to permit the migration of the interface material and the formation of compounds or solutions which ensure the diffusion brazing of the parts to be joined, and during at least a portion of the treatment, subjecting the parts to a moderate holding pressure to maintain their relative position and to promote the diffusion without causing deformation.
Claim 3
Independent Claim
139 words
The method of solidly joining parts made of stainless steel or of superalloy, comprising the steps of interposing a layer of an interface material consisting of a combination of materials selected from a group containing tin, indium, antimony, gallium and germanium between the contacting surfaces of the parts, subjecting the assembly to a treatment under a controlled atmosphere, at a temperature higher than 900° C. but lower than the solidus point of the parts to be joined, for an interval of time sufficient to permit the migration of the interface material and the formation of compounds or solutions which ensure the diffusion brazing of the parts to be joined, and during at least a portion of the treatment, subjecting the parts to a moderate holding pressure to maintain their relative position and to promote the diffusion without causing deformation.
Claim 4
Independent Claim
139 words
The method of solidly joining parts made of stainless steel or of superalloy, comprising the steps of interposing a layer of an interface material consisting of a combination of materials selected from a group containing tin, indium, antimony, gallium and germanium between the contacting surfaces of the parts, subjecting the assembly to a treatment under a controlled atmosphere, at a temperature higher than 900° C. but lower than the solidus point of the parts to be joined, for an interval of time sufficient to permit the migration of the interface material and the formation of compounds or solutions which ensure the diffusion brazing of the parts to be joined, and during at least a portion of the treatment, subjecting the parts to a moderate holding pressure to maintain their relative position and to promote the diffusion without causing deformation.
Claim 5
Dependent Claim
32 words
The method according to claim 1, characterized by the fact that the interface material is combined to a matrix whose composition is similar to that of the parts to be joined together.
Claim 6
Dependent Claim
65 words
The method according to claim 1, characterized by the fact that the heat treatment successively comprises a pre-joining stage wherein the parts are held together under pressure and at the end of which there remains no liquid phase at the interface of the parts, and a second stage to complete the diffusion phenomenon, wherein the pressure applied on the parts during the pre-joining is removed.
Claim 7
Independent Claim
31 words
The method according to any one of claims 1 through 4, characterized by the fact that the interface material is tin and that the treatment temperature is higher than 1050° C.
Claim 8
Dependent Claim
30 words
The method according to claim 1, characterized by the fact that the interface material is one of antimony and germanium and that the treatment temperature is higher than 1000° C.
Claim 9
Dependent Claim
24 words
The method according to claim 1, characterized by the fact that the contacting surfaces of the parts are plated with nickel before the assembly.
Claim 10
Dependent Claim
27 words
The method according to claim 1, characterized by the fact that the heat treatment takes place in a vacuum of less than 0.1 Pa [10 -6 bar].
Claim 11
Dependent Claim
19 words
The method according to claim 1, characterized by the fact that the treatment takes place in an inert atmosphere.
Claim 12
Dependent Claim
59 words
The method of claim 1 wherein said joining of parts comprises binding an abradable material, that is, a material capable of wearing down by abrasion, of the group consisting of the honeycomb type, refractory material, the porous type produced from sintered powders, and of felt based on refractory metals, onto a metallic support of one of steel and superalloy.
References Cited (Backward Citations)
US4038041A
Cited
US4059217A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-04-23 | 1982-10-23 | 1983-04-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-04-23 | 1986-10-23 | 1987-04-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-04-23 | 1990-10-23 | 1991-04-24 | $7700.00 | Window Closed / Lapsed |