Method for manufacture of poly-fatty acids and maleic anhydride-added fatty acids
Assignee: National Institute of Advanced Industrial Science and Technology
•
Filing: 1977-10-28
•
Granted: 1979-04-17
•
Expires: 1997-10-28
Abstract
Abstract A poly-fatty acid or maleic anhydride-added fatty acid is manufactured by continuously passing a higher unsaturated fatty acid, alone or in combination with maleic anhydride, over a catalyst having phosphoric acid deposited on a synthetic silica-alumina carrier.
Inventors
- 👤 Osamu Suzuki
- 👤 Keizo Tanabe
- 👤 Tetsutaro Hashimoto
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 06:35
CPC Classifications
C; C07; C07C; C07C57/00; C07C57/02; C07C57/03; C07C57/12; C09; C09F; C09F7/00; C09F7/06
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
154 words
A method for the manufacture of a maleic anhydride-added fatty acid, which comprises causing maleic anhydride and at least one ethylenically unsaturated fatty acid selected from the group consisting of oleic acid, linoleic acid, linolenic acid, α-eleostearic acid, β-eleostearic acid, ricinoleic acid, ricinelaidic acid and fatty acids derived from tall oil, soybean oil, linseed oil, cotton-seed oil, safflower oil, castor oil and tung oil, to flow continuously and come into contact with a synthetic silica-alumina catalyst having a composition of 69 to 72 wt.% of SiO 2 , 27 to 30 wt.% of Al 2 O 3 , not more than 1 wt.% of Fe 2 O 3 , not more than 1 wt.% of CaO and not more than 1 wt.% of MgO, having phosphoric acid supported thereon, and maintained in a temperature range of from 150° C. to 330° C., whereby the addition of maleic anhydride to said fatty acid is effected.
Claim 2
Independent Claim
154 words
A method for the manufacture of a maleic anhydride-added fatty acid, which comprises causing maleic anhydride and at least one ethylenically unsaturated fatty acid selected from the group consisting of oleic acid, linoleic acid, linolenic acid, α-eleostearic acid, β-eleostearic acid, ricinoleic acid, ricinelaidic acid and fatty acids derived from tall oil, soybean oil, linseed oil, cotton-seed oil, safflower oil, castor oil and tung oil, to flow continuously and come into contact with a synthetic silica-alumina catalyst having a composition of 69 to 72 wt.% of SiO 2 , 27 to 30 wt.% of Al 2 O 3 , not more than 1 wt.% of Fe 2 O 3 , not more than 1 wt.% of CaO and not more than 1 wt.% of MgO, having phosphoric acid supported thereon, and maintained in a temperature range of from 150° C. to 330° C., whereby the addition of maleic anhydride to said fatty acid is effected.
Claim 3
Dependent Claim
29 words
The method according to claim 1, wherein the amount of said phosphoric acid carried on the synthetic silica-alumina catalyst is from 0.1 to 2.0 milli-equivalent per g of silica-alumina.
Claim 4
Dependent Claim
26 words
The method according to claim 2, wherein said amount of phosphoric acid carried on the catalyst is from 0.5 to 1.5 milli-equivalent per g of silica-alumina.
Claim 5
Dependent Claim
49 words
The method according to claim 1, wherein said synthetic silica-alumina catalyst is dehydrated in advance by being heated in a current of nitrogen gas at a temperature about 10° C. higher than the temperature at which said catalyst is maintained in the manufacture of said maleic anhydride-added fatty acid.
Claim 6
Dependent Claim
33 words
The method of claim 1, wherein said ethylenically unsaturated fatty acid is selected from the group consisting of oleic acid, linoleic acid, linolenic acid, α-eleostearic acid, β-eleostearic acid, ricinoleic acid and ricinelaidic acid.
Claim 7
Dependent Claim
37 words
The method of claim 1, wherein said ethylenically unsaturated fatty acid is selected from the group consisting of fatty acids derived from tall oil, soybean oil, linseed oil, cotton-seed oil, safflower oil, castor oil and tung oil.
Claim 8
Dependent Claim
29 words
The method of claim 5, wherein said ethylenically unsaturated fatty acid is selected from the group consisting of oleic acid, linoleic acid, linolenic acid, ricinoleic acid and ricinelaidic acid.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-04-16 | 1982-10-16 | 1983-04-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-04-16 | 1986-10-16 | 1987-04-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-04-16 | 1990-10-16 | 1991-04-17 | $7700.00 | Window Closed / Lapsed |