Reforming with multimetallic catalysts
Assignee: ExxonMobil Technology and Engineering Co
•
Filing: 1977-12-19
•
Granted: 1979-04-10
•
Expires: 1997-12-19
Abstract
Abstract A process for desensitizing a hypersensitive, high activity reforming catalyst for suppression of hydrogenolysis which is particularly acute during the early portion of the period that the catalyst is placed on stream, i.e., at the start-up of a reactor. The catalyst is constituted of a composite which includes a Group VIII noble metal hydrogenation-dehydrogenation component, notably platinum, iridium or rhenium, and a sulfurous acid or sulfuric acid component. Hydrogenolysis is suppressed by incorporating within such reforming catalyst at the time of its preparation a sulfurous acid or sulfuric acid component. In another of its aspects the present invention embodies a reforming catalyst or catalyst composite comprising a refractory or inorganic oxide support material, particularly alumina, a Group VIII noble metal hydrogenation-dehydrogenation component, notably platinum, to which iridium or rhenium, and a sulfurous acid or sulfuric acid component have been added to promote the activity and selectivity of the catalysts, and said catalyst is prepared by a method wherein the sulfurous acid or sulfuric acid component is introduced into and deposited throughout said support. Suitably, the reforming catalyst, or composite also contains a halogen component, particularly chlorine and preferably the sulfurous acid or sulfuric acid component is introduced into the support, or catalyst, by impregnating with a liquid solution which contains one or both of these compounds.
Inventors
- 👤 Paul E. Eberly, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 19:24
CPC Classifications
B; B01; B01J; B01J23/00; B01J23/38; B01J23/40; B01J23/46; B01J23/468; B01J23/54; B01J23/56; B01J23/64; B01J23/656; B01J23/6567; B01J27/00; B01J27/02
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
135 words
In a process for preparing a reforming catalyst wherein a Group VIII noble metal hydrogenation-dehydrogenation component in concentration ranging from about 0.01 to about 3 percent, based on the weight of the catalyst, a component comprised of iridium or rhenium, or both, in concentration ranging from about 0.01 to about 3 percent, based on the weight of the catalyst, and a halogen component in concentration ranging from about 0.1 to about 3 percent, based on the weight of the catalyst, composited with an inorganic oxide support, the improvement which comprises incorporating sulfurous acid or sulfuric acid, or both, as a component within said catalyst at the time of its preparation in concentration ranging from about 0.001 to 3 percent, based on the weight of the catalyst, sufficient to increase the activity, or selectivity, or both.
Claim 2
Dependent Claim
135 words
In a process for preparing a reforming catalyst wherein a Group VIII noble metal hydrogenation-dehydrogenation component in concentration ranging from about 0.01 to about 3 percent, based on the weight of the catalyst, a component comprised of iridium or rhenium, or both, in concentration ranging from about 0.01 to about 3 percent, based on the weight of the catalyst, and a halogen component in concentration ranging from about 0.1 to about 3 percent, based on the weight of the catalyst, composited with an inorganic oxide support, the improvement which comprises incorporating sulfurous acid or sulfuric acid, or both, as a component within said catalyst at the time of its preparation in concentration ranging from about 0.001 to 3 percent, based on the weight of the catalyst, sufficient to increase the activity, or selectivity, or both.
Claim 3
Dependent Claim
124 words
In a process for preparing a reforming catalyst which comprises a platinum metal component in concentration ranging from about 0.01 to about 3 percent, based on the weight of the catalyst, a component comprised of iridium or rhenium, or both, in concentration ranging from about 0.01 to about 3 percent, based on the weight of the catalyst, and a halogen component in concentration ranging from about 0.1 to about 3 percent, based on the weight of the catalyst, composited with an inorganic oxide support, the improvement which comprises incorporating sulfurous acid or sulfuric acid, or both, as a component within said catalyst at the time of its preparation in concentration ranging from about 0.001 to 3 percent, based on the weight of the catalyst.
Claim 4
Dependent Claim
124 words
In a process for preparing a reforming catalyst which comprises a platinum metal component in concentration ranging from about 0.01 to about 3 percent, based on the weight of the catalyst, a component comprised of iridium or rhenium, or both, in concentration ranging from about 0.01 to about 3 percent, based on the weight of the catalyst, and a halogen component in concentration ranging from about 0.1 to about 3 percent, based on the weight of the catalyst, composited with an inorganic oxide support, the improvement which comprises incorporating sulfurous acid or sulfuric acid, or both, as a component within said catalyst at the time of its preparation in concentration ranging from about 0.001 to 3 percent, based on the weight of the catalyst.
Claim 5
Dependent Claim
20 words
The process of claim 2 wherein the halogen component is chlorine, and the inorganic oxide support is comprised of alumina.
Claim 6
Dependent Claim
32 words
The process of claim 2 wherein the sulfurous acid or sulfuric acid component is incorporated into the catalyst by impregnating same with a liquid solution of one or both of said compounds.
Claim 7
Dependent Claim
133 words
In a process for preparing a reforming catalyst which comprises a platinum metal component in concentration ranging from about 0.01 to about 3 percent, based on the weight of the catalyst, a component comprised of iridium or rhenium, or both in concentration ranging from about 0.01 to about 3 percent, based on the weight of the catalyst, and a halogen component in concentrating ranging from about 0.1 to about 3 percent, based on the weight of the catalyst, composited with an alumina support, the improvement which comprises impregnating said support with an aqueous solution containing salts of platinum, salts of iridium, or rhenium, or both, a halogen component, and sulfurous acid or sulfuric acid component, or both, in concentration ranging from 0.001-3% within said alumina support, based on the weight of the catalyst.
Claim 8
Dependent Claim
133 words
In a process for preparing a reforming catalyst which comprises a platinum metal component in concentration ranging from about 0.01 to about 3 percent, based on the weight of the catalyst, a component comprised of iridium or rhenium, or both in concentration ranging from about 0.01 to about 3 percent, based on the weight of the catalyst, and a halogen component in concentrating ranging from about 0.1 to about 3 percent, based on the weight of the catalyst, composited with an alumina support, the improvement which comprises impregnating said support with an aqueous solution containing salts of platinum, salts of iridium, or rhenium, or both, a halogen component, and sulfurous acid or sulfuric acid component, or both, in concentration ranging from 0.001-3% within said alumina support, based on the weight of the catalyst.
Claim 9
Dependent Claim
11 words
The process of claim 5 wherein the halogen component is chlorine.
Claim 10
Dependent Claim
127 words
A reforming catalyst which comprises a Group VIII noble metal hydrogenation-dehydrogenation component in concentration ranging from about 0.01 to about 3 percent, based on the weight of the catalyst, a component comprised of iridium or rhenium, or both, in concentration ranging from about 0.01 to about 3 percent, based on the weight of the catalyst a halogen component in concentration ranging from about 0.01 to about 3 percent, based on the weight of the catalyst, and a sulfurous acid or sulfuric acid component in concentration ranging from about 0.001 to about 3 percent, based on the weight of the catalyst sufficient to increase the activity or selectivity, or both, as contrasted with a catalyst otherwise similar except that it does not contain sulfurous acid or sulfuric acid.
Claim 11
Dependent Claim
127 words
A reforming catalyst which comprises a Group VIII noble metal hydrogenation-dehydrogenation component in concentration ranging from about 0.01 to about 3 percent, based on the weight of the catalyst, a component comprised of iridium or rhenium, or both, in concentration ranging from about 0.01 to about 3 percent, based on the weight of the catalyst a halogen component in concentration ranging from about 0.01 to about 3 percent, based on the weight of the catalyst, and a sulfurous acid or sulfuric acid component in concentration ranging from about 0.001 to about 3 percent, based on the weight of the catalyst sufficient to increase the activity or selectivity, or both, as contrasted with a catalyst otherwise similar except that it does not contain sulfurous acid or sulfuric acid.
References Cited (Backward Citations)
US2851399A
Cited
US3884799A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-04-09 | 1982-10-09 | 1983-04-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-04-09 | 1986-10-09 | 1987-04-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-04-09 | 1990-10-09 | 1991-04-10 | $7700.00 | Window Closed / Lapsed |