US4149876A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for producing tantalum and columbium powder
Assignee: TANTALUM PRODUCTION Inc A DE CORP
•
Filing: 1978-06-06
•
Granted: 1979-04-17
•
Expires: 1998-06-06
Abstract
Abstract A method of producing tantalum or columbium powder is described for producing a selected desired particle size powder under controlled conditions with a high rate of production and yield of usable powder. A molten salt bath of an alkali metal tantalum fluoride or an alkali metal columbium fluoride and a relatively large amount of diluent salt to act as a heat sink is initially maintained at a low temperature in the liquidus range, an addition of liquid alkali metal reducing metal is added at a very fast rate to the continuously stirred bath to create a rapid temperature rise to the reaction temperature, and liquid alkali metal is thereafter fed at a fast rate to complete the reaction quickly at the final reaction temperature. Cooling is used for at least a portion of the reaction cycle at a rate sufficient to maintain the final reaction temperature within a desired range.
Inventors
- 👤 Carlos F. Rerat
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 23:23
CPC Classifications
H; H01; H01G; H01G9/00; H01G9/004; H01G9/04; H01G9/048; H01G9/052; H01G9/0525; B; B22; B22F; B22F9/00; B22F9/16; B22F9/18; B22F9/24; C; C22; C22B; C22B34/00; C22B34/20; C22B34/24; C22B5/00; C22B5/02; C22B5/04
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
265 words
The process of producing a metal powder of the group consisting of tantalum and columbium powders which comprises maintaining a liquid bath of a double salt of the formula R.sub.2 MX.sub.7 wherein R is an alkali metal, M is a metal of the group consisting of tantalum or columbium and X is a halogen atom of the group consisting of fluorine, chlorine, or bromine, and a diluent comprising an alkali metal halide at a temperature above the liquidus temperature of said salt mixture but not exceeding 760° C. in a closed reaction vessel, adding a molten alkali metal to said bath at a rate of at least 0.2 kg per kg of said double salt per hour during a nucleation period until a desired reaction temperature between 760° C. and 1000° C. is reached, the temperature rise during said nucleation period being at a rate of at least 10° C. per minute, thereafter adding additional molten alkali metal to said bath at a rate of at least 0.1 kg per kg of said double salt per hour during a growth period while providing forced cooling to said bath at a rate of at least 10 kilocalories per minute per kilogram of said double salt, continuously agitating said liquid bath, continuously producing crystals of said metal M and collecting said crystals in a lower portion of said reaction vessel, said rate of alkali metal addition and said rate of forced cooling being balanced to maintain the reaction temperature in said growth period within 50° C. of said desired reaction temperature but in excess of 760° C.
Claim 2
Dependent Claim
265 words
The process of producing a metal powder of the group consisting of tantalum and columbium powders which comprises maintaining a liquid bath of a double salt of the formula R.sub.2 MX.sub.7 wherein R is an alkali metal, M is a metal of the group consisting of tantalum or columbium and X is a halogen atom of the group consisting of fluorine, chlorine, or bromine, and a diluent comprising an alkali metal halide at a temperature above the liquidus temperature of said salt mixture but not exceeding 760° C. in a closed reaction vessel, adding a molten alkali metal to said bath at a rate of at least 0.2 kg per kg of said double salt per hour during a nucleation period until a desired reaction temperature between 760° C. and 1000° C. is reached, the temperature rise during said nucleation period being at a rate of at least 10° C. per minute, thereafter adding additional molten alkali metal to said bath at a rate of at least 0.1 kg per kg of said double salt per hour during a growth period while providing forced cooling to said bath at a rate of at least 10 kilocalories per minute per kilogram of said double salt, continuously agitating said liquid bath, continuously producing crystals of said metal M and collecting said crystals in a lower portion of said reaction vessel, said rate of alkali metal addition and said rate of forced cooling being balanced to maintain the reaction temperature in said growth period within 50° C. of said desired reaction temperature but in excess of 760° C.
Claim 3
Dependent Claim
36 words
The process of claim 1 wherein said double salt is K 2 TaF 7 , said molten alkali metal is sodium and said diluent is selected from the group consisting of NaCl, KCl and mixtures thereof.
Claim 4
Dependent Claim
23 words
The process of claim 2 wherein said forced cooling includes a high velocity air stream applied to the exterior of said reaction vessel.
Claim 5
Dependent Claim
17 words
The process of claim 3 wherein said forced cooling is applied throughout the period of sodium addition.
Claim 6
Dependent Claim
37 words
The process of claim 2 wherein said diluent salt is NaCl and is present in said liquid bath in a weight ratio from about 0.25 to about 1.0 with respect to said K 2 TaF 7 .
Claim 7
Dependent Claim
40 words
The process of claim 5 wherein said weight ratio is from about 0.6 to about 1.0 and said process produces a tantalum metal powder having an average particle size less than about 5 microns, measured by the Fisher Sub-Sieve Sizer.
Claim 8
Dependent Claim
41 words
The process of claim 5 wherein said weight ratio is from about 0.25 to about 0.60 and said process produces a tantalum powder having an average particle size between about 5 and about 8 microns, measured by the Fisher Sub-Sieve Sizer.
Claim 9
Dependent Claim
19 words
The process of claim 2 wherein at least 50% of the weight of said tantalum crystals is -325 Mesh.
Claim 10
Dependent Claim
24 words
The process of claim 2 wherein said salt bath is maintained at a temperature not exceeding 660° C. before the start of sodium addition.
Claim 11
Dependent Claim
22 words
The process of claim 2 wherein the temperature in said growth period is maintained within 25° C. of said desired reaction temperature.
Claim 12
Dependent Claim
22 words
The process of claim 2 wherein the temperature in said growth period is maintained within 10° C. of said desired reaction temperature.
Claim 13
Dependent Claim
37 words
The process of claim 2 wherein the temperature in said growth period is maintained between about 760° C. and about 850° C. and said tantalum crystals average from about 5 microns in size by Fisher Sub-Sieve Sizer.
Claim 14
Dependent Claim
41 words
The process of claim 2 wherein the temperature in said growth period is maintained between about 850° C. and about 1000° C. and said tantalum crystals average less than about 5 to about 8 microns in size by Fisher Sub-Sieve Sizer.
Claim 15
Dependent Claim
53 words
The process of claim 1 in which said agitation is provided by an agitator maintained above the level of the formed tantalum metal crystals that collect in said reaction vessel and below the liquid level of the said bath by raising the level of said agitator during the period of sodium metal additions.
Claim 16
Dependent Claim
83 words
The process of claim 1 in which said agitation is provided by an agitator having a shaft and having blades which measure about one-half the reaction vessel diameter, said blades having a pitch in the range of 30° to 60° with respect to said agitator shaft, and said agitator rotates at a speed in the range of 0.05 to 0.50 rpm per kg of said salt mixture when the total weight of said mixture is in the range of 500 to 1000 kg.
Claim 17
Dependent Claim
23 words
The process of claim 15 in which the agitator rotational speed is varied within said range at least once during the reaction cycle.
Claim 18
Dependent Claim
243 words
The process of producing a tantalum powder which comprises maintaining a liquid bath of potassium fluotantalate and from about 0.6 to about 1.0 parts by a diluent comprising sodium chloride at a temperature above the liquidus temperature of said salt mixture but not exceeding 660° C. in a closed reaction vessel, adding molten sodium to said bath at a rate of at least 0.2 kg per kg of said potassium fluotantalate per hour during a nucleation period until a desired reaction temperature between 760° C. and 850° C. is reached, the temperature rise during said nucleation period being at a rate of at least 20° C. per minute, thereafter adding additional molten sodium to said bath at a rate of at least 0.1 kg per kg of said potassium fluotantalate per hour during a growth period while providing forced cooling to said bath by means of a high velocity air stream applied to the exterior of said vessel to extract heat at a rate of at least 10 kilocalories per minute per kilogram of said potassium fluotantalate, continuously agitating said liquid bath with an agitator maintained within said bath, continuously producing crystals of tantalum and collecting said crystals in a lower portion of said reaction vessel, said rate of alkali metal addition and said rate of forced cooling being balanced to maintain the reaction temperature in said growth period within 25° C. of said desired reaction temperature but in excess of 760° C.
Claim 19
Dependent Claim
243 words
The process of producing a tantalum powder which comprises maintaining a liquid bath of potassium fluotantalate and from about 0.6 to about 1.0 parts by a diluent comprising sodium chloride at a temperature above the liquidus temperature of said salt mixture but not exceeding 660° C. in a closed reaction vessel, adding molten sodium to said bath at a rate of at least 0.2 kg per kg of said potassium fluotantalate per hour during a nucleation period until a desired reaction temperature between 760° C. and 850° C. is reached, the temperature rise during said nucleation period being at a rate of at least 20° C. per minute, thereafter adding additional molten sodium to said bath at a rate of at least 0.1 kg per kg of said potassium fluotantalate per hour during a growth period while providing forced cooling to said bath by means of a high velocity air stream applied to the exterior of said vessel to extract heat at a rate of at least 10 kilocalories per minute per kilogram of said potassium fluotantalate, continuously agitating said liquid bath with an agitator maintained within said bath, continuously producing crystals of tantalum and collecting said crystals in a lower portion of said reaction vessel, said rate of alkali metal addition and said rate of forced cooling being balanced to maintain the reaction temperature in said growth period within 25° C. of said desired reaction temperature but in excess of 760° C.
Claim 20
Dependent Claim
25 words
The process of claim 17 in which said forced cooling includes a high velocity stream of carbon dioxide applied to the exterior of said vessel.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-04-16 | 1982-10-16 | 1983-04-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-04-16 | 1986-10-16 | 1987-04-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-04-16 | 1990-10-16 | 1991-04-17 | $7700.00 | Window Closed / Lapsed |